LTL Color Compounds ColorFast® FRPS100 Styrene, High Impact
| Category | Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Flame Retardant , Polystyrene, Impact Modified |
| Manufacturer | LTL Color Compounds |
| Trade Name | ColorFast® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LTL Color Compounds ColorFast® FRPS100 Styrene, High Impact.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
V1-rated high impact styreneAll information provided by LTL Color Compounders, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.08 g/cc | 1.08 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0030 - 0.0060 cm/cm | 0.0030 - 0.0060 in/in | 0.125; ASTM D955 |
| Melt Flow | 8.0 g/10 min @Load 5.00 kg, Temperature 200 °C |
8.0 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell L | 55 | 55 | ASTM D785 |
| Tensile Strength at Break | 20.7 MPa | 3000 psi | 2.0 in/min; ASTM D638 |
| Tensile Strength, Yield | 19.3 MPa | 2800 psi | 2.0 in/min; ASTM D638 |
| Elongation at Break | 40 % | 40 % | 2.0 in/min; ASTM D638 |
| Flexural Modulus | 1.86 GPa | 270 ksi | 2.0 in/min; ASTM D790 |
| Izod Impact, Notched | 1.07 J/cm @Temperature 22.8 °C |
2.00 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 82.2 °C | 180 °F | Unannealed (0.250"); ASTM D648 |
| Flammability, UL94 | V-1 | V-1 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 171 - 199 °C | 340 - 390 °F | |
| Middle Barrel Temperature | 193 - 227 °C | 380 - 440 °F | |
| Front Barrel Temperature | 218 - 254 °C | 425 - 490 °F | |
| Nozzle Temperature | 204 - 232 °C | 400 - 450 °F | |
| Melt Temperature | 204 - 238 °C | 400 - 460 °F | |
| Mold Temperature | 10.0 - 71.1 °C | 50.0 - 160 °F | |
| Drying Temperature | 71.1 °C | 160 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | nominal; maximum drying time of 8 hours |
| Back Pressure | 0.345 - 0.689 MPa | 50.0 - 100 psi | |
| Shot Size | 40 - 60 % | 40 - 60 % | |
| Vent Depth | 0.00254 - 0.00762 cm | 0.00100 - 0.00300 in | |
| Screw Speed | 40 - 70 rpm | 40 - 70 rpm |
Users viewing this material also viewed the following:
- Advanced Elastomer Systems Santoprene® 8281-90 Thermoplastic Rubber (discontinued **)
- LG Chemical Lupox® HI2152 PBT+GF15%
- Solvay TECHNYL® A 218C V10 PA66, 10% glass fiber, DRY
- SABIC Innovative Plastics NORYL PN275 PPE+PS
- Thermoseal KLINGERSIL® C-4433 Compressed Inorganic Fiber Sheet
- ExxonMobil Mobil Delvac 50 1650
- A. Schulman FORMION™ FI 391 Ionomer
- Zeon Chemicals Nipol® P70 Polyblend Nitrile Elastomer
- DuPont™ Tedlar® SP TTRJ10SH9 Clear Polyvinyl Fluoride Film
- EMS-Grivory Grivory® HT1V-3 FWA nat PA6T/6I-GF30
Copyright © lookpolymers.com All Rights Reserved