- Polycarbonate/ABS Alloy, Unreinforced
- Samsung Cheil Industries Infino® HI-1001BN PC/ABS, Unreinforced
Samsung Cheil Industries Infino® HI-1001BN PC/ABS, Unreinforced
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Infino® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Infino® HI-1001BN PC/ABS, Unreinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PC/ABS that is used for the housing of mobile phone, wheel cap, rice cooker, electric iron etc., refrigerator door handle, panel etc.Information provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.11 g/cc | 1.11 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 35 g/10 min @Load 10.0 kg, Temperature 250 °C |
35 g/10 min @Load 22.0 lb, Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 110 | 110 | ASTM D785 |
| Tensile Strength at Break | 446 MPa | 64700 psi | 50 mm/min; ASTM D638 |
| Tensile Strength, Yield | 56.9 MPa | 8250 psi | 50 mm/min; ASTM D638 |
| Elongation at Break | 45 % | 45 % | 50 mm/min; ASTM D638 |
| Tensile Modulus | 2.06 GPa | 299 ksi | 50 mm/min; ASTM D638 |
| Flexural Strength | 83.4 MPa | 12100 psi | 2.8 mm/min; ASTM D790 |
| Flexural Modulus | 2.26 GPa | 327 ksi | 2.8 mm/min; ASTM D790 |
| Izod Impact, Notched | 3.82 J/cm @Thickness 6.35 mm |
7.16 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| 4.90 J/cm @Thickness 3.17 mm |
9.18 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 113 °C @Thickness 6.40 mm |
235 °F @Thickness 0.252 in |
ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C @Thickness 6.40 mm |
212 °F @Thickness 0.252 in |
ASTM D648 |
| Vicat Softening Point | 114 °C | 237 °F | B/50; ISO R306 |
| 115 °C | 239 °F | B/120; ISO R306 | |
| Flammability, UL94 | HB @Thickness 1.50 - 6.00 mm |
HB @Thickness 0.0591 - 0.236 in |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Cycoloy® XCM850 PC+ABS (Europe-Africa-Middle East)
- Gouda Vuurvast ADHESIET 180 PCr Dry Air-Setting Refractory Mortar
- Karina 10/1-FC-LMP (SDB) White Color Concentrate for PVC
- H.C. Starck HPM 1750 Tungsten High Density Composite
- Lushan EV1050G1 EVA Film for Encapsulating Solar modules, Ultra Fast Cure
- DuPont Teijin Films Melinex® 618 Polyester Film, 1000 Gauge
- Petromont 7002 Medium Density Polyethylene Resin
Copyright © lookpolymers.com All Rights Reserved