- Lanxess Durethan® BKV 15 G H2.0 900051 Copolyamide, 15% Glass Fiber
Lanxess Durethan® BKV 15 G H2.0 900051 Copolyamide, 15% Glass Fiber
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | Lanxess |
| Trade Name | Durethan® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Durethan® BKV 15 G H2.0 900051 Copolyamide, 15% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
CoPA, injection molding grade, 15% glass fibers, better surface resistance to alcoholic calcium chloride-solution than BKV 15 H2.0, good heat-ageing resistance
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.24 g/cc | 0.0448 lb/in³ | ISO 1183 |
| Water Absorption | 7.8 % | 7.8 % | Test Sim. to ISO 62 |
| Moisture Absorption at Equilibrium | 2.6 % | 2.6 % | 23°C/50% R.H.; Test Sim. to ISO 62 |
| Viscosity Test | 138 cm³/g | 138 cm³/g | Viscosity number; ISO 307, 1157, 1628 |
| Melt Flow | 52 g/10 min @Load 5.00 kg, Temperature 260 °C |
52 g/10 min @Load 11.0 lb, Temperature 500 °F |
Estimated using room temperature density; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 70.0 MPa | 10200 psi | Conditioned; ISO 527-1/-2 |
| 120 MPa | 17400 psi | ISO 527-1/-2 | |
| Elongation at Break | 3.0 % | 3.0 % | ISO 527-1/-2 |
| 11 % | 11 % | Conditioned; ISO 527-1/-2 | |
| Tensile Modulus | 4.00 GPa | 580 ksi | Conditioned; ISO 527-1/-2 |
| 6.50 GPa | 943 ksi | ISO 527-1/-2 | |
| Charpy Impact Unnotched | 3.50 J/cm² @Temperature -30.0 °C |
16.7 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU |
| 3.50 J/cm² @Temperature -30.0 °C |
16.7 ft-lb/in² @Temperature -22.0 °F |
Conditioned; ISO 179/1eU | |
| 4.00 J/cm² @Temperature 23.0 °C |
19.0 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |
| 4.00 J/cm² @Temperature 23.0 °C |
19.0 ft-lb/in² @Temperature 73.4 °F |
Conditioned; ISO 179/1eU | |
| Charpy Impact, Notched | <= 1.00 J/cm² @Temperature -30.0 °C |
<= 4.76 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| <= 1.00 J/cm² @Temperature -30.0 °C |
<= 4.76 ft-lb/in² @Temperature -22.0 °F |
Conditioned; ISO 179/1eA | |
| <= 1.00 J/cm² @Temperature 23.0 °C |
<= 4.76 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA | |
| <= 1.00 J/cm² @Temperature 23.0 °C |
<= 4.76 ft-lb/in² @Temperature 73.4 °F |
Conditioned; ISO 179/1eA | |
| Impact | 559 | 559 | Puncture maximum force (N); ISO 6603-2 |
| 505 @Temperature -30.0 °C |
505 @Temperature -22.0 °F |
Puncture maximum force (N); ISO 6603-2 | |
| Puncture Energy | 2.00 J | 1.48 ft-lb | ISO 6603-2 |
| 1.50 J @Temperature -30.0 °C |
1.11 ft-lb @Temperature -22.0 °F |
ISO 6603-2 | |
| 1.50 J @Temperature -30.0 °C |
1.11 ft-lb @Temperature -22.0 °F |
Conditioned; ISO 6603-2 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 30.0 µm/m-°C | 16.7 µin/in-°F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 80.0 µm/m-°C | 44.4 µin/in-°F | ISO 11359-1/-2 |
| Melting Point | 218 °C | 424 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 180 °C | 356 °F | ISO 75-1/-2 |
| Deflection Temperature at 8.0 MPa | 55.0 °C | 131 °F | ISO 75-1/-2 |
| Vicat Softening Point | 200 °C | 392 °F | 50°C/h 50N; ISO 306 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
IEC 60695-11-10 |
| HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
IEC 60695-11-10 | |
| Oxygen Index | 23 % | 23 % | ISO 4589-1/-2 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+11 ohm-cm | 1.00e+11 ohm-cm | Conditioned; IEC 60093 |
| 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | IEC 60093 | |
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | IEC 60093 |
| Dielectric Constant | 3.7 @Frequency 1.00e+6 Hz |
3.7 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 4.1 @Frequency 100 Hz |
4.1 @Frequency 100 Hz |
IEC 60250 | |
| 4.3 @Frequency 1.00e+6 Hz |
4.3 @Frequency 1.00e+6 Hz |
Conditioned; IEC 60250 | |
| 10 @Frequency 100 Hz |
10 @Frequency 100 Hz |
Conditioned; IEC 60250 | |
| Dielectric Strength | 30.0 kV/mm | 762 kV/in | IEC 60243-1 |
| 30.0 kV/mm | 762 kV/in | Conditioned; IEC 60243-1 | |
| Dissipation Factor | 0.0080 @Frequency 100 Hz |
0.0080 @Frequency 100 Hz |
IEC 60250 |
| 0.018 @Frequency 1.00e+6 Hz |
0.018 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| 0.070 @Frequency 1.00e+6 Hz |
0.070 @Frequency 1.00e+6 Hz |
Conditioned; IEC 60250 | |
| 0.22 @Frequency 100 Hz |
0.22 @Frequency 100 Hz |
Conditioned; IEC 60250 | |
| Comparative Tracking Index | 375 V | 375 V | IEC 60112 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Additives | Release agent | |
| Features | Heat stabilized or stable to heat | |
| Form | Pellets | |
| ISO Shortname | ISO 1874-PA 6/66, MHR, 14-060, GF15 | |
| Processing | Injection molding | |
| Region | Asia Pacific | |
| Europe | ||
| Near East/Africa | ||
| North America | ||
| South and Central America |
Users viewing this material also viewed the following:
- Oxford Polymers Oxnilon 66-15-IMP Impact Modified Nylon 66 for Injection Molding
- Albis Plastics Cellulose Acetate Propionate CP808 (FDA), 10% Plasticizer (discontinued **)
- Fiberfil® J-60/15/MI/20 Polypropylene Homopolymer, 35% Glass/mica Reinforced
- Plenco 08122 Polyester BMC, Compression Molded
- EPICHEM Epiblend PC/ABS nero Polycarbonate/ABS
- Colorite Polymers 7088 Non-Phthalate 88 Series Vinyl Compound
- Dymax Light Weld® 426 High Clarity Glass Bonding Adhesive
- Ametek High Purity Nickel Strip 899L Hard
- A. Schulman ComAlloy Hiloy® 124 Polypropylene, Glass Reinforced, Chemically Coupled
Copyright © lookpolymers.com All Rights Reserved