Lubrizol Isoplast® 101 Engineering Thermoplastic Polyurethane Resin

Category Polymer , Thermoplastic , Polyurethane, TP
Manufacturer Lubrizol (former Noveon)
Trade Name Isoplast®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Lubrizol Isoplast® 101 Engineering Thermoplastic Polyurethane Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
ISOPLAST® 101 is an engineering thermoplastic polyurethane resin.Available in Americas, Europe, Middle East, Africa, India and AsiaData provided by LubrizolLubrizol acquired the Isoplast product line from Dow in 2009.
Physical Properties Metric English Comments
Density 1.19 g/cc
0.0430 lb/in³
ASTM D792
Water Absorption 0.17 %
0.17 %
24 hrs at 23°C; ASTM D570
Linear Mold Shrinkage 0.0040 - 0.0060 cm/cm
0.0040 - 0.0060 in/in
ASTM D955
Mechanical Properties Metric English Comments
Hardness, Rockwell R 116
116
ASTM D785
Tensile Strength, Ultimate 48.0 MPa
6960 psi
ASTM D638
Tensile Strength, Yield 48.0 MPa
6960 psi
ASTM D638
Elongation at Break 160 %
160 %
ASTM D638
Elongation at Yield 6.0 %
6.0 %
ASTM D638
Tensile Modulus 1.50 GPa
218 ksi
ASTM D638
Flexural Strength 68.0 MPa
9860 psi
ASTM D790
Flexural Modulus 1.80 GPa
261 ksi
ASTM D790
Izod Impact, Unnotched 1.60 J/cm

@Thickness 3.20 mm,
Temperature -40.0 °C
3.00 ft-lb/in

@Thickness 0.126 in,
Temperature -40.0 °F
ASTM D256
11.0 J/cm

@Thickness 6.40 mm,
Temperature 23.0 °C
20.6 ft-lb/in

@Thickness 0.252 in,
Temperature 73.4 °F
ASTM D256
12.8 J/cm

@Thickness 3.20 mm,
Temperature 23.0 °C
24.0 ft-lb/in

@Thickness 0.126 in,
Temperature 73.4 °F
ASTM D256
Dart Drop, Total Energy 68.0 J

@Temperature 23.0 °C
50.2 ft-lb

@Temperature 73.4 °F
ASTM D3763
68.0 J

@Temperature -29.0 °C
50.2 ft-lb

@Temperature -20.2 °F
ASTM D3763
Thermal Properties Metric English Comments
CTE, linear 81.0 µm/m-°C

@Temperature 20.0 °C
45.0 µin/in-°F

@Temperature 68.0 °F
ASTM D1525
Deflection Temperature at 0.46 MPa (66 psi) 71.0 °C
160 °F
Unannealed; ASTM D648
82.0 °C
180 °F
Annealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 60.0 °C
140 °F
Unannealed; ASTM D648
77.0 °C
171 °F
Annealed; ASTM D648
Vicat Softening Point 89.0 °C
192 °F
ASTM D696
Processing Properties Metric English Comments
Rear Barrel Temperature 205 °C
401 °F
Middle Barrel Temperature 220 °C
428 °F
Front Barrel Temperature 220 °C
428 °F
Nozzle Temperature 230 °C
446 °F
Melt Temperature 220 - 245 °C
428 - 473 °F
Drying Temperature 85.0 - 90.0 °C
185 - 194 °F