Lanxess Durethan® B 31 SK 000000 Nylon 6
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced |
| Manufacturer | Lanxess |
| Trade Name | Durethan® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Durethan® B 31 SK 000000 Nylon 6.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PA 6, injection molding grade, non-reinforced, easy flow, easy-release, rapid solidification, crystallizes somewhat more finely and uniformly than B 30 S
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | ISO 1183 |
| Water Absorption | 10 % | 10 % | Test Sim. to ISO 62 |
| Moisture Absorption at Equilibrium | 3.0 % | 3.0 % | 23°C/50% R.H.; Test Sim. to ISO 62 |
| Viscosity Test | 138 cm³/g | 138 cm³/g | Viscosity number; ISO 307, 1157, 1628 |
| Melt Flow | 99 g/10 min @Load 5.00 kg, Temperature 260 °C |
99 g/10 min @Load 11.0 lb, Temperature 500 °F |
Calculated from MVR using melt density; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 50.0 MPa | 7250 psi | Conditioned; ISO 527-1/-2 |
| 85.0 MPa | 12300 psi | ISO 527-1/-2 | |
| Elongation at Break | 10 % | 10 % | Nominal; ISO 527-1/-2 |
| >= 50 % | >= 50 % | Nominal, Conditioned; ISO 527-1/-2 | |
| Elongation at Yield | 4.0 % | 4.0 % | ISO 527-1/-2 |
| 20 % | 20 % | Conditioned; ISO 527-1/-2 | |
| Tensile Modulus | 1.10 GPa | 160 ksi | Conditioned; ISO 527-1/-2 |
| 3.50 GPa | 508 ksi | ISO 527-1/-2 | |
| Charpy Impact Unnotched | NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
ISO 179/1eU |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
Conditioned; ISO 179/1eU | |
| NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ISO 179/1eU | |
| NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
Conditioned; ISO 179/1eU | |
| Charpy Impact, Notched | <= 1.00 J/cm² @Temperature -30.0 °C |
<= 4.76 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| <= 1.00 J/cm² @Temperature -30.0 °C |
<= 4.76 ft-lb/in² @Temperature -22.0 °F |
Conditioned; ISO 179/1eA | |
| <= 1.00 J/cm² @Temperature 23.0 °C |
<= 4.76 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA | |
| 2.50 J/cm² @Temperature 23.0 °C |
11.9 ft-lb/in² @Temperature 73.4 °F |
Conditioned; ISO 179/1eA | |
| Impact | 4647 | 4647 | Puncture maximum force (N); ISO 6603-2 |
| 6813 @Temperature -30.0 °C |
6813 @Temperature -22.0 °F |
Puncture maximum force (N); ISO 6603-2 | |
| Puncture Energy | 46.0 J | 33.9 ft-lb | ISO 6603-2 |
| 70.0 J @Temperature -30.0 °C |
51.6 ft-lb @Temperature -22.0 °F |
ISO 6603-2 | |
| 70.0 J @Temperature -30.0 °C |
51.6 ft-lb @Temperature -22.0 °F |
Conditioned; ISO 6603-2 | |
| Tensile Creep Modulus, 1 hour | 900 MPa | 131000 psi | ISO 899-1 |
| Tensile Creep Modulus, 1000 hours | 700 MPa | 102000 psi | ISO 899-1 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 70.0 µm/m-°C | 38.9 µin/in-°F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 90.0 µm/m-°C | 50.0 µin/in-°F | ISO 11359-1/-2 |
| Melting Point | 222 °C | 432 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 170 °C | 338 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F | ISO 75-1/-2 |
| Deflection Temperature at 8.0 MPa | 50.0 °C | 122 °F | ISO 75-1/-2 |
| Vicat Softening Point | 200 °C | 392 °F | 50°C/h 50N; ISO 306 |
| Flammability, UL94 | V-2 @Thickness 1.60 mm |
V-2 @Thickness 0.0630 in |
IEC 60695-11-10 |
| V-2 @Thickness 3.20 mm |
V-2 @Thickness 0.126 in |
IEC 60695-11-10 | |
| Oxygen Index | 25 % | 25 % | ISO 4589-1/-2 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | Conditioned; IEC 60093 |
| 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 | |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | IEC 60093 |
| Dielectric Constant | 3.5 @Frequency 1.00e+6 Hz |
3.5 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 4.0 @Frequency 100 Hz |
4.0 @Frequency 100 Hz |
IEC 60250 | |
| 4.0 @Frequency 1.00e+6 Hz |
4.0 @Frequency 1.00e+6 Hz |
Conditioned; IEC 60250 | |
| 13 @Frequency 100 Hz |
13 @Frequency 100 Hz |
Conditioned; IEC 60250 | |
| Dielectric Strength | 30.0 kV/mm | 762 kV/in | IEC 60243-1 |
| 30.0 kV/mm | 762 kV/in | Conditioned; IEC 60243-1 | |
| Dissipation Factor | 0.0060 @Frequency 100 Hz |
0.0060 @Frequency 100 Hz |
IEC 60250 |
| 0.020 @Frequency 1.00e+6 Hz |
0.020 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| 0.10 @Frequency 1.00e+6 Hz |
0.10 @Frequency 1.00e+6 Hz |
Conditioned; IEC 60250 | |
| 0.19 @Frequency 100 Hz |
0.19 @Frequency 100 Hz |
Conditioned; IEC 60250 | |
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Form | Pellets | |
| ISO Shortname | ISO 1874-PA 6,MR,14-030,N | |
| Processing | Injection molding | |
| Region | Asia Pacific | |
| Europe | ||
| Near East/Africa | ||
| North America | ||
| South and Central America |
Users viewing this material also viewed the following:
- DuPont™ Sclairfilm® SL-3 LLDPE Film, Laminating, 76.2 µm Thickness (discontinued **)
- Saint-Gobain CHR® M765 Polyester Film Backing Natural Rubber Adhesive Pressure Sensitive Tape
- Samsung Cheil Industries Starex® CM-0140UV ABS, Unreinforced
- Teknor Apex Monprene® MP-2295 Thermoplastic Elastomer
- Sinotek Materials WT75-45/75 Amorphous Graphite Powder
- Zoltek Pyron® Continuous Tow Oxidized Pan Fiber
- ExxonMobil HD 6719.17 Injection Molding Resin
- Arkema Group Nakan® FKS 902 R PVC, Soft Extrusion Grade
- Axiall 11441 Wire & Cable Flexible PVC
Copyright © lookpolymers.com All Rights Reserved