Lanxess Durethan® B 40 SK 000000 Nylon 6
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced |
| Manufacturer | Lanxess |
| Trade Name | Durethan® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Durethan® B 40 SK 000000 Nylon 6.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PA 6, non-reinforced, injection molding
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.14 g/cc | 1.14 g/cc | ISO 1183 |
| Bulk Density | 0.700 g/cc | 0.0253 lb/in³ | ISO 60 |
| Moisture Absorption at Equilibrium | 3.0 % | 3.0 % | 50% RH; ISO 62 |
| Water Absorption at Saturation | 10 % | 10 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0090 cm/cm @Thickness 3.00 mm |
0.0090 in/in @Thickness 0.118 in |
Mold Temp 80°C; Melt Temp 280°C; 600 bar; ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0096 cm/cm @Thickness 3.00 mm |
0.0096 in/in @Thickness 0.118 in |
Mold Temp 80°C; Melt Temp 280°C; 600 bar; ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 50.0 MPa | 7250 psi | Conditioned; ISO 2039-1 |
| 150 MPa | 21800 psi | ISO 2039-1 | |
| Tensile Strength, Yield | 40.0 MPa | 5800 psi | Conditioned; ISO 527-1,-2 |
| 85.0 MPa | 12300 psi | ISO 527-1,-2 | |
| Elongation at Break | 20 % | 20 % | ISO 527-1,-2 |
| >= 50 % | >= 50 % | Conditioned; ISO 527-1,-2 | |
| Elongation at Yield | 4.0 % | 4.0 % | ISO 527-1,-2 |
| 25 % | 25 % | Conditioned; ISO 527-1,-2 | |
| Tensile Modulus | 0.900 GPa | 131 ksi | Conditioned; ISO 527-1,-2 |
| 3.20 GPa | 464 ksi | ISO 527-1,-2 | |
| Flexural Strength | 35.0 MPa @Strain 9.00 % |
5080 psi @Strain 9.00 % |
Conditioned; ISO 178 |
| 115 MPa @Strain 6.00 % |
16700 psi @Strain 6.00 % |
ISO 178 | |
| Flexural Yield Strength | 25.0 MPa @Strain 3.50 % |
3630 psi @Strain 3.50 % |
Conditioned; ISO 178 |
| 95.0 MPa @Strain 3.50 % |
13800 psi @Strain 3.50 % |
ISO 178 | |
| Flexural Modulus | 0.800 GPa | 116 ksi | Conditioned; ISO 178 |
| 2.80 GPa | 406 ksi | ISO 178 | |
| Izod Impact, Notched (ISO) | <= 10.0 kJ/m² @Temperature -30.0 °C |
<= 4.76 ft-lb/in² @Temperature -22.0 °F |
ISO 180-1A |
| <= 10.0 kJ/m² @Temperature -30.0 °C |
<= 4.76 ft-lb/in² @Temperature -22.0 °F |
Conditioned; ISO 180-1A | |
| <= 10.0 kJ/m² @Temperature -40.0 °C |
<= 4.76 ft-lb/in² @Temperature -40.0 °F |
ISO 180-1A | |
| <= 10.0 kJ/m² @Temperature -40.0 °C |
<= 4.76 ft-lb/in² @Temperature -40.0 °F |
Conditioned; ISO 180-1A | |
| Izod Impact, Unnotched (ISO) | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ISO 180-1U |
| NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
Conditioned; ISO 180-1U | |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
ISO 180-1U | |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
Conditioned; ISO 180-1U | |
| Charpy Impact Unnotched | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ISO 179-1eU |
| NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
Conditioned; ISO 179-1eU | |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
ISO 179-1eU | |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
Conditioned; ISO 179-1eU | |
| Charpy Impact, Notched | <= 1.00 J/cm² @Temperature 23.0 °C |
<= 4.76 ft-lb/in² @Temperature 73.4 °F |
ISO 179-1eA |
| <= 1.00 J/cm² @Temperature -30.0 °C |
<= 4.76 ft-lb/in² @Temperature -22.0 °F |
ISO 179-1eA | |
| <= 1.00 J/cm² @Temperature -30.0 °C |
<= 4.76 ft-lb/in² @Temperature -22.0 °F |
Conditioned; ISO 179-1eA | |
| <= 1.00 J/cm² @Temperature -40.0 °C |
<= 4.76 ft-lb/in² @Temperature -40.0 °F |
ISO 179-1eA | |
| <= 1.00 J/cm² @Temperature -40.0 °C |
<= 4.76 ft-lb/in² @Temperature -40.0 °F |
Conditioned; ISO 179-1eA | |
| 5.00 J/cm² @Temperature 23.0 °C |
23.8 ft-lb/in² @Temperature 73.4 °F |
Conditioned; ISO 179-1eA | |
| Puncture Energy | 160 J @Temperature 23.0 °C |
118 ft-lb @Temperature 73.4 °F |
ISO 6603-2 |
| 160 J @Temperature -30.0 °C |
118 ft-lb @Temperature -22.0 °F |
ISO 6603-2 | |
| 165 J @Temperature 23.0 °C |
122 ft-lb @Temperature 73.4 °F |
Conditioned; ISO 6603-2 | |
| Tensile Creep Modulus, 1 hour | 700 MPa | 102000 psi | Conditioned; ISO 889-1 |
| Tensile Creep Modulus, 1000 hours | 570 MPa | 82700 psi | Conditioned; ISO 889-1 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 80.0 µm/m-°C | 44.4 µin/in-°F | ISO 11359-1,-2 |
| CTE, linear, Transverse to Flow | 90.0 µm/m-°C | 50.0 µin/in-°F | ISO 11359-1,-2 |
| Melting Point | 222 °C | 432 °F | ISO 11357-1,-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 150 °C | 302 °F | ISO 75-1,-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | ISO 75-1,-2 |
| Deflection Temperature at 8.0 MPa | 45.0 °C | 113 °F | ISO 75-1,-2 |
| Vicat Softening Point | 200 °C @Load 5.10 kg |
392 °F @Load 11.2 lb |
120°C/h; ISO 306 |
| 200 °C @Load 5.10 kg |
392 °F @Load 11.2 lb |
50°C/h; ISO 306 | |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| HB @Thickness 0.800 mm |
HB @Thickness 0.0315 in |
||
| Oxygen Index | 24 % | 24 % | Method A; ISO 4589-2 |
| Glow Wire Test | 750 °C @Diameter 2.00 mm |
1380 °F @Diameter 0.0787 in |
IEC 60695-2-12 |
| Shrinkage | 0.20 % @Temperature 120 °C, Time 14400 sec |
0.20 % @Temperature 248 °F, Time 4.00 hour |
Molding Post-shrinkage; ISO 294-4 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+11 ohm-cm | 1.00e+11 ohm-cm | Conditioned; IEC 60093 |
| 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 | |
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | Conditioned; IEC 60093 |
| 1.00e+14 ohm | 1.00e+14 ohm | IEC 60093 | |
| Dielectric Constant | 3.5 @Frequency 1.00e+6 Hz |
3.5 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 4.0 @Frequency 100 Hz |
4.0 @Frequency 100 Hz |
IEC 60250 | |
| 4.5 @Frequency 1.00e+6 Hz |
4.5 @Frequency 1.00e+6 Hz |
Conditioned; IEC 60250 | |
| 20 @Frequency 100 Hz |
20 @Frequency 100 Hz |
Conditioned; IEC 60250 | |
| Dielectric Strength | 30.0 kV/mm @Thickness 1.00 mm |
762 kV/in @Thickness 0.0394 in |
IEC 60243-1 |
| 35.0 kV/mm @Thickness 1.00 mm |
889 kV/in @Thickness 0.0394 in |
Conditioned; IEC 60243-1 | |
| Dissipation Factor | 0.012 @Frequency 100 Hz |
0.012 @Frequency 100 Hz |
IEC 60250 |
| 0.020 @Frequency 1.00e+6 Hz |
0.020 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| 0.135 @Frequency 1.00e+6 Hz |
0.135 @Frequency 1.00e+6 Hz |
Conditioned; IEC 60250 | |
| 0.185 @Frequency 100 Hz |
0.185 @Frequency 100 Hz |
Conditioned; IEC 60250 | |
| Comparative Tracking Index | 600 V | 600 V | Solution A, Rating; IEC 60112 |
| 600 V | 600 V | Solution B, Rating 600 (475) M; IEC 60112 |
Users viewing this material also viewed the following:
- RheTech Products T30P100-01 30% Talc Reinforced Polypropylene, Black
- PolyOne Versaflex™ CL40 Thermoplastic Elastomer (TPE)
- PolyOne Lubri-Tech™ PS-30GF/02S Polybutylene Terephthalate (PBT), Glass Filled, PTFE/Silicone Lubricated (dis
- Taiwan PU Corporation CPU-69-A/B Polyurethane Casting Elastomer
- SABIC Innovative Plastics PC2800 PC (Europe-Africa-Middle East)
- Teknor Apex Telcar® TL-1123 BLK 111 Thermoplastic Elastomer
- Toho Tenax Pyromex® CPX 2d 312K Non-crimped Carbon Fiber
- EMS-Grivory Grivory® BGZ-15 PA6-GF15
- Diamond Polymers PC FR 500 10%GF 10% Glass Reinforced, Flame Retardant Polycarbonate
Copyright © lookpolymers.com All Rights Reserved