LTL Color Compounds ColorFast® FRPBT130 PBT, 30% Glass-Filled
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 30% Glass Fiber Filled |
| Manufacturer | LTL Color Compounds |
| Trade Name | ColorFast® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LTL Color Compounds ColorFast® FRPBT130 PBT, 30% Glass-Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
30% glass-filled V-0 rated PBT - UL listedAll information provided by LTL Color Compounders, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.14 g/cc | 1.14 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0050 - 0.0080 cm/cm | 0.0050 - 0.0080 in/in | 0.125; ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 119 | 119 | ASTM D785 |
| Tensile Strength at Break | 186 MPa | 27000 psi | 2.0 in/min; ASTM D638 |
| Tensile Strength, Yield | 117 MPa | 17000 psi | 2.0 in/min; ASTM D638 |
| Flexural Modulus | 7.58 GPa | 1100 ksi | 2.0 in/min; ASTM D790 |
| Izod Impact, Notched | 0.694 J/cm @Temperature 22.8 °C |
1.30 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 204 °C | 400 °F | Unannealed (0.250"); ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 0.830 mm |
V-0 @Thickness 0.0327 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 243 - 266 °C | 470 - 510 °F | |
| Middle Barrel Temperature | 249 - 271 °C | 480 - 520 °F | |
| Front Barrel Temperature | 254 - 277 °C | 490 - 530 °F | |
| Nozzle Temperature | 249 - 271 °C | 480 - 520 °F | |
| Melt Temperature | 254 - 277 °C | 490 - 530 °F | |
| Mold Temperature | 65.6 - 87.8 °C | 150 - 190 °F | |
| Drying Temperature | 121 °C | 250 °F | |
| Dry Time | 3 - 4 hour | 3 - 4 hour | nominal; maximum drying time of 12 hours |
| Back Pressure | 0.345 - 0.689 MPa | 50.0 - 100 psi | |
| Shot Size | 40 - 60 % | 40 - 60 % | |
| Vent Depth | 0.00127 - 0.00254 cm | 0.000500 - 0.00100 in | |
| Screw Speed | 40 - 70 rpm | 40 - 70 rpm |
Users viewing this material also viewed the following:
- MV Labs LU810 Lu2O3 Lutetium oxide
- Huntsman IROGRAN® A 70 H 4673 M Polyester-Based TPU-Injection Molding Grade
- FloMet Fe-42% Ni Controlled Expansion Alloy
- LTL Color Compounds ColorRxâ„¢ ABS-0500RX Biocompatible ABS
- Chesterton ARC BX1 Sliding Wear Compound
- ConocoPhillips Hydroclear® 46 Turbine Oil
- Abatron AboCast 8502-5/AboCure 8502-5 Colorless, Low-Exotherm Epoxy Casting Compound
- BASF Ultramid® 8333G HI HS BK-102 33% Glass Filled PA6 (Conditioned)
Copyright © lookpolymers.com All Rights Reserved