- Acrylonitrile Butadiene Styrene (ABS), Transparent, Molded
- Samsung Cheil Industries Starex® TX-0510 TRABS, Unreinforced
Samsung Cheil Industries Starex® TX-0510 TRABS, Unreinforced
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Transparent, Molded |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Starex® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Starex® TX-0510 TRABS, Unreinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.10 g/cc | 1.10 g/cc | ASTM D792 |
| Melt Flow | 16 g/10 min @Load 10.0 kg, Temperature 220 °C |
16 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 109 | 109 | ASTM D785 |
| Tensile Strength, Yield | 44.1 MPa | 6400 psi | 5 mm/min; ASTM D638 |
| Flexural Strength | 63.7 MPa | 9240 psi | 2.8 mm/min; ASTM D638 |
| Flexural Modulus | 2.06 GPa | 299 ksi | 2.8 mm/min; ASTM D790 |
| Izod Impact, Notched | 1.47 J/cm @Thickness 3.17 mm |
2.76 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Vicat Softening Point | 88.0 °C | 190 °F | B/50; ISO R306 |
| Flammability, UL94 | HB @Thickness 1.50 - 3.00 mm |
HB @Thickness 0.0591 - 0.118 in |
Users viewing this material also viewed the following:
- Fiberfil® J-60/10/E/M Polypropylene Homopolymer, 10% Glass Reinforced, Chemically coupled
- Karina 02/127-FC-LMP Yellow Color Concentrate for PVC
- SYNTHOS Koplen® 0822 FR Expandable Polystyrene
- Schott NEO 1730 Alkaline Earth Aluminosilicate Glass
- Solvay TECHNYLSTARâ„¢ S 216L2 V30 PA6, 30% glass filled, DRY
- Teknor Apex Monprene® MP 7002 Thermoplastic Elastomer
- A. Schulman POLYBATCH™ CE-505-B Concentrate Based In Polyethylene
- DuPont™ Bynel® 50E803 Anhydride Modified Polypropylene
- Solvay Engineered Polymers DEXFLEX® 880 TPO (discontinued **)
- Bulk Molding Compounds BMC T60-6006 Wear Resistant Molding Compound
Copyright © lookpolymers.com All Rights Reserved