Lanxess Durethan® BKV 215 H3.0 000000 Nylon 6-Copolymer, 15% Glass Fibers
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 20% Glass Fiber Filled |
| Manufacturer | Lanxess |
| Trade Name | Durethan® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Durethan® BKV 215 H3.0 000000 Nylon 6-Copolymer, 15% Glass Fibers.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PA 6-Copolymer, 15% glass fibers, injection molding, impact modified
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.18 g/cc | 1.18 g/cc | ISO 1183 |
| Bulk Density | 0.600 g/cc | 0.0217 lb/in³ | ISO 60 |
| Moisture Absorption at Equilibrium | 2.0 % | 2.0 % | 50% RH; ISO 62 |
| Water Absorption at Saturation | 7.0 % | 7.0 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm @Thickness 3.00 mm |
0.0030 in/in @Thickness 0.118 in |
Mold Temp 80°C; Melt Temp 280°C; 400 bar; ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0083 cm/cm @Thickness 3.00 mm |
0.0083 in/in @Thickness 0.118 in |
Mold Temp 80°C; Melt Temp 280°C; 400 bar; ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 55.0 MPa | 7980 psi | Conditioned; ISO 527-1,-2 |
| 85.0 MPa | 12300 psi | ISO 527-1,-2 | |
| Elongation at Break | 4.5 % | 4.5 % | ISO 527-1,-2 |
| 15 % | 15 % | Conditioned; ISO 527-1,-2 | |
| Tensile Modulus | 2.40 GPa | 348 ksi | Conditioned; ISO 527-1,-2 |
| 4.50 GPa | 653 ksi | ISO 527-1,-2 | |
| Flexural Strength | 75.0 MPa @Strain 8.50 % |
10900 psi @Strain 8.50 % |
Conditioned; ISO 178 |
| 130 MPa @Strain 5.50 % |
18900 psi @Strain 5.50 % |
ISO 178 | |
| Flexural Yield Strength | 55.0 MPa @Strain 3.50 % |
7980 psi @Strain 3.50 % |
Conditioned; ISO 178 |
| 125 MPa @Strain 3.50 % |
18100 psi @Strain 3.50 % |
ISO 178 | |
| Flexural Modulus | 2.20 GPa | 319 ksi | Conditioned; ISO 178 |
| 3.80 GPa | 551 ksi | ISO 178 | |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² @Temperature -30.0 °C |
4.76 ft-lb/in² @Temperature -22.0 °F |
ISO 180-1A |
| 10.0 kJ/m² @Temperature -30.0 °C |
4.76 ft-lb/in² @Temperature -22.0 °F |
Conditioned; ISO 180-1A | |
| 20.0 kJ/m² @Temperature 23.0 °C |
9.52 ft-lb/in² @Temperature 73.4 °F |
ISO 180-1A | |
| 30.0 kJ/m² @Temperature 23.0 °C |
14.3 ft-lb/in² @Temperature 73.4 °F |
Conditioned; ISO 180-1A | |
| Izod Impact, Unnotched (ISO) | 50.0 kJ/m² @Temperature -30.0 °C |
23.8 ft-lb/in² @Temperature -22.0 °F |
ISO 180-1U |
| 55.0 kJ/m² @Temperature -30.0 °C |
26.2 ft-lb/in² @Temperature -22.0 °F |
Conditioned; ISO 180-1U | |
| 60.0 kJ/m² @Temperature 23.0 °C |
28.6 ft-lb/in² @Temperature 73.4 °F |
ISO 180-1U | |
| 80.0 kJ/m² @Temperature 23.0 °C |
38.1 ft-lb/in² @Temperature 73.4 °F |
Conditioned; ISO 180-1U | |
| Charpy Impact Unnotched | 7.00 J/cm² @Temperature 23.0 °C |
33.3 ft-lb/in² @Temperature 73.4 °F |
ISO 179-1eU |
| 8.00 J/cm² @Temperature -30.0 °C |
38.1 ft-lb/in² @Temperature -22.0 °F |
ISO 179-1eU | |
| 8.00 J/cm² @Temperature -30.0 °C |
38.1 ft-lb/in² @Temperature -22.0 °F |
Conditioned; ISO 179-1eU | |
| 8.50 J/cm² @Temperature 23.0 °C |
40.4 ft-lb/in² @Temperature 73.4 °F |
Conditioned; ISO 179-1eU | |
| Charpy Impact, Notched | 1.20 J/cm² @Temperature -30.0 °C |
5.71 ft-lb/in² @Temperature -22.0 °F |
ISO 179-1eA |
| 1.20 J/cm² @Temperature -30.0 °C |
5.71 ft-lb/in² @Temperature -22.0 °F |
Conditioned; ISO 179-1eA | |
| 2.00 J/cm² @Temperature 23.0 °C |
9.52 ft-lb/in² @Temperature 73.4 °F |
ISO 179-1eA | |
| 3.50 J/cm² @Temperature 23.0 °C |
16.7 ft-lb/in² @Temperature 73.4 °F |
Conditioned; ISO 179-1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 40.0 µm/m-°C | 22.2 µin/in-°F | ISO 11359-1,-2 |
| CTE, linear, Transverse to Flow | 150 µm/m-°C | 83.3 µin/in-°F | ISO 11359-1,-2 |
| Melting Point | 213 °C | 415 °F | ISO 11357-1,-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 205 °C | 401 °F | ISO 75-1,-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 175 °C | 347 °F | ISO 75-1,-2 |
| Vicat Softening Point | 200 °C @Load 5.10 kg |
392 °F @Load 11.2 lb |
120°C/h; ISO 306 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
||
| Oxygen Index | 22 % | 22 % | Method A; ISO 4589-2 |
| Shrinkage | 0.050 % @Temperature 120 °C, Time 14400 sec |
0.050 % @Temperature 248 °F, Time 4.00 hour |
Molding Post-shrinkage; ISO 294-4 |
| 0.15 % @Temperature 120 °C, Time 14400 sec |
0.15 % @Temperature 248 °F, Time 4.00 hour |
Molding Post-shrinkage; ISO 294-4 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 260 - 290 °C | 500 - 554 °F | Recommended |
| 280 °C | 536 °F | Processing conditions for test specimens; ISO 294 | |
| Mold Temperature | 80.0 °C | 176 °F | Processing conditions for test specimens; ISO 294 |
| 80.0 - 100 °C | 176 - 212 °F | Recommended | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Dry Time | 2 - 6 hour | 2 - 6 hour | |
| Moisture Content | 0.030 - 1.12 % | 0.030 - 1.12 % | Residual; Acc. To Karl Fischer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| ISO Shortname | ISO 1874-PA 6/66-HI,GHR,14-050,GF15 |
Users viewing this material also viewed the following:
- Objet FullCure® 840 Vero Blue Resin for Rapid Prototyping
- Eastman Eastar 5445 PCTG Copolyester, Injection Molded (discontinued **)
- Techmer ES Electrablend® ABS CF30 BK 30% Carbon Filled
- Shinkong Synthetic Fibers Shinite® D202G15 PBT, 15% Glass Filled, Fire Retardant
- TIMCAL TIMREX® MB44 Primary Synthetic Graphite
- DSM Biomedical BioSpan® S SPU Segmented Polyether Polyurethane (SPU)
- Crucible Steel 440A Chromium Steel
- Aearo E-A-R Specialty Composites Isodamp® C-1000 Series TPE
- ATI Allegheny Ludlum Ohmaloy® 30 Resistance Alloy
- Techmer ES Statiblend® PPS GF23 IM BK 23% Glass Filled
Copyright © lookpolymers.com All Rights Reserved