Lanxess Durethan® A 30 S H3.0 000000 Nylon 66, Injection Molding
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Unreinforced |
| Manufacturer | Lanxess |
| Trade Name | Durethan® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Durethan® A 30 S H3.0 000000 Nylon 66, Injection Molding.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PA 66, non-reinforced, injection moldingInformation provided by LANXESS.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm | 0.0020 in/in | Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4 |
| 0.011 cm/cm | 0.011 in/in | 60x60x2; 280°C / WZ 80°C; 600 bar; ISO 294-4 | |
| Linear Mold Shrinkage, Transverse | 0.0030 cm/cm | 0.0030 in/in | Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4 |
| 0.015 cm/cm | 0.015 in/in | 60x60x2; 280°C / WZ 80°C; 600 bar; ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 60.0 MPa | 8700 psi | cond.; ISO 527-1, -2; 50 mm/min |
| 95.0 MPa | 13800 psi | d.a.m.; ISO 527-1, -2; 50 mm/min | |
| Elongation at Yield | 4.5 % | 4.5 % | d.a.m.; ISO 527-1, -2; 50 mm/min |
| 18 % | 18 % | cond.; ISO 527-1, -2; 50 mm/min | |
| Tensile Modulus | 1.60 GPa | 232 ksi | cond.; ISO 527-1, -2; 1 mm/min |
| 3.80 GPa | 551 ksi | d.a.m.; ISO 527-1, -2; 1 mm/min | |
| Flexural Strength | 50.0 MPa @Strain 8.00 % |
7250 psi @Strain 8.00 % |
cond., 2 mm/min; ISO 178-A |
| 130 MPa @Strain 6.50 % |
18900 psi @Strain 6.50 % |
d.a.m., 2 mm/min; ISO 178-A | |
| Flexural Yield Strength | 40.0 MPa @Strain 3.50 % |
5800 psi @Strain 3.50 % |
cond., 2 mm/min; ISO 178-A |
| 110 MPa @Strain 3.50 % |
16000 psi @Strain 3.50 % |
d.a.m., 2 mm/min; ISO 178-A | |
| Flexural Modulus | 1.30 GPa | 189 ksi | cond., 2 mm/min; ISO 178-A |
| 3.20 GPa | 464 ksi | d.a.m., 2 mm/min; ISO 178-A | |
| Izod Impact, Notched (ISO) | <= 10.0 kJ/m² @Temperature 23.0 °C |
<= 4.76 ft-lb/in² @Temperature 73.4 °F |
d.a.m.; ISO 180-1A |
| <= 10.0 kJ/m² @Temperature 23.0 °C |
<= 4.76 ft-lb/in² @Temperature 73.4 °F |
cond.; ISO 180-1A | |
| <= 10.0 kJ/m² @Temperature -30.0 °C |
<= 4.76 ft-lb/in² @Temperature -22.0 °F |
d.a.m.; ISO 180-1A | |
| <= 10.0 kJ/m² @Temperature -30.0 °C |
<= 4.76 ft-lb/in² @Temperature -22.0 °F |
cond.; ISO 180-1A | |
| Charpy Impact Unnotched | 10.0 J/cm² @Temperature -30.0 °C |
47.6 ft-lb/in² @Temperature -22.0 °F |
d.a.m.; ISO 179-1eU |
| 15.0 J/cm² @Temperature 23.0 °C |
71.4 ft-lb/in² @Temperature 73.4 °F |
d.a.m.; ISO 179-1eU | |
| NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
cond.; ISO 179-1eU | |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
cond.; ISO 179-1eU | |
| Charpy Impact, Notched | <= 1.00 J/cm² @Temperature 23.0 °C |
<= 4.76 ft-lb/in² @Temperature 73.4 °F |
d.a.m.; ISO 179-1eA |
| <= 1.00 J/cm² @Temperature -30.0 °C |
<= 4.76 ft-lb/in² @Temperature -22.0 °F |
d.a.m.; ISO 179-1eA | |
| <= 1.00 J/cm² @Temperature -30.0 °C |
<= 4.76 ft-lb/in² @Temperature -22.0 °F |
cond.; ISO 179-1eA | |
| <= 1.00 J/cm² @Temperature -40.0 °C |
<= 4.76 ft-lb/in² @Temperature -40.0 °F |
d.a.m.; ISO 179-1eA | |
| <= 1.00 J/cm² @Temperature -40.0 °C |
<= 4.76 ft-lb/in² @Temperature -40.0 °F |
cond.; ISO 179-1eA | |
| 1.00 J/cm² @Temperature 23.0 °C |
4.76 ft-lb/in² @Temperature 73.4 °F |
cond.; ISO 179-1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 60.0 µm/m-°C @Temperature 23.0 - 55.0 °C |
33.3 µin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359-1, -2 |
| CTE, linear, Transverse to Flow | 90.0 µm/m-°C @Temperature 23.0 - 55.0 °C |
50.0 µin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359-1, -2 |
| Melting Point | 263 °C | 505 °F | 10°C/min; ISO 11357-1, -3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 214 °C | 417 °F | ISO 75-1, -2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C | 167 °F | ISO 75-1, -2 |
| Vicat Softening Point | >= 230 °C @Load 5.10 kg |
>= 446 °F @Load 11.2 lb |
120°C/hour; ISO 306 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 280 °C | 536 °F | for test specimens; ISO 294 |
| 275 - 295 °C | 527 - 563 °F | ||
| Mold Temperature | 80.0 °C | 176 °F | for test specimens; ISO 294 |
| 80.0 - 100 °C | 176 - 212 °F | ||
| Drying Temperature | 80.0 °C | 176 °F | |
| Dry Time | 2 - 6 hour | 2 - 6 hour | |
| Moisture Content | 0.030 - 0.12 % | 0.030 - 0.12 % | residual; Karl Fischer Test |
| Descriptive Properties | Value | Comments |
|---|---|---|
| ISO Shortname | ISO 1874-PA 66, GHR, 14-040 |
Users viewing this material also viewed the following:
- MV Labs BA880 Ba(OH)2.8H2O Barium hydroxide hydrate
- Lehmann & Voss LUVOCOM® 1-7395 Polyamide 66, with carbon fiber, aramid reinforcement and PTFE, heat stabilized
- LG Chemical SEETEC R3420 Polypropylene, Random Copolymer
- Haysite 48600 Polyester SMC, 30% Glass Reinforced
- Styron Magnumâ„¢ 545 ABS, General Purpose
- Eurotec® Tecomid® NA40 GR30 NL HW PA6.6, 30% glass fiber reinforced, hydrolysis stabilized, natural
- Cheng Yu Plastic E500 PC/PET
- ACC QMSkin 30 Specialist Molding 2-Part Condensation Cure
- Haynes Hastelloy® C-22® alloy, transverse, GTAW spray weldment, 12.7 mm (1/2 in.) thick plate
- Permabond 947 Cyanoacrylate, low odor
Copyright © lookpolymers.com All Rights Reserved