Lanxess Pocan® T 7331 POS151 700226 PBT + PET, 30% Glass Fiber

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , PBT + PET Blend, Glass Filled , Polyethylene Terephthalate (PET)
Manufacturer Lanxess
Trade Name Pocan®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Lanxess Pocan® T 7331 POS151 700226 PBT + PET, 30% Glass Fiber.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PBT + PET, 30% glass fibers, injection molding, improved surface finish, increased temperature peak load, UV stabilizedInformation provided by LANXESS.
Physical Properties Metric English Comments
Specific Gravity 1.55 g/cc
1.55 g/cc
ISO 1183
Bulk Density 0.800 g/cc
0.0289 lb/in³
ISO 60
Moisture Absorption at Equilibrium 0.10 %
0.10 %
50% RH; ISO 62
Water Absorption at Saturation 0.30 %
0.30 %
ISO 62
Viscosity Test 91 cm³/g
91 cm³/g
Viscosity number; ISO 1628-5
Linear Mold Shrinkage, Flow 0.0010 cm/cm
0.0010 in/in
Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4
0.0030 cm/cm
0.0030 in/in
60x60x2; 270°C / MT 90°C; 600 bar; ISO 294-4
Linear Mold Shrinkage, Transverse 0.0020 cm/cm
0.0020 in/in
Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4
0.0090 cm/cm
0.0090 in/in
60x60x2; 270°C / MT 90°C; 600 bar; ISO 294-4
Melt Flow 30 g/10 min

@Load 5.00 kg,
Temperature 260 °C
 30 g/10 min

@Load 11.0 lb,
Temperature 500 °F
 ISO 1133-1
Mechanical Properties Metric English Comments
Ball Indentation Hardness 200 MPa
29000 psi
ISO 2039-1
Tensile Strength at Break 145 MPa
21000 psi
ISO 527-1, -2; 5 mm/min
Elongation at Break 2.8 %
2.8 %
ISO 527-1, -2; 5 mm/min
Tensile Modulus 10.4 GPa
1510 ksi
ISO 527-1, -2; 1 mm/min
Flexural Strength 230 MPa

@Strain 3.00 %
 33400 psi

@Strain 3.00 %
 2 mm/min; ISO 178-A
Flexural Modulus 10.3 GPa
1490 ksi
2 mm/min; ISO 178-A
Izod Impact, Notched (ISO) <= 10.0 kJ/m²

@Temperature 23.0 °C
 <= 4.76 ft-lb/in²

@Temperature 73.4 °F
 ISO 180-1A
<= 10.0 kJ/m²

@Temperature -30.0 °C
 <= 4.76 ft-lb/in²

@Temperature -22.0 °F
 ISO 180-1A
<= 10.0 kJ/m²

@Temperature -40.0 °C
 <= 4.76 ft-lb/in²

@Temperature -40.0 °F
 ISO 180-1A
Izod Impact, Unnotched (ISO) 55.0 kJ/m²

@Temperature 23.0 °C
 26.2 ft-lb/in²

@Temperature 73.4 °F
 ISO 180-1U
55.0 kJ/m²

@Temperature -30.0 °C
 26.2 ft-lb/in²

@Temperature -22.0 °F
 ISO 180-1U
Charpy Impact Unnotched 5.50 J/cm²

@Temperature -30.0 °C
 26.2 ft-lb/in²

@Temperature -22.0 °F
 ISO 179-1eU
6.50 J/cm²

@Temperature 23.0 °C
 30.9 ft-lb/in²

@Temperature 73.4 °F
 ISO 179-1eU
Charpy Impact, Notched <= 1.00 J/cm²

@Temperature 23.0 °C
 <= 4.76 ft-lb/in²

@Temperature 73.4 °F
 ISO 179-1eA
<= 1.00 J/cm²

@Temperature -30.0 °C
 <= 4.76 ft-lb/in²

@Temperature -22.0 °F
 ISO 179-1eA
Puncture Energy 2.10 J

@Load <=66.3 kg,
Temperature 23.0 °C
 1.55 ft-lb

@Load <=146 lb,
Temperature 73.4 °F
 ISO 6603-2
Tensile Creep Modulus, 1 hour 10000 MPa
1.45e+6 psi
ISO 899-1
Tensile Creep Modulus, 1000 hours 8500 MPa
1.23e+6 psi
ISO 899-1
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 30.0 µm/m-°C

@Temperature 23.0 - 55.0 °C
 16.7 µin/in-°F

@Temperature 73.4 - 131 °F
 ISO 11359-1, -2
CTE, linear, Transverse to Flow 60.0 µm/m-°C

@Temperature 23.0 - 55.0 °C
 33.3 µin/in-°F

@Temperature 73.4 - 131 °F
 ISO 11359-1, -2
Thermal Conductivity 0.270 W/m-K
1.87 BTU-in/hr-ft²-°F
ISO 8302
Melting Point 225 - 250 °C
437 - 482 °F
10°C/min; ISO 11357-1, -3
Maximum Service Temperature, Air 140 °C
284 °F
IEC 60216-1, Tensile impact strength, 20000 h
155 °C
311 °F
IEC 60216-1, Tensile strength, 20000 h
155 °C
311 °F
IEC 60216-1, Electric strength, 20000 h
220 °C
428 °F
Resistance to heat - ball pressure test; IEC 60695-10-2
Deflection Temperature at 0.46 MPa (66 psi) 220 °C
428 °F
ISO 75-1, -2
Deflection Temperature at 1.8 MPa (264 psi) 200 °C
392 °F
ISO 75-1, -2
Vicat Softening Point 205 °C

@Load 5.10 kg
 401 °F

@Load 11.2 lb
 120°C/hour; ISO 306
UL RTI, Electrical 140 °C
284 °F
UL 746B
UL RTI, Mechanical with Impact 125 °C
257 °F
UL 746B
UL RTI, Mechanical without Impact 140 °C
284 °F
UL 746B
Flammability, UL94 HB

@Thickness 1.60 mm
 HB

@Thickness 0.0630 in
HB

@Thickness 0.800 mm
 HB

@Thickness 0.0315 in
Oxygen Index 21 %
21 %
Method A; ISO 4589-2
Glow Wire Test 750 °C

@Diameter 2.00 mm
 1380 °F

@Diameter 0.0787 in
 GWFI; IEC 60695-2-12
Electrical Properties Metric English Comments
Dielectric Constant 3.8

@Frequency 1.00e+6 Hz
 3.8

@Frequency 1.00e+6 Hz
 IEC 60250
4.0

@Frequency 100 Hz
 4.0

@Frequency 100 Hz
 IEC 60250
Dielectric Strength 27.0 kV/mm

@Thickness 1.00 mm
 686 kV/in

@Thickness 0.0394 in
 IEC 60243-1
Comparative Tracking Index 250 V
250 V
d.a.m.; Solution A; IEC 60112
Processing Properties Metric English Comments
Melt Temperature 260 - 280 °C
500 - 536 °F
270 °C
518 °F
for test specimens; ISO 294
Mold Temperature 80.0 - 100 °C
176 - 212 °F
90.0 °C
194 °F
for test specimens; ISO 294
Drying Temperature 120 °C
248 °F
Dry Time 4 - 8 hour
4 - 8 hour
Moisture Content 0.00 - 0.020 %
0.00 - 0.020 %
residual; Karl Fischer Test
Descriptive Properties Value Comments
Electrolytic Corrosion IEC 60426
A 1
Halving Interval (°C) 10.2
IEC 60216-1, Tensile strength
10.2
IEC 60216-1, Electric strength
13.5
IEC 60216-1, Tensile impact strength
ISO Shortname ISO 7792-1-PBT+PET, GHlMR, 09-100, GF30