Lanxess Pocan® B 3235 000000 PBT, 30% Glass Fiber

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 30% Glass Fiber Filled
Manufacturer Lanxess
Trade Name Pocan®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Lanxess Pocan® B 3235 000000 PBT, 30% Glass Fiber.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PBT, 30% glass fibers, injection molding
Physical Properties Metric English Comments
Density 1.55 g/cc
0.0560 lb/in³
ISO 1183
Water Absorption 0.40 %
0.40 %
Test Sim. to ISO 62
Moisture Absorption at Equilibrium 0.10 %
0.10 %
23°C/50% R.H.; Test Sim. to ISO 62
Viscosity Test 95 cm³/g
95 cm³/g
Viscosity number; ISO 307, 1157, 1628
Melt Flow 25 g/10 min

@Load 2.16 kg,
Temperature 260 °C
 25 g/10 min

@Load 4.76 lb,
Temperature 500 °F
 Estimated using room temperature density; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 140 MPa
20300 psi
ISO 527-1/-2
Elongation at Break 2.5 %
2.5 %
ISO 527-1/-2
Tensile Modulus 10.0 GPa
1450 ksi
ISO 527-1/-2
Charpy Impact Unnotched 6.00 J/cm²

@Temperature -30.0 °C
 28.6 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/1eU
6.50 J/cm²

@Temperature 23.0 °C
 30.9 ft-lb/in²

@Temperature 73.4 °F
 ISO 179/1eU
Charpy Impact, Notched <= 1.00 J/cm²

@Temperature -30.0 °C
 <= 4.76 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/1eA
1.00 J/cm²

@Temperature 23.0 °C
 4.76 ft-lb/in²

@Temperature 73.4 °F
 ISO 179/1eA
Puncture Energy 2.30 J
1.70 ft-lb
ISO 6603-2
2.50 J

@Temperature -30.0 °C
 1.84 ft-lb

@Temperature -22.0 °F
 ISO 6603-2
Tensile Creep Modulus, 1 hour 9800 MPa
1.42e+6 psi
ISO 899-1
Tensile Creep Modulus, 1000 hours 8900 MPa
1.29e+6 psi
ISO 899-1
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 30.0 µm/m-°C
16.7 µin/in-°F
ISO 11359-1/-2
CTE, linear, Transverse to Flow 90.0 µm/m-°C
50.0 µin/in-°F
ISO 11359-1/-2
Melting Point 225 °C
437 °F
10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi) 220 °C
428 °F
ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 210 °C
410 °F
ISO 75-1/-2
Deflection Temperature at 8.0 MPa 165 °C
329 °F
ISO 75-1/-2
Vicat Softening Point 215 °C
419 °F
50°C/h 50N; ISO 306
Flammability, UL94 HB

@Thickness 0.800 mm
 HB

@Thickness 0.0315 in
 IEC 60695-11-10
HB

@Thickness 1.60 mm
 HB

@Thickness 0.0630 in
 IEC 60695-11-10
Oxygen Index 20 %
20 %
ISO 4589-1/-2
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+15 ohm-cm
>= 1.00e+15 ohm-cm
IEC 60093
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
IEC 60093
Dielectric Constant 3.8

@Frequency 1.00e+6 Hz
 3.8

@Frequency 1.00e+6 Hz
 IEC 60250
4.0

@Frequency 100 Hz
 4.0

@Frequency 100 Hz
 IEC 60250
Dielectric Strength 29.0 kV/mm
737 kV/in
IEC 60243-1
Dissipation Factor 0.0030

@Frequency 100 Hz
 0.0030

@Frequency 100 Hz
 IEC 60250
0.018

@Frequency 1.00e+6 Hz
 0.018

@Frequency 1.00e+6 Hz
 IEC 60250
Comparative Tracking Index 350 V
350 V
IEC 60112
Processing Properties Metric English Comments
Melt Temperature 260 °C
500 °F
Injection Molding; ISO 294
Mold Temperature 80.0 °C
176 °F
Injection Molding; ISO 10724
Descriptive Properties Value Comments
Additives Release agent
Form Pellets
ISO Shortname ISO 7792-1-PBT,GHMR,09-100,GF30
Processing Injection molding
Region Asia Pacific
Europe
Near East/Africa
North America
South and Central America