Lanxess Pocan® BF 4130 XF 000000 PBT, 30% Glass Fiber
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), Glass Fiber Filled, Flame Retardant |
| Manufacturer | Lanxess |
| Trade Name | Pocan® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Pocan® BF 4130 XF 000000 PBT, 30% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PBT, 30% glass fibers, injection molding, flame retardant, improved flowabilityInformation provided by LANXESS.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.62 g/cc | 1.62 g/cc | ISO 1183 |
| Bulk Density | 0.700 g/cc | 0.0253 lb/in³ | ISO 60 |
| Viscosity Test | 62 cm³/g | 62 cm³/g | Viscosity number; ISO 1628-5 |
| Linear Mold Shrinkage, Flow | 0.0010 cm/cm | 0.0010 in/in | Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4 |
| 0.0030 cm/cm | 0.0030 in/in | 60x60x2; 250°C / WZ 80°C; 600 bar; ISO 294-4 | |
| Linear Mold Shrinkage, Transverse | 0.0010 cm/cm | 0.0010 in/in | Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4 |
| 0.0080 cm/cm | 0.0080 in/in | 60x60x2; 250°C / WZ 80°C; 600 bar; ISO 294-4 | |
| Melt Flow | 17 g/10 min @Load 2.16 kg, Temperature 260 °C |
17 g/10 min @Load 4.76 lb, Temperature 500 °F |
ISO 1133-1 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 160 MPa | 23200 psi | ISO 2039-1 |
| Tensile Strength at Break | 130 MPa | 18900 psi | ISO 527-1, -2; 5 mm/min |
| Elongation at Break | 2.2 % | 2.2 % | ISO 527-1, -2; 5 mm/min |
| Tensile Modulus | 10.5 GPa | 1520 ksi | ISO 527-1, -2; 1 mm/min |
| Flexural Strength | 200 MPa @Strain 2.60 % |
29000 psi @Strain 2.60 % |
2 mm/min; ISO 178-A |
| Flexural Modulus | 10.0 GPa | 1450 ksi | 2 mm/min; ISO 178-A |
| Izod Impact, Notched (ISO) | <= 10.0 kJ/m² @Temperature 23.0 °C |
<= 4.76 ft-lb/in² @Temperature 73.4 °F |
ISO 180-1A |
| <= 10.0 kJ/m² @Temperature -30.0 °C |
<= 4.76 ft-lb/in² @Temperature -22.0 °F |
ISO 180-1A | |
| Izod Impact, Unnotched (ISO) | 50.0 kJ/m² @Temperature -30.0 °C |
23.8 ft-lb/in² @Temperature -22.0 °F |
ISO 180-1U |
| 55.0 kJ/m² @Temperature 23.0 °C |
26.2 ft-lb/in² @Temperature 73.4 °F |
ISO 180-1U | |
| Charpy Impact Unnotched | 5.00 J/cm² @Temperature -30.0 °C |
23.8 ft-lb/in² @Temperature -22.0 °F |
ISO 179-1eU |
| 5.50 J/cm² @Temperature 23.0 °C |
26.2 ft-lb/in² @Temperature 73.4 °F |
ISO 179-1eU | |
| Charpy Impact, Notched | <= 1.00 J/cm² @Temperature 23.0 °C |
<= 4.76 ft-lb/in² @Temperature 73.4 °F |
ISO 179-1eA |
| <= 1.00 J/cm² @Temperature -30.0 °C |
<= 4.76 ft-lb/in² @Temperature -22.0 °F |
ISO 179-1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 20.0 µm/m-°C @Temperature 23.0 - 55.0 °C |
11.1 µin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359-1, -2 |
| CTE, linear, Transverse to Flow | 90.0 µm/m-°C @Temperature 23.0 - 55.0 °C |
50.0 µin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359-1, -2 |
| Melting Point | 228 °C | 442 °F | 10°C/min; ISO 11357-1, -3 |
| Maximum Service Temperature, Air | 215 °C | 419 °F | Resistance to heat - ball pressure test; IEC 60695-10-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ISO 75-1, -2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | ISO 75-1, -2 |
| Vicat Softening Point | 205 °C @Load 5.10 kg |
401 °F @Load 11.2 lb |
120°C/hour; ISO 306 |
| Flammability, UL94 | V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
|
| V-0 @Thickness 0.750 mm |
V-0 @Thickness 0.0295 in |
||
| Glow Wire Test | 775 °C @Diameter 0.800 mm |
1430 °F @Diameter 0.0315 in |
GWIT; IEC 60695-2-13 |
| 775 °C @Diameter 1.50 mm |
1430 °F @Diameter 0.0591 in |
GWIT; IEC 60695-2-13 | |
| 775 °C @Diameter 3.00 mm |
1430 °F @Diameter 0.118 in |
GWIT; IEC 60695-2-13 | |
| 960 °C @Diameter 0.800 mm |
1760 °F @Diameter 0.0315 in |
GWFI; IEC 60695-2-12 | |
| 960 °C @Diameter 1.50 mm |
1760 °F @Diameter 0.0591 in |
GWFI; IEC 60695-2-12 | |
| 960 °C @Diameter 3.00 mm |
1760 °F @Diameter 0.118 in |
GWFI; IEC 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Comparative Tracking Index | 200 V | 200 V | d.a.m.; Solution A; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 240 - 260 °C | 464 - 500 °F | |
| 250 °C | 482 °F | for test specimens; ISO 294 | |
| Mold Temperature | 80.0 °C | 176 °F | for test specimens; ISO 294 |
| 80.0 - 100 °C | 176 - 212 °F | ||
| Drying Temperature | 120 °C | 248 °F | |
| Dry Time | 4 - 8 hour | 4 - 8 hour | |
| Moisture Content | 0.00 - 0.020 % | 0.00 - 0.020 % | residual; Karl Fischer Test |
| Descriptive Properties | Value | Comments |
|---|---|---|
| ISO Shortname | ISO 7792-PBT, GFHR, 07-100, GF30; ISO 1043-PBT GF FR(17) |
Users viewing this material also viewed the following:
- Polymer Resources NY66-GP1 General Purpose Nylon 66
- Polimeri Europa SINKRAL B733/E ABS, Impact & Heat Stabilized Grade (discontinued **)
- Indium Corp. Indalloy 85 Bismuth-Lead-Tin Solder Alloy
- Haynes Hastelloy® C-22® alloy, GTAW, as welded, notched
- Techmer ES Plastiblend® ABS E
- A. Schulman POLYBATCH™ Green 3600 Concentrate Based In Polyethylene
- DuPont Performance Polymers Zytel® HTN 54G15HSLR NC010 Polyphthalamide (PPA) (Unverified Data**)