LG Chemical Lupoy 1200-03 Polycarbonate Resin

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer LG Chemical
Trade Name LUPOY
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LG Chemical Lupoy 1200-03 Polycarbonate Resin.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
Description: LUPOY PC 1200-03 resin is designed for extrusion and injection molding products. It exhibits an excellent physical property balance of heat resistance, transparency and impact strength.Main Characteristics: FDA, High Viscosity, No mold release agent and No UV absorbersApplications: Toys, Bottle and caps, Packaging applications and Food utensils.CAS: 103598-77-2Information provided by LG Chemical
Physical Properties Metric English Comments
Specific Gravity 1.20 g/cc
1.20 g/cc
ASTM D792
Water Absorption 0.32 %

@Temperature 23.0 °C
 0.32 %

@Temperature 73.4 °F
 equilibrium, 50% RH; ASTM D570
0.15 %

@Temperature 23.0 °C,
Time 86400 sec
 0.15 %

@Temperature 73.4 °F,
Time 24.0 hour
 ASTM D570
Linear Mold Shrinkage, Flow 0.00050 - 0.00070 cm/cm
0.00050 - 0.00070 in/in
ASTM D955
Melt Flow 3.0 g/10 min

@Load 1.20 kg,
Temperature 300 °C
 3.0 g/10 min

@Load 2.65 lb,
Temperature 572 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell M 74
74
ASTM D785
Hardness, Rockwell R 118
118
ASTM D785
Tensile Strength, Ultimate 72.0 MPa
10400 psi
ASTM D638
Tensile Strength, Yield 60.0 MPa
8700 psi
50mm/min; ASTM D638
Elongation at Break 150 %
150 %
ASTM D638
Elongation at Yield 6.0 %
6.0 %
ASTM D638
Tensile Modulus 2.41 GPa
350 ksi
ASTM D638
Flexural Yield Strength 96.0 MPa
13900 psi
ASTM D790
Flexural Modulus 2.41 GPa
350 ksi
ASTM D790
Izod Impact, Unnotched NB

@Temperature 23.0 °C
 NB

@Temperature 73.4 °F
 ASTM D256
Dart Drop, Total Energy 10.62 J

@Thickness 3.20 mm
 7.833 ft-lb

@Thickness 0.126 in
 203m/min; ASTM D3763
Abrasion 45

@Load 1.00 kg
 45

@Load 2.20 lb
 [%], CS-10 F wheel, 500 cycles; ASTM D1044
Thermal Properties Metric English Comments
CTE, linear 68.0 µm/m-°C

@Temperature -40.0 - 82.0 °C
 37.8 µin/in-°F

@Temperature -40.0 - 180 °F
 ASTM D696
Hot Ball Pressure Test >= 125 °C
>= 257 °F
IEC 598-1
Deflection Temperature at 0.46 MPa (66 psi) 146 °C

@Thickness 4.00 mm
 295 °F

@Thickness 0.157 in
 Annealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 132 °C

@Thickness 4.00 mm
 270 °F

@Thickness 0.157 in
 Unannealed; ASTM D648
143 °C

@Thickness 4.00 mm
 289 °F

@Thickness 0.157 in
 Annealed; ASTM D648
Vicat Softening Point 151 °C

@Load 5.10 kg
 304 °F

@Load 11.2 lb
 50°C/hr; ASTM D1525
Softening Point 150 - 200 °C
302 - 392 °F
melting point per MSDS
Flammability, UL94 HB

@Thickness 3.00 mm
 HB

@Thickness 0.118 in
 ASTM D635
V-2

@Thickness 0.500 mm
 V-2

@Thickness 0.0197 in
 ASTM D635
V-2

@Thickness 1.60 - 1.70 mm
 V-2

@Thickness 0.0630 - 0.0669 in
 ASTM D635
Flash Point >= 450 °C
>= 842 °F
Oxygen Index 26 %
26 %
ASTM D2863
Glow Wire Test 850 °C

@Thickness 2.00 mm,
Time 5.00 sec
 1560 °F

@Thickness 0.0787 in,
Time 0.00139 hour
 IEC 695-2-1
Optical Properties Metric English Comments
Refractive Index 1.586
1.586
ASTM D542
Haze 0.70 - 1.5 %
0.70 - 1.5 %
ASTM D1003
Transmission, Visible 89 %
89 %
ASTM D1003
Electrical Properties Metric English Comments
Volume Resistivity 2.00e+17 ohm-cm
2.00e+17 ohm-cm
ASTM D257
Dielectric Constant 3.0

@Frequency 60.0 Hz
 3.0

@Frequency 60.0 Hz
 ASTM D150
Dielectric Strength 17.0 kV/mm
432 kV/in
ASTM D149
Dissipation Factor 0.0010

@Frequency 60.0 Hz
 0.0010

@Frequency 60.0 Hz
 ASTM D150
Comparative Tracking Index 250 V

@Thickness 2.00 mm
 250 V

@Thickness 0.0787 in
 IEC 112
Descriptive Properties Value Comments
Autoignition Temperature >460°C
Average Extent of Burning ASTM D635