Polymer Property : Tensile Strength, Ultimate = 72.0 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	72.0 MPa	10400 psi
Polycasa Acryl® G 87 E Acrylic Grade for extruding semi-finished products such as twin-strapped panels, profile and tubes, as well as injection molding of watch glasses, dishes, bowls, water-tap hand grips and bathroom fittings, ..
Tensile Strength, Ultimate	72.0 MPa @Temperature 90.0 °C	10400 psi @Temperature 194 °F	ISO 527
LATI LARIL 13 G/20 20% Glass Fiber Reinforced Polyphenylene Oxide (PPOm) (Unverified Data**) Description: Laril thermoplastics are polyphenylene oxide (PPOm) products. They exhibit excellent toughness, even at low temperatures, good thermal resistance and dimensional stability are the most ..
Tensile Strength, Ultimate	72.0 MPa	10400 psi	ASTM D638
Glastic Laminates/Shapes FHT Flexible High Temperature Polyester Laminate Data provided by Glastic Corporation.Excellent flexibility plus good electrical strength retention values after long term heat aging. Widely used in motors and dry type transformers.
Tensile Strength, Ultimate	72.0 MPa	10400 psi	ASTM D638
LG Chemical Lupoy 1200-03 Polycarbonate Resin Description: LUPOY PC 1200-03 resin is designed for extrusion and injection molding products. It exhibits an excellent physical property balance of heat resistance, transparency and impact strength...
Tensile Strength, Ultimate	72.0 MPa	10400 psi	ASTM D638
LG Chemical Lupoy 1201-05 Polycarbonate Resin Description: LUPOY PC 1201-05 resin is designed for extrusion and injection molding products. It exhibits an excellent physical property balance of heat resistance, transparency and impact strength...
Tensile Strength, Ultimate	72.0 MPa	10400 psi	ASTM D638
LG Chemical Lupoy 1201-10 Polycarbonate Resin Description: LUPOY PC 1201-10 resin is designed for extrusion and injection molding products. It exhibits an excellent physical property balance of heat resistance, transparency and impact strength...
Tensile Strength, Ultimate	72.0 MPa	10400 psi	ASTM D638
LG Chemical Lupoy 1261-03 Polycarbonate Resin Description: LUPOY PC 1261-03 resin is designed for extrusion blow molding(EBM) and injection stretch blow molding (ISBM) products. It exhibits an excellent physical property balance of heat resista..
Tensile Strength, Ultimate	72.0 MPa	10400 psi	ASTM D638
LG Chemical Lupoy 1301V-7 Polycarbonate Resin Description: LUPOY PC 1301V-07 resin is designed for extrusion and injection molding products. It exhibits an excellent physical property balance of heat resistance, transparency and impact strength..
Tensile Strength, Ultimate	72.0 MPa	10400 psi	ASTM D638
LG Chemical Lupoy 1302-07 Polycarbonate Resin Description: LUPOY PC 1302-07 resin is designed for extrusion and injection molding products. It exhibits an excellent physical property balance of heat resistance, transparency and impact strength...
Tensile Strength, Ultimate	72.0 MPa	10400 psi	ASTM D638
LG Chemical Lupoy 1600-03 Polycarbonate Resin Description: LUPOY PC 1600-03 resin is designed for extrusion products. It exhibits an excellent physical property balance of heat resistance, transparency and impact strength.Main Characteristics: ..
Tensile Strength, Ultimate	72.0 MPa @Temperature 22.0 Â°C	10400 psi @Temperature 71.6 Â°F	25mm flat samples, compression moulded; ISO 527-4
Menzolit MenzolitÂ® SMC 0180 Unsaturated Polyester UP SMC 0180 is a general purpose SMC for applications in the field of electrical industry. Typical applications are housings, covers, wire distribution boxes and metering cabinets. The material meets t..
Tensile Strength, Ultimate	72.0 MPa	10400 psi	ASTM D638
LG Chemical Lupoy NF1009F 08R Polycarbonate Resin Description: LUPOY NF 1009F08R, eco-friendly UL94 V0/2.0 mm, is designed for extrusion and injection molding products. It combines an excellent physical property balance of heat resistance, transpar..
Tensile Strength, Ultimate	72.0 MPa	10400 psi	ASTM D638
LG Chemical Lupoy 1201HP-08 Polycarbonate Resin Description: LUPOY PC 1201HP-08 resin is designed for extrusion and injection molding products. It exhibits an excellent physical property balance of heat resistance, transparency and impact strengt..
Tensile Strength, Ultimate	72.0 MPa	10400 psi	ASTM D638
LG Chemical Lupoy 1302UV-08 Polycarbonate Resin Description: LUPOY PC 1302UV-08 resin is designed for extrusion and injection molding products. It exhibits an excellent physical property balance of heat resistance, transparency and impact strengt..
Tensile Strength, Ultimate	72.0 MPa	10400 psi	ASTM D638
LG Chemical Lupoy 1303-07 Polycarbonate Resin Description: LUPOY PC 1303-07 resin is designed for extrusion and injection molding products. It exhibits an excellent physical property balance of heat resistance, transparency and impact strength...
Tensile Strength, Ultimate	72.0 MPa	10400 psi	5mm/min; ISO 527
Styrolution LuranÂ® 358 N SAN Luran 358 N is an easy-flowing injection molding SAN grade.Information provided by STYROLUTION, which is a joint venture between BASF and INEOS.
Tensile Strength, Ultimate	72.0 MPa	10400 psi	ASTM D638
Covestro Makrolon® 2605 Polycarbonate, Injection Grade Easy flowing injection molding grade with easy mold release, Makrolon grade 2658 for food contact applications.Information provided by Bayer.As of 1 September 2015, Bayer MaterialScience was separat..
Tensile Strength, Ultimate	72.0 MPa	10400 psi	ASTM D638
Covestro Makrolon® 2858 Polycarbonate, Injection Grade Medium flowing BgVV- and FDA injection molding grade, for food contact applications, better resistance to hot water.Information provided by Bayer.As of 1 September 2015, Bayer MaterialScience was se..
Tensile Strength, Ultimate	72.0 MPa	10400 psi	ASTM D638
Covestro Makrolon® 6485 Polycarbonate, Injection Grade Medium viscosity, flame retardant injection molding grade with easy mold release, not available in transparent colors.Information provided by Bayer.As of 1 September 2015, Bayer MaterialScience was ..
Tensile Strength, Ultimate	72.0 MPa	10400 psi	5 mm/min
Arkema Group Rilsan® AZM 15 TLD Nylon 12, 15% Glass Fiber Filled (Conditioned) Designation ISO 1874-PA12,MHLR,16-030,GF15Rigid grade with glass fiber filler (15%) for injection molding.Available color: natural. Light and heat stabilized. Mold-release agent.Rigidity combined wi..
Tensile Strength, Ultimate	72.0 MPa	10400 psi	ASTM D638
Chem Polymer Chemlon 182 Nylon 66, Flame Retarded A non-halogenated, unfilled nylon 66 used in electrical applications where improved flame retardancy is required. The material has excellent moldability, good snap-fit properties and is available i..
Tensile Strength, Ultimate	72.0 MPa	10400 psi	ASTM D638
A. Schulman ComAlloy Lubrilon® 604 Nylon 6/6, PTFE/Molybdenum Disulfide Filled, Flow Enhanced Data provided by the manufacturer, ComAlloy International Company. High performance and excellent lubricity with minimal surface wear.The ComAlloy product line has been integrated into the A Schulma..
Tensile Strength, Ultimate	72.0 MPa	10400 psi	ASTM D638
A. Schulman ComAlloy Lubrilon® 605 Nylon 6/6, PTFE Filled, Flow Enhanced Data provided by the manufacturer, ComAlloy International Company. High performance and excellent lubricity with minimal surface wear.The ComAlloy product line has been integrated into the A Schulma..
Tensile Strength, Ultimate	72.0 MPa	10400 psi	ASTM D638
A. Schulman ComAlloy Comtuf® 631 Nylon 6/6, Glass Reinforced, Impact Modified Data provided by the manufacturer, ComAlloy International Company.13% Glass Reinforced. Superior toughness and impact resistance characterize Comtuf® materialsThe ComAlloy product line has been int..
Tensile Strength, Ultimate	72.0 MPa	10400 psi	ASTM D638
A. Schulman ComAlloy Hiloy® 272 Polystyrene Alloy, Glass Reinforced, Flow Enhanced Data provided by the manufacturer, ComAlloy International Company.20% Glass Reinforced.The ComAlloy product line has been integrated into the A Schulman product line.
Tensile Strength, Ultimate	72.0 MPa	10400 psi	ASTM D638
PolyOne Edgetek® CTXC-084 Polyethersulfone - Mineral Reinforced (discontinued **) Data provided by PolyOne.
Tensile Strength, Ultimate	72.0 MPa	10400 psi	ASTM D638
Sumitomo Bakelite North America FM 4017F Fiberglass and Mineral Reinforced Phenolic FM 4017F is a fiberglass and mineral reinforced phenolic molding compound, with excellent dimensional stability and good strength at elevated temperatures. Information supplied by Sumitomo Bak North..
Tensile Strength, Ultimate	72.0 MPa	10400 psi	ASTM D638
UBE UPIMOL® SA201 Heat-Resistant Polyimide Shape Description: UPIMOL SA201 is an excellent heat-resistant polyimide shape, based on Biphenyl tetracarboxilic dianhydride(BPDA) originally developed by UBE. UPIMOL SA201 can save costs, and suit vario..
Tensile Strength, Ultimate	72.0 MPa	10400 psi	ASTM D638
Covestro Makrolon® LQ-2847 Polycarbonate, Lens Quality Optical, Mold Release, UV Stabilized (discontinued **) Information provided by Bayer Corporation, Plastics DivisionAs of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and has officially adopted its new name – Covestro. This produ..