Lanxess Durethan® BKV 15 H2.0 DUS008 901510 Nylon 6, Glass Fiber Reinforced

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 20% Glass Fiber Filled
Manufacturer Lanxess
Trade Name Durethan®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Lanxess Durethan® BKV 15 H2.0 DUS008 901510 Nylon 6, Glass Fiber Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
PA 6, 15% glass fibers, injection molding, heat-aging stabilizedInformation provided by LANXESS.
Physical Properties Metric English Comments
Specific Gravity 1.23 g/cc
1.23 g/cc
ISO 1183
Moisture Absorption at Equilibrium 2.6 %
2.6 %
50% RH; ISO 62
Water Absorption at Saturation 8.5 %
8.5 %
ISO 62
Linear Mold Shrinkage, Flow 0.0010 cm/cm
0.0010 in/in
Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4
0.0050 cm/cm
0.0050 in/in
60x60x2; 280°C / MT 80°C; 600 bar; ISO 294-4
Linear Mold Shrinkage, Transverse 0.0020 cm/cm
0.0020 in/in
Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4
0.0080 cm/cm
0.0080 in/in
60x60x2; 280°C / MT 80°C; 600 bar; ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength at Break 59.0 MPa
8560 psi
cond.; ISO 527-1, -2; 5 mm/min
120 MPa
17400 psi
d.a.m.; ISO 527-1, -2; 5 mm/min
Elongation at Break 2.4 %
2.4 %
d.a.m.; ISO 527-1, -2; 5 mm/min
12 %
12 %
cond.; ISO 527-1, -2; 5 mm/min
Tensile Modulus 3.10 GPa
450 ksi
cond.; ISO 527-1, -2; 1 mm/min
6.60 GPa
957 ksi
d.a.m.; ISO 527-1, -2; 1 mm/min
Flexural Strength 100 MPa

@Strain 7.30 %
 14500 psi

@Strain 7.30 %
 cond., 2 mm/min; ISO 178-A
195 MPa

@Strain 4.80 %
 28300 psi

@Strain 4.80 %
 d.a.m., 2 mm/min; ISO 178-A
Flexural Yield Strength 75.0 MPa

@Strain 3.50 %
 10900 psi

@Strain 3.50 %
 cond., 2 mm/min; ISO 178-A
175 MPa

@Strain 3.50 %
 25400 psi

@Strain 3.50 %
 d.a.m., 2 mm/min; ISO 178-A
Flexural Modulus 2.80 GPa
406 ksi
cond., 2 mm/min; ISO 178-A
5.70 GPa
827 ksi
d.a.m., 2 mm/min; ISO 178-A
Izod Impact, Notched (ISO) <= 10.0 kJ/m²
<= 4.76 ft-lb/in²
d.a.m.; ISO 180-1A
10.0 kJ/m²
4.76 ft-lb/in²
cond.; ISO 180-1A
Izod Impact, Unnotched (ISO) 40.0 kJ/m²
19.0 ft-lb/in²
d.a.m.; ISO 180-1U
90.0 kJ/m²
42.8 ft-lb/in²
cond.; ISO 180-1U
Charpy Impact Unnotched 3.50 J/cm²
16.7 ft-lb/in²
d.a.m.; ISO 179-1eU
10.0 J/cm²
47.6 ft-lb/in²
cond.; ISO 179-1eU
Charpy Impact, Notched <= 1.00 J/cm²

@Temperature 23.0 °C
 <= 4.76 ft-lb/in²

@Temperature 73.4 °F
 d.a.m.; ISO 179-1eA
<= 1.00 J/cm²

@Temperature 23.0 °C
 <= 4.76 ft-lb/in²

@Temperature 73.4 °F
 cond.; ISO 179-1eA
<= 1.00 J/cm²

@Temperature -30.0 °C
 <= 4.76 ft-lb/in²

@Temperature -22.0 °F
 d.a.m.; ISO 179-1eA
<= 1.00 J/cm²

@Temperature -30.0 °C
 <= 4.76 ft-lb/in²

@Temperature -22.0 °F
 cond.; ISO 179-1eA
Puncture Energy 2.00 J

@Load <=55.7 kg,
Temperature -30.0 °C
 1.48 ft-lb

@Load <=123 lb,
Temperature -22.0 °F
 ISO 6603-2
2.20 J

@Load <=58.5 kg,
Temperature 23.0 °C
 1.62 ft-lb

@Load <=129 lb,
Temperature 73.4 °F
 ISO 6603-2
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 30.0 µm/m-°C

@Temperature 23.0 - 55.0 °C
 16.7 µin/in-°F

@Temperature 73.4 - 131 °F
 ISO 11359-1, -2
CTE, linear, Transverse to Flow 100 µm/m-°C

@Temperature 23.0 - 55.0 °C
 55.6 µin/in-°F

@Temperature 73.4 - 131 °F
 ISO 11359-1, -2
Melting Point 220 °C
428 °F
10°C/min; ISO 11357-1, -3
Deflection Temperature at 0.46 MPa (66 psi) 216 °C
421 °F
ISO 75-1, -2
Deflection Temperature at 1.8 MPa (264 psi) 190 °C
374 °F
ISO 75-1, -2
Processing Properties Metric English Comments
Melt Temperature 260 - 290 °C
500 - 554 °F
280 °C
536 °F
for test specimens; ISO 294
Mold Temperature 80.0 °C
176 °F
for test specimens; ISO 294
80.0 - 100 °C
176 - 212 °F
Drying Temperature 80.0 °C
176 °F
Dry Time 2 - 6 hour
2 - 6 hour
Moisture Content 0.030 - 0.12 %
0.030 - 0.12 %
residual; Karl Fischer Test
Descriptive Properties Value Comments
ISO Shortname ISO 1874-PA 6, GHR, 14-070, GF15