Stellarchem DIOSHY® MP-960NC TPE Compound
| Category | Polymer , Thermoplastic , Elastomer, TPE , Olefinic TPE |
| Manufacturer | Stellarchem |
| Trade Name | DIOSHY® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Stellarchem DIOSHY® MP-960NC TPE Compound.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
This grade of Stellarchem MP series is shear dependent and can be processed on conventional thermoplastics equipment for injection molding or extrusion. It's a soft, styrene block copolymers based, completely recyclable, colorable & non-hygroscopic thermoplastics elastomer material. It's formulated to overmold to PP thermoplastics in normal dual injection & extrusion processing.Information provided by Stellarchem Polymer & Industrial
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.930 g/cc | 0.0336 lb/in³ | |
| Particle Mesh Size | 80 - 150 Mesh | 80 - 150 Mesh | |
| Melt Flow | 26.9 g/10 min | 26.9 g/10 min | JIS K7210 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 59 | 59 | JIS K6301 |
| Tensile Strength, Ultimate | 0.883 MPa | 128 psi | JIS K6301 |
| Elongation at Break | 662 % | 662 % | JIS K6301 |
| 100% Modulus | 0.00588 GPa | 0.853 ksi | JIS K6301 |
| 300% Modulus | 0.000490 GPa | 0.0711 ksi | JIS K6301 |
| Tear Strength | 1.33 kN/m | 7.62 pli | JIS K6301-B |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 190 - 205 °C | 374 - 401 °F | Metering Temperature, Extrusion |
| Rear Barrel Temperature | 160 - 190 °C | 320 - 374 °F | Injection Molding |
| 180 - 190 °C | 356 - 374 °F | Extrusion | |
| Middle Barrel Temperature | 170 - 190 °C | 338 - 374 °F | Injection Molding |
| 185 - 195 °C | 365 - 383 °F | Transition, Extrusion | |
| Front Barrel Temperature | 180 - 200 °C | 356 - 392 °F | Injection Molding |
| 195 - 210 °C | 383 - 410 °F | Extrusion | |
| Nozzle Temperature | 190 - 210 °C | 374 - 410 °F | Injection Molding |
| Die Temperature | 195 - 210 °C | 383 - 410 °F | Extrusion |
| Melt Temperature | 170 - 210 °C | 338 - 410 °F | Injection Molding |
| 190 - 210 °C | 374 - 410 °F | Extrusion | |
| Mold Temperature | 25.0 - 40.0 °C | 77.0 - 104 °F | Injection Molding |
| Injection Pressure | 5.00 - 40.0 MPa | 725 - 5800 psi | Injection Molding |
| Back Pressure | 0.500 - 1.00 MPa | 72.5 - 145 psi | Injection Molding |
| Screw Speed | 60 - 100 rpm | 60 - 100 rpm | Extrusion |
| 100 - 200 rpm | 100 - 200 rpm | Injection Molding |
Users viewing this material also viewed the following:
- KiON CERASET® POLYSILAZANE 20 (PSZ 20)
- Saint-Gobain CHR® M852 Polyester Film Backing Natural Rubber Adhesive Pressure Sensitive Tape
- A. Schulman POLYBATCH™ Brown 1281 Concentrate Based In Polyethylene
- Cheng Yu Plastic NG1250S Nylon 66, 25% Glass Fiber Reinforced
- Dow Corning MOLYKOTE® 44 HIGH TEMPERATURE BEARING GREASE, MEDIUM
- Eurotec® Tecomid® NA40 KC50 BK111 PA6.6, 50% glass/carbon fiber reinforced, black
- Fainplast Compounds PG 50 Flexible PVC, Extrusion Modified with Rubber
- 3M 2A26 Co-Extruded Multi-Polymer Protect Tapes
- DuPont Performance Polymers Delrin® FG100TL NC010 Acetal Homopolymer (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved