Star Plastics PC1510UV Molding Grade PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Molded |
| Manufacturer | Star Plastics, Inc |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Star Plastics PC1510UV Molding Grade PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Star Plastics, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D792 |
| Maximum Moisture Content | 0.020 | 0.020 | |
| Linear Mold Shrinkage | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | ASTM D955 |
| Melt Flow | 16 g/10 min @Load 3.80 kg, Temperature 230 °C |
16 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 58.6 MPa | 8500 psi | ASTM D638 |
| Tensile Modulus | 2.38 GPa | 345 ksi | ASTM D638 |
| Flexural Yield Strength | 86.2 MPa | 12500 psi | ASTM D790 |
| Flexural Modulus | 2.38 GPa | 345 ksi | ASTM D790 |
| Izod Impact, Notched | 6.41 J/cm | 12.0 ft-lb/in | 73°F, 0.125 in.; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 132 °C | 270 °F | unannealed, .125in; ASTM D648 |
| Flammability, UL94 | V-2 | V-2 | .06in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 271 - 288 °C | 520 - 550 °F | |
| Middle Barrel Temperature | 277 - 299 °C | 530 - 570 °F | |
| Front Barrel Temperature | 288 - 316 °C | 550 - 600 °F | |
| Nozzle Temperature | 288 - 316 °C | 550 - 600 °F | |
| Melt Temperature | 288 - 316 °C | 550 - 600 °F | |
| Mold Temperature | 76.7 - 104 °C | 170 - 220 °F | |
| Drying Temperature | 121 °C | 250 °F | |
| Dry Time | 4 hour | 4 hour | |
| Back Pressure | 0.345 - 1.38 MPa | 50.0 - 200 psi | |
| Screw Speed | 40 - 75 rpm | 40 - 75 rpm |
Users viewing this material also viewed the following:
- PolyOne Dynaflex™ D3204-1000-03 Thermoplastic Elastomer (TPE)
- Hong Kun Group Benzyl 4-(hydroxymethyl)tetrahydro-1(2H)-pyridinec Pharmaceutical Intermediate
- SABIC Innovative Plastics Ultem 1010A PEI (Europe-Africa-Middle East)
- Corning 7761 Potash Borosilicate Crushed/Powdered Glass
- CP-Polymer-Technik Wellamid® 6000 GVZ 45 HWCP 45% Glass Fiber Nylon 6, Impact Resistant, Good Surface Finish, Heat Stabilized, Dry
- Arlon Thermabond® 99A60X008 0.008" (0.203 mm) Uncured Silicone Rubber with PTFE Coated Fiberglass Carrier
- ArcelorMittal Extragal® Z100 Double-sided pure zinc galvanized steel
- Aaron Industries AVPP C 200-4 Virgin Polypropylene, No Break
- ATI Allegheny Ludlum Martensitic Stainless Steel Type 440A, Hardened + 204°C Temper
Copyright © lookpolymers.com All Rights Reserved