LTL Color Compounds ColorFast® NY2GF130 Nylon 66, 13% Glass-Filled
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 10% Glass Fiber Filled |
| Manufacturer | LTL Color Compounds |
| Trade Name | ColorFast® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LTL Color Compounds ColorFast® NY2GF130 Nylon 66, 13% Glass-Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
13% glass-filled nylon 6,6All information provided by LTL Color Compounders, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.22 g/cc | 1.22 g/cc | ASTM D792 |
| Water Absorption | 1.5 % | 1.5 % | @ 24 Hours; ASTM D570 |
| Linear Mold Shrinkage | 0.0030 - 0.010 cm/cm | 0.0030 - 0.010 in/in | 0.125; ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| Tensile Strength, Yield | 103 MPa | 15000 psi | 2.0 in/min; ASTM D638 |
| Elongation at Break | 5.0 % | 5.0 % | 2.0 in/min; ASTM D638 |
| Elongation at Yield | 3.0 % | 3.0 % | 2.0 in/min; ASTM D638 |
| Flexural Strength | 152 MPa | 22000 psi | 2.0 in/min; ASTM D790 |
| Flexural Modulus | 4.83 GPa | 700 ksi | 2.0 in/min; ASTM D790 |
| Izod Impact, Notched | 0.534 J/cm @Temperature 22.8 °C |
1.00 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 238 °C | 460 °F | Unannealed (0.250"); ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 260 - 293 °C | 500 - 560 °F | |
| Middle Barrel Temperature | 266 - 293 °C | 510 - 560 °F | |
| Front Barrel Temperature | 266 - 293 °C | 510 - 560 °F | |
| Nozzle Temperature | 260 - 288 °C | 500 - 550 °F | |
| Melt Temperature | 279 - 304 °C | 535 - 580 °F | |
| Mold Temperature | 37.8 - 93.3 °C | 100 - 200 °F | |
| Drying Temperature | 82.2 °C | 180 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | nominal; maximum drying time of 8 hours |
| Back Pressure | 0.345 - 0.689 MPa | 50.0 - 100 psi | |
| Shot Size | 30 - 60 % | 30 - 60 % | |
| Vent Depth | 0.00381 - 0.00762 cm | 0.00150 - 0.00300 in | |
| Screw Speed | 60 - 120 rpm | 60 - 120 rpm |
Users viewing this material also viewed the following:
- BASF Capron® GR40 HS 40% Glass-Filled Nylon 6 (Conditioned) (discontinued **)
- LyondellBasell Montell 1900LCM UHMW Polyethylene
- Garlock 5507 Compressed Inorganic Fiber Gasketing, EPDM Binder
- UBE 1024FDX41 Nylon 6 BOPA Film
- Teknor Apex Telcar® TL-8712R Thermoplastic Elastomer
- Plastics Group Polifil® 628-13GF Glass Fiber-Reinforced Nylon 6/6 (DAM)
- A. Schulman SCHULAMID® 6 NV12 Easy Flow Low Viscosity Nylon 6
- A. Schulman POLYBATCH™ ASC-331 Inorganic Antislip Masterbatch Based in Polyethylene
- ExxonMobil Mobil EAL 224H
Copyright © lookpolymers.com All Rights Reserved