SABIC Innovative Plastics LNP LUBRICOMP Lexan_WR5210R PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP Lexan_WR5210R PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Lubricomp* Lexan_WR5210R compound is a wear resistant, 7% PTFE filled PC.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0060 cm/cm @Thickness 3.20 mm |
0.0040 - 0.0060 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 21.5 g/10 min @Load 1.20 kg, Temperature 300 °C |
21.5 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 55.0 MPa | 7980 psi | Type I, 50 mm/min; ASTM D638 |
| Tensile Strength, Yield | 53.0 MPa | 7690 psi | Type I, 50 mm/min; ASTM D638 |
| Elongation at Break | 75 % | 75 % | Type I, 50 mm/min; ASTM D638 |
| Flexural Yield Strength | 83.0 MPa | 12000 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 2.03 GPa | 294 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 1.81 J/cm | 3.39 ft-lb/in | ASTM D256 |
| Dart Drop, Total Energy | 38.0 J | 28.0 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 126 °C @Thickness 6.40 mm |
259 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| UL RTI, Electrical | 80.0 °C | 176 °F | UL 746B |
| UL RTI, Mechanical with Impact | 80.0 °C | 176 °F | UL 746B |
| UL RTI, Mechanical without Impact | 80.0 °C | 176 °F | UL 746B |
| Flammability, UL94 | HB @Thickness 1.49 mm |
HB @Thickness 0.0587 in |
UL 94 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Gloss | 52 % | 52 % | untextured, 60 degrees; ASTM D523 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Comparative Tracking Index | 175 - 250 V | 175 - 250 V | UL 746A |
| Hot Wire Ignition, HWI | 30 - 60 sec | 30 - 60 sec | UL 746A |
| High Amp Arc Ignition, HAI | >= 120 arcs | >= 120 arcs | UL 746A |
| High Voltage Arc-Tracking Rate, HVTR | 25.4 - 80.0 mm/min | 1.00 - 3.15 in/min | UL 746A |
Users viewing this material also viewed the following:
- Radici Radilon® A ECP3808 (dry) Nylon 66
- Polymer Resources PPX-MF-FRG20 Modified-PPO, 40% Glass/Mineral Reinforced, Flame Retardant
- Karina E550D06/957 Blue PVC Compound
- Lord Adhesives Circalokâ„¢ 6009 A/B Flame Retardant Epoxy Encapsulant
- MRC Polymers NAXALOYâ„¢ 780 GF11 PC+PBT Polyester Blend, 11% Glass Fiber Filled
- Gouda Vuurvast CURON 130 HRCC RAPID Dense Refractory Castable
- Teknor Apex Telcar® TL-2560F Thermoplastic Elastomer
- A. Schulman POLYPUR™ FPU 1380 Thermoplastic Polyurethane Compound
- Hippe EP CC 31 Woven Cotton Cloth Reinforced Epoxy Resin - Round, Molded Tube and Rod
- 3M 5153 PTFE Glass Cloth Tape
Copyright © lookpolymers.com All Rights Reserved