Lanxess Durethan® BKV 15 DUS008 000000 Nylon 6, Glass Fiber Reinforced

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 20% Glass Fiber Filled
Manufacturer Lanxess
Trade Name Durethan®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Lanxess Durethan® BKV 15 DUS008 000000 Nylon 6, Glass Fiber Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PA 6, 15% glass fibers, injection moldingInformation provided by LANXESS.
Physical Properties Metric English Comments
Specific Gravity 1.23 g/cc
1.23 g/cc
ISO 1183
Linear Mold Shrinkage, Flow 0.0013 cm/cm
0.0013 in/in
Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4
0.0035 cm/cm
0.0035 in/in
60x60x2; 280°C / MT 80°C; 600 bar; ISO 294-4
Linear Mold Shrinkage, Transverse 0.0016 cm/cm
0.0016 in/in
Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4
0.0059 cm/cm
0.0059 in/in
60x60x2; 280°C / MT 80°C; 600 bar; ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength at Break 65.0 MPa
9430 psi
cond.; ISO 527-1, -2; 5 mm/min
130 MPa
18900 psi
d.a.m.; ISO 527-1, -2; 5 mm/min
Elongation at Break 3.0 %
3.0 %
d.a.m.; ISO 527-1, -2; 5 mm/min
12 %
12 %
cond.; ISO 527-1, -2; 5 mm/min
Tensile Modulus 3.10 GPa
450 ksi
cond.; ISO 527-1, -2; 1 mm/min
6.50 GPa
943 ksi
d.a.m.; ISO 527-1, -2; 1 mm/min
Flexural Strength 110 MPa

@Strain 8.00 %
 16000 psi

@Strain 8.00 %
 cond., 2 mm/min; ISO 178-A
205 MPa

@Strain 5.30 %
 29700 psi

@Strain 5.30 %
 d.a.m., 2 mm/min; ISO 178-A
Flexural Yield Strength 80.0 MPa

@Strain 3.50 %
 11600 psi

@Strain 3.50 %
 cond., 2 mm/min; ISO 178-A
180 MPa

@Strain 3.50 %
 26100 psi

@Strain 3.50 %
 d.a.m., 2 mm/min; ISO 178-A
Flexural Modulus 3.10 GPa
450 ksi
cond., 2 mm/min; ISO 178-A
5.50 GPa
798 ksi
d.a.m., 2 mm/min; ISO 178-A
Izod Impact, Notched (ISO) <= 10.0 kJ/m²
<= 4.76 ft-lb/in²
d.a.m.; ISO 180-1A
10.0 kJ/m²
4.76 ft-lb/in²
cond.; ISO 180-1A
Izod Impact, Unnotched (ISO) 40.0 kJ/m²

@Temperature -30.0 °C
 19.0 ft-lb/in²

@Temperature -22.0 °F
 d.a.m.; ISO 180-1U
40.0 kJ/m²

@Temperature -30.0 °C
 19.0 ft-lb/in²

@Temperature -22.0 °F
 cond.; ISO 180-1U
45.0 kJ/m²

@Temperature 23.0 °C
 21.4 ft-lb/in²

@Temperature 73.4 °F
 d.a.m.; ISO 180-1U
85.0 kJ/m²

@Temperature 23.0 °C
 40.4 ft-lb/in²

@Temperature 73.4 °F
 cond.; ISO 180-1U
Charpy Impact Unnotched 4.50 J/cm²

@Temperature -30.0 °C
 21.4 ft-lb/in²

@Temperature -22.0 °F
 d.a.m.; ISO 179-1eU
4.50 J/cm²

@Temperature -30.0 °C
 21.4 ft-lb/in²

@Temperature -22.0 °F
 cond.; ISO 179-1eU
5.00 J/cm²

@Temperature 23.0 °C
 23.8 ft-lb/in²

@Temperature 73.4 °F
 d.a.m.; ISO 179-1eU
10.0 J/cm²

@Temperature 23.0 °C
 47.6 ft-lb/in²

@Temperature 73.4 °F
 cond.; ISO 179-1eU
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 30.0 µm/m-°C

@Temperature 23.0 - 55.0 °C
 16.7 µin/in-°F

@Temperature 73.4 - 131 °F
 ISO 11359-1, -2
CTE, linear, Transverse to Flow 100 µm/m-°C

@Temperature 23.0 - 55.0 °C
 55.6 µin/in-°F

@Temperature 73.4 - 131 °F
 ISO 11359-1, -2
Melting Point 220 °C
428 °F
10°C/min; ISO 11357-1, -3
Deflection Temperature at 0.46 MPa (66 psi) 215 °C
419 °F
ISO 75-1, -2
Deflection Temperature at 1.8 MPa (264 psi) 195 °C
383 °F
ISO 75-1, -2
Vicat Softening Point 210 °C

@Load 5.10 kg
 410 °F

@Load 11.2 lb
 120°C/hour; ISO 306
Processing Properties Metric English Comments
Melt Temperature 260 - 290 °C
500 - 554 °F
280 °C
536 °F
for test specimens; ISO 294
Mold Temperature 80.0 °C
176 °F
for test specimens; ISO 294
80.0 - 100 °C
176 - 212 °F
Drying Temperature 80.0 °C
176 °F
Dry Time 2 - 6 hour
2 - 6 hour
Descriptive Properties Value Comments
ISO Shortname ISO 1874-PA 6, GR, 14-060, GF15