LTL Color Compounds ColorFast® PAHF Polycarbonate-ABS Alloy
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | LTL Color Compounds |
| Trade Name | ColorFast® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LTL Color Compounds ColorFast® PAHF Polycarbonate-ABS Alloy.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
General purpose HB-rated PC/ABS with improved chemical resistanceAll information provided by LTL Color Compounders, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.15 g/cc | 1.15 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | 0.125; ASTM D955 |
| Melt Flow | 19 g/10 min @Load 5.00 kg, Temperature 260 °C |
19 g/10 min @Load 11.0 lb, Temperature 500 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 50.3 MPa | 7300 psi | 2.0 in/min; ASTM D638 |
| Tensile Strength, Yield | 57.2 MPa | 8300 psi | 2.0 in/min; ASTM D638 |
| Elongation at Break | 100 % | 100 % | 2.0 in/min; ASTM D638 |
| Elongation at Yield | 5.0 % | 5.0 % | 2.0 in/min; ASTM D638 |
| Flexural Strength | 88.3 MPa | 12800 psi | 2.0 in/min; ASTM D790 |
| Flexural Modulus | 2.34 GPa | 340 ksi | 2.0 in/min; ASTM D790 |
| Izod Impact, Notched | 6.41 J/cm @Temperature 22.8 °C |
12.0 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 104 °C | 220 °F | Unannealed (0.250"); ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 249 - 288 °C | 480 - 550 °F | |
| Middle Barrel Temperature | 254 - 293 °C | 490 - 560 °F | |
| Front Barrel Temperature | 260 - 302 °C | 500 - 575 °F | |
| Nozzle Temperature | 274 - 302 °C | 525 - 575 °F | |
| Melt Temperature | 274 - 302 °C | 525 - 575 °F | |
| Mold Temperature | 60.0 - 87.8 °C | 140 - 190 °F | |
| Drying Temperature | 104 - 110 °C | 220 - 230 °F | |
| Dry Time | 3 - 4 hour | 3 - 4 hour | nominal; maximum drying time of 8 hours |
| Back Pressure | 0.345 - 0.689 MPa | 50.0 - 100 psi | |
| Shot Size | 30 - 80 % | 30 - 80 % | |
| Vent Depth | 0.00381 - 0.00762 cm | 0.00150 - 0.00300 in | |
| Screw Speed | 40 - 70 rpm | 40 - 70 rpm |
Users viewing this material also viewed the following:
- MV Labs PD185 K2Pd(CN)4·3H2O Potassium tetracyanopalladate(II) trihydrate
- MV Labs YB1000 Yb2(SO4)3·8H2O Ytterbium sulfate octahydrate
- SABIC Innovative Plastics Lexan® ML7686 PC (Asia Pacific)
- Polychloroprene Rubber (CR)
- GrafTech eGRAF® SPREADERSHIELD™ SS600 Graphite
- Karina 10/1075-IE White Color Concentrate MBU
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with Control Plasticizer
- Denka TH-11 Transparent Resin Polymer (MBS resin) Polymethacrylate Butadiene Styrene
- Overview of materials for PEKK, Unreinforced
- Hexcel® Redux® 810 Two-Part Epoxy Paste Adhesive
Copyright © lookpolymers.com All Rights Reserved