- Lanxess Durethan® BKV 215 000000 Nylon 6-Copolymer, Glass Fiber Reinforced, Impact Modified
Lanxess Durethan® BKV 215 000000 Nylon 6-Copolymer, Glass Fiber Reinforced, Impact Modified
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Glass Filled, Impact Grade |
| Manufacturer | Lanxess |
| Trade Name | Durethan® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Durethan® BKV 215 000000 Nylon 6-Copolymer, Glass Fiber Reinforced, Impact Modified.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PA 6-Copolymer, 15% glass fibers, injection molding impact modifiedInformation provided by LANXESS.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.18 g/cc | 1.18 g/cc | ISO 1183 |
| Bulk Density | 0.600 g/cc | 0.0217 lb/in³ | ISO 60 |
| Moisture Absorption at Equilibrium | 2.0 % | 2.0 % | 50% RH; ISO 62 |
| Water Absorption at Saturation | 7.0 % | 7.0 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0014 cm/cm | 0.0014 in/in | Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4 |
| 0.0059 cm/cm | 0.0059 in/in | 60x60x2; 280°C / MT 80°C; 600 bar; ISO 294-4 | |
| Linear Mold Shrinkage, Transverse | 0.0015 cm/cm | 0.0015 in/in | Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4 |
| 0.0061 cm/cm | 0.0061 in/in | 60x60x2; 280°C / MT 80°C; 600 bar; ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 55.0 MPa | 7980 psi | ISO 2039-1 |
| 110 MPa | 16000 psi | ISO 2039-1 | |
| Tensile Strength at Break | 55.0 MPa | 7980 psi | cond.; ISO 527-1, -2; 5 mm/min |
| 85.0 MPa | 12300 psi | d.a.m.; ISO 527-1, -2; 5 mm/min | |
| Elongation at Break | 4.5 % | 4.5 % | d.a.m.; ISO 527-1, -2; 5 mm/min |
| 15 % | 15 % | cond.; ISO 527-1, -2; 5 mm/min | |
| Tensile Modulus | 2.40 GPa | 348 ksi | cond.; ISO 527-1, -2; 1 mm/min |
| 4.50 GPa | 653 ksi | d.a.m.; ISO 527-1, -2; 1 mm/min | |
| Flexural Strength | 80.0 MPa @Strain 7.00 % |
11600 psi @Strain 7.00 % |
cond., 2 mm/min; ISO 178-A |
| 130 MPa @Strain 5.00 % |
18900 psi @Strain 5.00 % |
d.a.m., 2 mm/min; ISO 178-A | |
| Flexural Yield Strength | 60.0 MPa @Strain 3.50 % |
8700 psi @Strain 3.50 % |
cond., 2 mm/min; ISO 178-A |
| 125 MPa @Strain 3.50 % |
18100 psi @Strain 3.50 % |
d.a.m., 2 mm/min; ISO 178-A | |
| Flexural Modulus | 2.20 GPa | 319 ksi | cond., 2 mm/min; ISO 178-A |
| 4.00 GPa | 580 ksi | d.a.m., 2 mm/min; ISO 178-A | |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² @Temperature -30.0 °C |
4.76 ft-lb/in² @Temperature -22.0 °F |
d.a.m.; ISO 180-1A |
| 10.0 kJ/m² @Temperature -30.0 °C |
4.76 ft-lb/in² @Temperature -22.0 °F |
cond.; ISO 180-1A | |
| 18.0 kJ/m² @Temperature 23.0 °C |
8.57 ft-lb/in² @Temperature 73.4 °F |
d.a.m.; ISO 180-1A | |
| 30.0 kJ/m² @Temperature 23.0 °C |
14.3 ft-lb/in² @Temperature 73.4 °F |
cond.; ISO 180-1A | |
| Charpy Impact Unnotched | 7.00 J/cm² @Temperature 23.0 °C |
33.3 ft-lb/in² @Temperature 73.4 °F |
d.a.m.; ISO 179-1eU |
| 7.50 J/cm² @Temperature -30.0 °C |
35.7 ft-lb/in² @Temperature -22.0 °F |
cond.; ISO 179-1eU | |
| 8.00 J/cm² @Temperature 23.0 °C |
38.1 ft-lb/in² @Temperature 73.4 °F |
cond.; ISO 179-1eU | |
| 8.00 J/cm² @Temperature -30.0 °C |
38.1 ft-lb/in² @Temperature -22.0 °F |
d.a.m.; ISO 179-1eU | |
| Charpy Impact, Notched | 1.20 J/cm² @Temperature -30.0 °C |
5.71 ft-lb/in² @Temperature -22.0 °F |
d.a.m.; ISO 179-1eA |
| 1.20 J/cm² @Temperature -30.0 °C |
5.71 ft-lb/in² @Temperature -22.0 °F |
cond.; ISO 179-1eA | |
| 2.00 J/cm² @Temperature 23.0 °C |
9.52 ft-lb/in² @Temperature 73.4 °F |
d.a.m.; ISO 179-1eA | |
| 3.50 J/cm² @Temperature 23.0 °C |
16.7 ft-lb/in² @Temperature 73.4 °F |
cond.; ISO 179-1eA | |
| Puncture Energy | 32.0 J @Temperature 23.0 °C |
23.6 ft-lb @Temperature 73.4 °F |
cond.; ISO 6603-2 |
| 4.80 J @Load <=66.3 kg, Temperature -30.0 °C |
3.54 ft-lb @Load <=146 lb, Temperature -22.0 °F |
d.a.m.; ISO 6603-2 | |
| 13.0 J @Load <=102.3 kg, Temperature 23.0 °C |
9.59 ft-lb @Load <=225.5 lb, Temperature 73.4 °F |
d.a.m.; ISO 6603-2 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 40.0 µm/m-°C @Temperature 23.0 - 55.0 °C |
22.2 µin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359-1, -2 |
| CTE, linear, Transverse to Flow | 150 µm/m-°C @Temperature 23.0 - 55.0 °C |
83.3 µin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359-1, -2 |
| Melting Point | 214 °C | 417 °F | 10°C/min; ISO 11357-1, -3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 205 °C | 401 °F | ISO 75-1, -2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 175 °C | 347 °F | ISO 75-1, -2 |
| Deflection Temperature at 8.0 MPa | 60.0 °C | 140 °F | ISO 75-1, -2 |
| Vicat Softening Point | 200 °C @Load 5.10 kg |
392 °F @Load 11.2 lb |
120°C/hour; ISO 306 |
| 200 °C @Load 5.10 kg |
392 °F @Load 11.2 lb |
50°C/hour; ISO 306 | |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
||
| Oxygen Index | 22 % | 22 % | Method A; ISO 4589-2 |
| Glow Wire Test | 650 °C @Diameter 2.00 mm |
1200 °F @Diameter 0.0787 in |
GWFI; IEC 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | cond.; IEC 60093 |
| 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | d.a.m.; IEC 60093 | |
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | cond.; IEC 60093 |
| 1.00e+15 ohm | 1.00e+15 ohm | d.a.m.; IEC 60093 | |
| Dielectric Constant | 3.2 @Frequency 1.00e+6 Hz |
3.2 @Frequency 1.00e+6 Hz |
d.a.m.; IEC 60250 |
| 3.5 @Frequency 100 Hz |
3.5 @Frequency 100 Hz |
d.a.m.; IEC 60250 | |
| 3.7 @Frequency 1.00e+6 Hz |
3.7 @Frequency 1.00e+6 Hz |
cond.; IEC 60250 | |
| 10 @Frequency 100 Hz |
10 @Frequency 100 Hz |
cond.; IEC 60250 | |
| Dielectric Strength | 43.0 kV/mm @Thickness 1.00 mm |
1090 kV/in @Thickness 0.0394 in |
d.a.m.; IEC 60243-1 |
| 43.0 kV/mm @Thickness 1.00 mm |
1090 kV/in @Thickness 0.0394 in |
cond.; IEC 60243-1 | |
| Dissipation Factor | 0.0060 @Frequency 100 Hz |
0.0060 @Frequency 100 Hz |
d.a.m.; IEC 60250 |
| 0.015 @Frequency 1.00e+6 Hz |
0.015 @Frequency 1.00e+6 Hz |
d.a.m.; IEC 60250 | |
| 0.080 @Frequency 1.00e+6 Hz |
0.080 @Frequency 1.00e+6 Hz |
cond.; IEC 60250 | |
| 0.15 @Frequency 100 Hz |
0.15 @Frequency 100 Hz |
cond.; IEC 60250 | |
| Comparative Tracking Index | 600 V | 600 V | d.a.m.; Solution A; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 260 - 290 °C | 500 - 554 °F | |
| 280 °C | 536 °F | for test specimens; ISO 294 | |
| Mold Temperature | 80.0 °C | 176 °F | for test specimens; ISO 294 |
| 80.0 - 100 °C | 176 - 212 °F | ||
| Drying Temperature | 80.0 °C | 176 °F |
Users viewing this material also viewed the following:
- MarkeTech Repton 214 Aluminum Oxide
- Solvay Specialty Polymers Amodel® AT-1001L Polyphthalamide (PPA)
- Zhejiang Juner PP201-G30 PP For Automotive Parts
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, Hardness 90A, Black Sulfur Cure
- Eagle Brass 302 Austenitic Stainless Steel, Full Hardened
- DuPont™ Bynel® 41E871 Anhydride Modified LLDPE
- ELASTO UK Dryflex® 600400S SEBS Based Material, Filled Qualities, 40A Hardness, Natural
- Dow VORANOL™ 4701 Polyether Polyol
- Dynasol Solprene® 4301 Thermoplastic Rubber (SBS)
- Ametek High Purity Nickel Strip 899L 1/2 Hard
Copyright © lookpolymers.com All Rights Reserved