SABIC Innovative Plastics ULTEM AR9200 PEI (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | ULTEM |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics ULTEM AR9200 PEI (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
20% Glass fiber filled, standard flow Polyetherimide (Tg 217C). Meets FAR 25.853 and OSU 65/65 with low toxicity, smoke, and flame evolution. ECO Conforming.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.40 g/cc | 1.40 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0050 cm/cm @Thickness 3.20 mm |
0.0030 - 0.0050 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 5.7 g/10 min @Load 6.60 kg, Temperature 337 °C |
5.7 g/10 min @Load 14.6 lb, Temperature 639 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 151 MPa | 21900 psi | Type I, 5 mm/min; ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | Type I, 5 mm/min; ASTM D638 |
| Tensile Modulus | 6.96 GPa | 1010 ksi | 5 mm/min; ASTM D638 |
| Flexural Yield Strength | 206 MPa | 29900 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
| Flexural Modulus | 7.23 GPa | 1050 ksi | 2.6 mm/min, 100 mm span; ASTM D790 |
| Izod Impact, Notched | 1.01 J/cm | 1.89 ft-lb/in | ASTM D256 |
| 5.34 J/cm @Thickness 3.20 mm |
10.0 ft-lb/in @Thickness 0.126 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 211 °C @Thickness 6.40 mm |
412 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| Glass Transition Temp, Tg | 217 °C | 423 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| FAA Flammability, FAR 25.853 A/B | NATURAL | FAR 25.853 |
| NBS Smoke Density, Flaming, Dmax | 5 | ASTM E 662 |
| NBS Smoke Density, Flaming, Ds 1.5 min | 0 | ASTM E 662 |
| NBS Smoke Density, Flaming, Ds 4 min | 5 | ASTM E 662 |
| OSU total heat release (2 minute test) | 5kW-min/m^2 | FAR 25.853 |
| OSU peak heat release rate (5 minute test) | 40kW/m^2 | FAR 25.853 |
| Vertical Burn a (60s) passes at | 0sec | FAR 25.853 |
| Vertical Burn b (12s) passes at | 0sec | FAR 25.853 |
Users viewing this material also viewed the following:
- Rogers Corporation Bisco™ HT-820 Cellular Silicone Foam
- Isoflon PTFE + 50% Stainless Steel (AISI 316 L) Polytetrafluoroethylene with 50% INOX Stainless Steel
- Cossa Polimeri ESTAPROP H0260 MC/EC Conductive Polypropylene, Mineral Filled
- DuPont Teijin Films Mylar® E Polyester Film, 300 Gauge
- Carpenter MP35N* Ni-Co-Cr-Mo Alloy, 35% Cold Reduction + Aged 538°C (1000°F)/4hr/AC
- Bulk Molding Compounds BMC 940 Vinyl Ester Bipolar Plate Material
- Cheng Yu Plastic FV30BK Electric Conducting Polyformaldehyde
- Addiplast Addilene H 210 Polypropylene Homopolymer
- Borealis MD231U Polypropylene Compound, Mineral Filled
Copyright © lookpolymers.com All Rights Reserved