- Lanxess Durethan® AKV 35 CX H2.0 900876 Nylon 66, Glass Fiber Reinforced
Lanxess Durethan® AKV 35 CX H2.0 900876 Nylon 66, Glass Fiber Reinforced
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 40% Glass Fiber Filled |
| Manufacturer | Lanxess |
| Trade Name | Durethan® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Durethan® AKV 35 CX H2.0 900876 Nylon 66, Glass Fiber Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PA 66, 35% glass fibers, injection molding, heat-aging stabilizedInformation provided by LANXESS.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.413 g/cc | 1.413 g/cc | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.00070 cm/cm | 0.00070 in/in | Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4 |
| 0.0030 cm/cm | 0.0030 in/in | 60x60x2; 290°C / MT 80°C; 600 bar; ISO 294-4 | |
| Linear Mold Shrinkage, Transverse | 0.00070 cm/cm | 0.00070 in/in | Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4 |
| 0.0090 cm/cm | 0.0090 in/in | 60x60x2; 290°C / MT 80°C; 600 bar; ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 197 MPa | 28600 psi | d.a.m.; ISO 527-1, -2; 5 mm/min |
| Elongation at Break | 2.8 % | 2.8 % | d.a.m.; ISO 527-1, -2; 5 mm/min |
| Tensile Modulus | 11.0 GPa | 1600 ksi | d.a.m.; ISO 527-1, -2; 1 mm/min |
| Flexural Strength | 296 MPa @Strain 3.20 % |
42900 psi @Strain 3.20 % |
d.a.m., 2 mm/min; ISO 178-A |
| Flexural Modulus | 10.9 GPa | 1580 ksi | d.a.m., 2 mm/min; ISO 178-A |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² @Temperature 23.0 °C |
4.76 ft-lb/in² @Temperature 73.4 °F |
d.a.m.; ISO 180-1A |
| Izod Impact, Unnotched (ISO) | 58.0 kJ/m² | 27.6 ft-lb/in² | ISO 180-1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 260 °C | 500 °F | 10°C/min; ISO 11357-1, -3 |
| Deflection Temperature at 1.8 MPa (264 psi) | >= 240 °C | >= 464 °F | ISO 75-1, -2 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 280 - 300 °C | 536 - 572 °F | |
| 290 °C | 554 °F | for test specimens; ISO 294 | |
| Mold Temperature | 80.0 °C | 176 °F | for test specimens; ISO 294 |
| 80.0 - 120 °C | 176 - 248 °F | ||
| Drying Temperature | 80.0 °C | 176 °F | |
| Dry Time | 2 - 6 hour | 2 - 6 hour | |
| Moisture Content | 0.020 - 0.070 % | 0.020 - 0.070 % | residual; Karl Fischer Test |
| Descriptive Properties | Value | Comments |
|---|---|---|
| ISO Shortname | ISO 1874-PA 66, GHR, 12-110, GF35 |
Users viewing this material also viewed the following:
- Plastcom SLOVAMID 6 GF 20 Polyamide 6, 20% Glass Fiber
- DuPont Elvax® 3174SHB Ethylene-Vinyl Acetate Copolymer Resin for Coextrusion, Cast Film (discontinued **)
- Special Metals INCONEL® 625LCF® Nickel Superalloy (UNS N06626) Annealed 2150°F (1180°C)
- Zeon Chemicals Hydrin® H-55 Epichlorohydrin Homopolymer
- A. Schulman SCHULAMID® 66 MK4015 40% Glass Fiber/Mineral Reinforced 66
- Chosun Refractories BTB-18S Casting Block
- E-Polymers Tekaster® F615GM , 40% GF/MF Reinforced PET
- Ashley Polymers Ashlene® 851 Nylon 6, High Viscosity
- Technetics Group Texolon™ 8764 PTFE (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved