SABIC Innovative Plastics Xenoy® 1101 PBT+PC (Asia Pacific)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/Polybutylene Terephthalate (PBT) Blend, Unreinforced , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Xenoy® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Xenoy® 1101 PBT+PC (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Unreinforced, opaque polycarbonate/polyester alloy. Excellent low temperature impact plus chemical resistance to automotive fluid.This data was supplied by SABIC-IP for the Asia Pacific region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.21 g/cc | 1.21 g/cc | ASTM D 792 |
| Linear Mold Shrinkage, Flow | 0.0080 - 0.010 cm/cm @Thickness 3.20 mm |
0.0080 - 0.010 in/in @Thickness 0.126 in |
SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 58.0 MPa | 8410 psi | Type I, 50 mm/min; ASTM D 638 |
| Tensile Strength, Yield | 52.0 MPa | 7540 psi | Type I, 50 mm/min; ASTM D 638 |
| Elongation at Break | 120 % | 120 % | Type I, 50 mm/min; ASTM D 638 |
| Flexural Yield Strength | 84.0 MPa | 12200 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Flexural Modulus | 2.04 GPa | 296 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Izod Impact, Notched | 2.99 J/cm @Temperature -40.0 °C |
5.60 ft-lb/in @Temperature -40.0 °F |
ASTM D 256 |
| 6.08 J/cm @Temperature -20.0 °C |
11.4 ft-lb/in @Temperature -4.00 °F |
ASTM D 256 | |
| 6.78 J/cm @Temperature 0.000 °C |
12.7 ft-lb/in @Temperature 32.0 °F |
ASTM D 256 | |
| 7.10 J/cm @Temperature 23.0 °C |
13.3 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 | |
| Gardner Impact | 54.0 J @Temperature 23.0 °C |
39.8 ft-lb @Temperature 73.4 °F |
ASTM D 3029 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 90.0 µm/m-°C @Temperature -40.0 - 95.0 °C |
50.0 µin/in-°F @Temperature -40.0 - 203 °F |
ASTM E 831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 106 °C @Thickness 6.40 mm |
223 °F @Thickness 0.252 in |
unannealed; ASTM D 648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 98.0 °C @Thickness 6.40 mm |
208 °F @Thickness 0.252 in |
unannealed; ASTM D 648 |
Users viewing this material also viewed the following:
- Polykemi AB POLYblend 50LG PC/ABS-Blend, Low Gloss
- SABIC Innovative Plastics Lexan® EXL1112 PC Copolymer
- SABIC Innovative Plastics Valox® 4012G PBT
- Saint-Gobain CHR® SG56-03(R) Anti-Static Glass-PTFE Backing Silicone Adhesive Pressure Sensitive Tape
- Teknor Apex Sarlink® 4145 Thermoplastic Elastomer
- Wellman Wellamid® 22L-N Unfilled Nylon 66, Lubricated
- Lubrizol ESTANE® 5722 Ester Based Thermoplastic Polyurethane (European Grade)
- DuPont™ Nomex® Type 993, 95 mil Nominal Thickness Medium-Density Aromatic Nylon Pressboard
- Eurofoam Porocell POR 301/F NR-SBR Foam
- ConocoPhillips HD Fleet Supreme™ 15W-40 Engine Oil
Copyright © lookpolymers.com All Rights Reserved