Styrolution Novodur® 5300 ABS
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Heat Resistant, Molded |
| Manufacturer | Styrolution |
| Trade Name | Novodur® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Styrolution Novodur® 5300 ABS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Novodur 5300 is a high heat injection molding grade with high impact strength, good chemical resistance and reduced emission (PC modified)Information provided by Styrolution
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.07 g/cc | 0.0387 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.0050 - 0.0080 cm/cm | 0.0050 - 0.0080 in/in | ISO 294-4 |
| Melt Flow | 5.0 g/10 min @Load 10.0 kg, Temperature 220 °C |
5.0 g/10 min @Load 22.0 lb, Temperature 428 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 100 MPa | 14500 psi | ISO 2039-1 |
| Tensile Strength, Yield | 49.0 MPa | 7110 psi | ISO 527 |
| Elongation at Yield | 2.9 % | 2.9 % | ISO 527 |
| Tensile Modulus | 2.35 GPa | 341 ksi | ISO 527 |
| Flexural Strength | 75.0 MPa | 10900 psi | ISO 178 |
| Flexural Modulus | 2.30 GPa | 334 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 12.0 kJ/m² @Temperature -30.0 °C |
5.71 ft-lb/in² @Temperature -22.0 °F |
ISO 180/A |
| 32.0 kJ/m² @Temperature 23.0 °C |
15.2 ft-lb/in² @Temperature 73.4 °F |
ISO 180/A | |
| Charpy Impact Unnotched | 18.0 J/cm² @Temperature -30.0 °C |
85.7 ft-lb/in² @Temperature -22.0 °F |
ISO 179 |
| NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ISO 179 | |
| Charpy Impact, Notched | 1.20 J/cm² @Temperature -30.0 °C |
5.71 ft-lb/in² @Temperature -22.0 °F |
ISO 179 |
| 3.20 J/cm² @Temperature 23.0 °C |
15.2 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 90.0 µm/m-°C | 50.0 µin/in-°F | ISO 11359 |
| Deflection Temperature at 0.46 MPa (66 psi) | 106 °C | 223 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 99.0 °C | 210 °F | ISO 75 |
| Vicat Softening Point | 106 °C @Load 5.10 kg |
223 °F @Load 11.2 lb |
50°C/h; ISO 306 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 3.1 @Frequency 100 Hz |
3.1 @Frequency 100 Hz |
IEC 60250 |
| Dissipation Factor | 0.0040 @Frequency 100 Hz |
0.0040 @Frequency 100 Hz |
IEC 60250 |
| 0.0090 @Frequency 1.00e+6 Hz |
0.0090 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 240 °C | 464 °F | ISO 294 |
| Mold Temperature | 70.0 °C | 158 °F | ISO 294 |
| Injection Velocity | 240 mm/sec | 9.45 in/sec | ISO 294 |
| Drying Temperature | 80.0 °C @Time 7200 - 14400 sec |
176 °F @Time 2.00 - 4.00 hour |
Users viewing this material also viewed the following:
- NanoAmor 95%, OD: 50-80 nm COOH Functionalized Aligned Multi-Walled Carbon Nanotubes
- Osprey Metals HTN 7 Brazing Powder
- Kazanorgsintez 102-12K Cable Composition Based on Low Density Polyethylene
- Ineos ABS Lustran® H950
- Solvay Specialty Polymers KetaSpire® KT-850 Polyetheretherketone (PEEK)
- Dow AFFINITY™ EG 8150G Ethylene alpha-olefin copolymer
- DuPont Teijin Films Mylar® HR951 Polyester Film, 140 Gauge
- Covestro Makrolon® 1143 Polycarbonate
- ATI Allegheny Ludlum AL 800™ Nickel-Base Alloy, UNS N08800
- NOVA Chemicals Sclair® 11M1 Butene LLDPE Film Resin (discontinued **)
Copyright © lookpolymers.com All Rights Reserved