SABIC Innovative Plastics LNP LUBRICOMP ECL36 PEI (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP ECL36 PEI (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Lubricomp* ECL36 is a compound based on Polyetherimide resin containing PTFE, Carbon Fiber. Added features of this material include: Internally Lubricated.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.48 g/cc | 0.0535 lb/in³ | ASTM D792 |
| 1.50 g/cc | 0.0542 lb/in³ | ISO 1183 | |
| Linear Mold Shrinkage, Flow | 0.00040 cm/cm @Time 86400 sec |
0.00040 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0040 cm/cm @Time 86400 sec |
0.0040 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 160 MPa | 23200 psi | ISO 527 |
| 179 MPa | 26000 psi | ASTM D638 | |
| Elongation at Break | 1.2 % | 1.2 % | ISO 527 |
| 1.7 % | 1.7 % | ASTM D638 | |
| Tensile Modulus | 21.6 GPa | 3130 ksi | 1 mm/min; ISO 527 |
| Flexural Strength | 210 MPa | 30500 psi | ISO 178 |
| 230 MPa | 33400 psi | ASTM D790 | |
| Flexural Modulus | 16.0 GPa | 2320 ksi | ISO 178 |
| 19.16 GPa | 2779 ksi | ASTM D790 | |
| Izod Impact, Notched | 0.420 J/cm | 0.787 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 2.67 J/cm | 5.00 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 18.0 kJ/m² | 8.57 ft-lb/in² | 80*10*4; ISO 180/1U |
| Coefficient of Friction, Dynamic | 0.39 | 0.39 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.48 | 0.48 | ASTM D3702 Modified |
| K (wear) Factor | 62.4 x 10-8 mm³/N-M | 31.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 10 - 1.00e+6 ohm | 10 - 1.00e+6 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- Qualchem Danamid FCP-40 Polyamide 6, 40% Carbon Fiber
- NOVA Chemicals Sclair® 2714 HDPE Injection Molding Resin
- Polykemi AB POLYfill PPH K8040 Polypropylene Homopolymer, Mineral Reinforced
- Lehmann & Voss LUVOCOM® 19-7660 Polyamide 46, with glass fiber, PTFE, lubricant modified
- SABIC Innovative Plastics LNP LUBRICOMP WG003 PBT (Europe-Africa-Middle East)
- Unitika A1030BRL PA6, Dry
- ChevronTexaco Meropa® 1500
Copyright © lookpolymers.com All Rights Reserved