LATI Latamid 66 H2PX-V0 PA 66, Heat Stabilized, Flame Retardant

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Heat Stabilized , Nylon 66, Unreinforced, Flame Retardant
Manufacturer LATI
Trade Name Latamid
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Latamid 66 H2PX-V0 PA 66, Heat Stabilized, Flame Retardant.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polyamide 66 (PA66) based compound. Heat stabilized. Toughened. UL94 V-0 classified, with brominated flame retardants, PBB/PBDE free. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.35 g/cc
0.0488 lb/in³
Linear Mold Shrinkage, Flow 0.011 - 0.014 cm/cm
0.011 - 0.014 in/in
Linear Mold Shrinkage, Transverse 0.0115 - 0.0145 cm/cm
0.0115 - 0.0145 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 40.0 MPa

@Temperature 60.0 °C
 5800 psi

@Temperature 140 °F
50.0 MPa

@Temperature 23.0 °C
 7250 psi

@Temperature 73.4 °F
Elongation at Break 10 %

@Temperature 23.0 °C
 10 %

@Temperature 73.4 °F
60 %

@Temperature 60.0 °C
 60 %

@Temperature 140 °F
>= 100 %

@Temperature 90.0 °C
 >= 100 %

@Temperature 194 °F
>= 100 %

@Temperature 120 °C
 >= 100 %

@Temperature 248 °F
>= 100 %

@Temperature 150 °C
 >= 100 %

@Temperature 302 °F
Elongation at Yield 2.5 %

@Temperature 23.0 °C
 2.5 %

@Temperature 73.4 °F
Tensile Modulus 0.400 GPa

@Temperature 150 °C
 58.0 ksi

@Temperature 302 °F
0.550 GPa

@Temperature 120 °C
 79.8 ksi

@Temperature 248 °F
0.800 GPa

@Temperature 90.0 °C
 116 ksi

@Temperature 194 °F
1.40 GPa

@Temperature 60.0 °C
 203 ksi

@Temperature 140 °F
2.80 GPa

@Temperature 23.0 °C
 406 ksi

@Temperature 73.4 °F
Charpy Impact Unnotched NB
NB
Charpy Impact, Notched 0.700 J/cm²
3.33 ft-lb/in²
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 100 °C
212 °F
Deflection Temperature at 0.46 MPa (66 psi) 170 °C
338 °F
Deflection Temperature at 1.8 MPa (264 psi) 70.0 °C
158 °F
Vicat Softening Point 180 °C

@Load 5.00 kg
 356 °F

@Load 11.0 lb
Flammability, UL94 V-0

@Thickness 3.00 mm
 V-0

@Thickness 0.118 in
V-0

@Thickness 1.50 mm
 V-0

@Thickness 0.0591 in
V-0

@Thickness 0.750 mm
 V-0

@Thickness 0.0295 in
Oxygen Index 34 %
34 %
Glow Wire Test 775 °C

@Thickness 1.00 mm
 1430 °F

@Thickness 0.0394 in
 GWIT
775 °C

@Thickness 2.00 mm
 1430 °F

@Thickness 0.0787 in
 GWIT
960 °C

@Thickness 1.00 mm
 1760 °F

@Thickness 0.0394 in
 GWFI/GWT
960 °C

@Thickness 2.00 mm
 1760 °F

@Thickness 0.0787 in
 GWFI/GWT
Electrical Properties Metric English Comments
Comparative Tracking Index 250 V
250 V
A solution
Processing Properties Metric English Comments
Melt Temperature 270 - 290 °C
518 - 554 °F
Mold Temperature 70.0 - 90.0 °C
158 - 194 °F
Drying Temperature 90.0 - 100 °C

@Time 10800 sec
 194 - 212 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa
Users viewing this material also viewed the following: