- Lanxess Durethan® BKV 50 H3.0 000000 Nylon 6, 50% Glass Fibers
Lanxess Durethan® BKV 50 H3.0 000000 Nylon 6, 50% Glass Fibers
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 50% Glass Fiber Filled |
| Manufacturer | Lanxess |
| Trade Name | Durethan® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Durethan® BKV 50 H3.0 000000 Nylon 6, 50% Glass Fibers.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PA 6, 50% glass fibers, injection molding, heat-ageing stabilized
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.57 g/cc | 1.57 g/cc | ISO 1183 |
| Bulk Density | 0.700 g/cc | 0.0253 lb/in³ | ISO 60 |
| Moisture Absorption at Equilibrium | 1.5 % | 1.5 % | 50% RH; ISO 62 |
| Water Absorption at Saturation | 5.0 % | 5.0 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0016 cm/cm @Thickness 3.00 mm |
0.0016 in/in @Thickness 0.118 in |
Mold Temp 80°C; Melt Temp 280°C; 400 bar; ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0085 cm/cm @Thickness 3.00 mm |
0.0085 in/in @Thickness 0.118 in |
Mold Temp 80°C; Melt Temp 280°C; 400 bar; ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 140 MPa | 20300 psi | Conditioned; ISO 527-1,-2 |
| 220 MPa | 31900 psi | ISO 527-1,-2 | |
| Elongation at Break | 3.0 % | 3.0 % | ISO 527-1,-2 |
| 5.0 % | 5.0 % | Conditioned; ISO 527-1,-2 | |
| Tensile Modulus | 9.50 GPa | 1380 ksi | Conditioned; ISO 527-1,-2 |
| 14.5 GPa | 2100 ksi | ISO 527-1,-2 | |
| Flexural Strength | 230 MPa @Strain 5.00 % |
33400 psi @Strain 5.00 % |
Conditioned; ISO 178 |
| 360 MPa @Strain 3.00 % |
52200 psi @Strain 3.00 % |
ISO 178 | |
| Flexural Yield Strength | 230 MPa @Strain 5.00 % |
33400 psi @Strain 5.00 % |
Conditioned; ISO 178 |
| 360 MPa @Strain 3.00 % |
52200 psi @Strain 3.00 % |
ISO 178 | |
| Flexural Modulus | 9.00 GPa | 1310 ksi | Conditioned; ISO 178 |
| 13.9 GPa | 2020 ksi | ISO 178 | |
| Izod Impact, Notched (ISO) | 15.0 kJ/m² @Temperature -30.0 °C |
7.14 ft-lb/in² @Temperature -22.0 °F |
ISO 180-1A |
| 15.0 kJ/m² @Temperature -30.0 °C |
7.14 ft-lb/in² @Temperature -22.0 °F |
Conditioned; ISO 180-1A | |
| 20.0 kJ/m² @Temperature 23.0 °C |
9.52 ft-lb/in² @Temperature 73.4 °F |
ISO 180-1A | |
| 25.0 kJ/m² @Temperature 23.0 °C |
11.9 ft-lb/in² @Temperature 73.4 °F |
Conditioned; ISO 180-1A | |
| Izod Impact, Unnotched (ISO) | 95.0 kJ/m² @Temperature 23.0 °C |
45.2 ft-lb/in² @Temperature 73.4 °F |
ISO 180-1U |
| 95.0 kJ/m² @Temperature -30.0 °C |
45.2 ft-lb/in² @Temperature -22.0 °F |
ISO 180-1U | |
| 95.0 kJ/m² @Temperature -30.0 °C |
45.2 ft-lb/in² @Temperature -22.0 °F |
Conditioned; ISO 180-1U | |
| 100 kJ/m² @Temperature 23.0 °C |
47.6 ft-lb/in² @Temperature 73.4 °F |
Conditioned; ISO 180-1U | |
| Charpy Impact Unnotched | 9.00 J/cm² @Temperature -30.0 °C |
42.8 ft-lb/in² @Temperature -22.0 °F |
ISO 179-1eU |
| 9.00 J/cm² @Temperature -30.0 °C |
42.8 ft-lb/in² @Temperature -22.0 °F |
Conditioned; ISO 179-1eU | |
| 10.0 J/cm² @Temperature 23.0 °C |
47.6 ft-lb/in² @Temperature 73.4 °F |
ISO 179-1eU | |
| 11.0 J/cm² @Temperature 23.0 °C |
52.3 ft-lb/in² @Temperature 73.4 °F |
Conditioned; ISO 179-1eU | |
| Charpy Impact, Notched | 1.50 J/cm² @Temperature -30.0 °C |
7.14 ft-lb/in² @Temperature -22.0 °F |
ISO 179-1eA |
| 1.50 J/cm² @Temperature -30.0 °C |
7.14 ft-lb/in² @Temperature -22.0 °F |
Conditioned; ISO 179-1eA | |
| 2.00 J/cm² @Temperature 23.0 °C |
9.52 ft-lb/in² @Temperature 73.4 °F |
ISO 179-1eA | |
| 2.50 J/cm² @Temperature 23.0 °C |
11.9 ft-lb/in² @Temperature 73.4 °F |
Conditioned; ISO 179-1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 20.0 µm/m-°C | 11.1 µin/in-°F | ISO 11359-1,-2 |
| CTE, linear, Transverse to Flow | 70.0 µm/m-°C | 38.9 µin/in-°F | ISO 11359-1,-2 |
| Melting Point | 222 °C | 432 °F | ISO 11357-1,-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 215 °C | 419 °F | ISO 75-1,-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | ISO 75-1,-2 |
| Vicat Softening Point | >= 200 °C @Load 5.10 kg |
>= 392 °F @Load 11.2 lb |
120°C/h; ISO 306 |
| >= 200 °C @Load 5.10 kg |
>= 392 °F @Load 11.2 lb |
50°C/h; ISO 306 | |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
||
| Glow Wire Test | 650 °C @Diameter 2.00 mm |
1200 °F @Diameter 0.0787 in |
IEC 60695-2-12 |
| Shrinkage | 0.020 % @Temperature 120 °C, Time 14400 sec |
0.020 % @Temperature 248 °F, Time 4.00 hour |
Molding Post-shrinkage; ISO 294-4 |
| 0.050 % @Temperature 120 °C, Time 14400 sec |
0.050 % @Temperature 248 °F, Time 4.00 hour |
Molding Post-shrinkage; ISO 294-4 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 280 °C | 536 °F | Processing conditions for test specimens; ISO 294 |
| 270 - 290 °C | 518 - 554 °F | Recommended | |
| Mold Temperature | 80.0 °C | 176 °F | Processing conditions for test specimens; ISO 294 |
| 80.0 - 120 °C | 176 - 248 °F | Recommended | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Dry Time | 2 - 6 hour | 2 - 6 hour | |
| Moisture Content | 0.030 - 0.12 % | 0.030 - 0.12 % | Residual; Acc. To Karl Fischer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Flammability | Passed US-FMVSS302 | ISO 3795 |
| ISO Shortname | ISO 1874-PA 6,GHR,14-140,GF50 |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Dry Blend E7001 Polyvinyl Chloride, Rigid (PVC, Rigid)
- Plansee DENAL® 917 108 XXX (3) Tungsten-Nickel-Iron-Cobalt Alloy
- Polymer Resources PC-UV3-D Polycarbonate, UV-stabilized, High Flow
- STAR Thermoplastic Alloys & Rubbers StarFlex® P 7360-9000 TPE
- Saint-Gobain Tygon® S3™ B-44-4X I.B. Pressure Tubing Formulation for filling, draining, transfer and processing applications
- Polyram Polytron P20B01 Homopolymer Polypropylene, Chemically Coupled 20% Long Fiber
- DuPont Teijin Films Mylar® RL43 Polyester Packaging Film, 100 Gauge
- PolyOne Lubri-Tech™ NI-10CF/15T Nylon 6/10, Carbon Fiber Reinforced, PTFE Lubricated (discontinued **)
- Budd DSM-949, Diesel Grade SMC, Vinyl Ester, Black (discontinued **)
Copyright © lookpolymers.com All Rights Reserved