LG Chemical LUPOY SC2202 PC+GF20%, High Impact

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, 20% Glass Filled , Polycarbonate, Impact Modified
Manufacturer LG Chemical
Trade Name LUPOY
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LG Chemical LUPOY SC2202 PC+GF20%, High Impact.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Injection Molding, PC+GF20%, Good Toughness, Good Impact, Chemical ResistanceApplication: Mobile Phone HousingCAS: 103598-77-2 and 65997-17-3Information provided by LG Chemical
Physical Properties Metric English Comments
Specific Gravity 1.35 g/cc
1.35 g/cc
ASTM D792
Maximum Moisture Content 0.020
0.020
Injection Molding
Linear Mold Shrinkage, Flow 0.010 - 0.030 cm/cm

@Thickness 3.20 mm
 0.010 - 0.030 in/in

@Thickness 0.126 in
 ASTM D955
Melt Flow 6.0 g/10 min

@Load 1.20 kg,
Temperature 300 °C
 6.0 g/10 min

@Load 2.65 lb,
Temperature 572 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 122
122
ASTM D785
Tensile Strength, Yield 90.7 MPa

@Thickness 3.20 mm
 13200 psi

@Thickness 0.126 in
 5mm/min; ASTM D638
Elongation at Break 7.0 %

@Thickness 3.20 mm
 7.0 %

@Thickness 0.126 in
 5mm/min; ASTM D638
Flexural Yield Strength 147 MPa

@Thickness 3.20 mm
 21300 psi

@Thickness 0.126 in
 1.3mm/min; ASTM D790
Flexural Modulus 4.51 GPa

@Thickness 3.20 mm
 654 ksi

@Thickness 0.126 in
 1.3mm/min; ASTM D790
Izod Impact, Notched >= 2.06 J/cm

@Thickness 3.20 mm,
Temperature 23.0 °C
 >= 3.86 ft-lb/in

@Thickness 0.126 in,
Temperature 73.4 °F
 ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 144 °C

@Thickness 6.40 mm
 291 °F

@Thickness 0.252 in
 Unannealed; ASTM D648
UL RTI, Electrical 80.0 °C

@Thickness >=0.750 mm
 176 °F

@Thickness >=0.0295 in
80.0 °C

@Thickness >=3.00 mm
 176 °F

@Thickness >=0.118 in
UL RTI, Mechanical with Impact 80.0 °C

@Thickness >=0.750 mm
 176 °F

@Thickness >=0.0295 in
80.0 °C

@Thickness >=3.00 mm
 176 °F

@Thickness >=0.118 in
UL RTI, Mechanical without Impact 80.0 °C

@Thickness >=0.750 mm
 176 °F

@Thickness >=0.0295 in
80.0 °C

@Thickness >=3.00 mm
 176 °F

@Thickness >=0.118 in
Flammability, UL94 HB

@Thickness >=0.750 mm
 HB

@Thickness >=0.0295 in
HB

@Thickness >=3.00 mm
 HB

@Thickness >=0.118 in
Processing Properties Metric English Comments
Rear Barrel Temperature 280 - 295 °C
536 - 563 °F
Injection Molding
Middle Barrel Temperature 285 - 305 °C
545 - 581 °F
Injection Molding
Front Barrel Temperature 290 - 305 °C
554 - 581 °F
Injection Molding
Nozzle Temperature 290 - 305 °C
554 - 581 °F
Injection Molding
Melt Temperature 295 - 315 °C
563 - 599 °F
Injection Molding
Mold Temperature 100 - 140 °C
212 - 284 °F
Injection Molding
Drying Temperature 100 - 120 °C
212 - 248 °F
Injection Molding
Dry Time 3.00 - 5.00 hour
3.00 - 5.00 hour
Injection Molding
Back Pressure 0.981 - 3.92 MPa
142 - 569 psi
Injection Molding
Screw Speed 40 - 70 rpm
40 - 70 rpm
Injection Molding