- Solvay TECHNYL® A 718 V30 PA66, 30% glass fiber, DRY
Solvay TECHNYL® A 718 V30 PA66, 30% glass fiber, DRY
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled |
| Manufacturer | Solvay |
| Trade Name | Technyl® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay TECHNYL® A 718 V30 PA66, 30% glass fiber, DRY.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: TECHNYL A 718 V30 is a polyamide 66 reinforced with glass fiber and thermal stabilized for injection moldingColors: it is sailed on natural and black colorAvailable in: Latin AmericaMain Properties: Good mechanical properties, Great superficial aspect, Dimensional stability and Excellent flow characteristicsApplications: This product is indicated for pieces with complex geometries, which need an excellent superficial aspect and good mechanical properties.Information provided by Rhodia, Rhodia has been acquired by Solvay.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.37 g/cc | 0.0495 lb/in³ | ISO 1183/A |
| Water Absorption | 0.50 - 1.0 % @Temperature 23.0 °C, Time 86400 sec |
0.50 - 1.0 % @Temperature 73.4 °F, Time 24.0 hour |
ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0050 cm/cm | 0.0050 in/in | |
| Linear Mold Shrinkage, Transverse | 0.013 cm/cm | 0.013 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 150 MPa | 21800 psi | ISO 527 |
| Elongation at Break | 2.5 % | 2.5 % | ISO 527 |
| Tensile Modulus | 9.00 GPa | 1310 ksi | ISO 527 |
| Flexural Strength | 250 MPa | 36300 psi | ISO 178 |
| Flexural Modulus | 8.20 GPa | 1190 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 3.00 kJ/m² | 1.43 ft-lb/in² | ISO 180 |
| Charpy Impact Unnotched | 3.50 J/cm² | 16.7 ft-lb/in² | ISO 178 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 255 - 265 °C | 491 - 509 °F | ISO 3146-A |
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | ISO 75 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 250 - 270 °C | 482 - 518 °F | |
| Nozzle Temperature | 270 - 290 °C | 518 - 554 °F | |
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Compression Zone | 260-280°C |
Users viewing this material also viewed the following:
- Nye Lubricants 168F (SO) Synthetic Oil
- Polymer Resources TP-G20 Polybutylene Terephthalate, 20% Glass Reinforced
- SABIC Innovative Plastics Lexan® ML7647 PC (Europe-Africa-Middle East)
- KaMin KaMin® HG90 Kaolin Clay - Ultrafine, high brightness
- SABIC Innovative Plastics LNP THERMOTUF PF00AIS PA 6 (Asia Pacific)
- A. Schulman FORMION™ FI 391 Ionomer
- A. Schulman POLYBATCH™ Birch 60171U/4 Concentrate Based in LLDPE
- ATI Allvac® Nickelvac® TJA-1537™ UNS R31537 & UNS R31538 Nickel Superalloy
- Lubrizol Advanced Materials Pearlstick® 45-40/15 Polycaprolactone based TPU
Copyright © lookpolymers.com All Rights Reserved