- LG Chemical LUPOY GN5001RFT PC/ABS, Halogen Free Flame Retardant
LG Chemical LUPOY GN5001RFT PC/ABS, Halogen Free Flame Retardant
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | LG Chemical |
| Trade Name | LUPOY |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical LUPOY GN5001RFT PC/ABS, Halogen Free Flame Retardant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Injection Molding, PC/ABS, Halogen Free Flame Retardant, Good FlowApplication: E&E (TV, Navigation Housing)CAS: 103598-77-2, 9003-56-9 and 181028-79-5Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.19 g/cc | 1.19 g/cc | ASTM D792 |
| Maximum Moisture Content | 0.020 | 0.020 | Injection Molding |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 28 g/10 min @Load 2.16 kg, Temperature 250 °C |
28 g/10 min @Load 4.76 lb, Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 56.9 MPa @Thickness 3.20 mm |
8250 psi @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Elongation at Break | >= 20 % @Thickness 3.20 mm |
>= 20 % @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Flexural Yield Strength | 95.1 MPa @Thickness 3.20 mm |
13800 psi @Thickness 0.126 in |
10mm/min; ASTM D790 |
| Flexural Modulus | 2.55 GPa @Thickness 3.20 mm |
370 ksi @Thickness 0.126 in |
10mm/min; ASTM D790 |
| Izod Impact, Notched | 5.20 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
9.74 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 85.0 °C @Thickness 6.40 mm |
185 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| UL RTI, Electrical | 80.0 °C | 176 °F | |
| UL RTI, Mechanical with Impact | 80.0 °C | 176 °F | |
| UL RTI, Mechanical without Impact | 85.0 °C | 185 °F | |
| Flammability, UL94 | V-0 @Thickness >=1.20 mm |
V-0 @Thickness >=0.0472 in |
|
| V-0 @Thickness >=2.50 mm |
V-0 @Thickness >=0.0984 in |
||
| V-0 @Thickness >=3.00 mm |
V-0 @Thickness >=0.118 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 220 - 240 °C | 428 - 464 °F | Injection Molding |
| Middle Barrel Temperature | 235 - 255 °C | 455 - 491 °F | Injection Molding |
| Front Barrel Temperature | 250 - 265 °C | 482 - 509 °F | Injection Molding |
| Nozzle Temperature | 250 - 265 °C | 482 - 509 °F | Injection Molding |
| Melt Temperature | 235 - 265 °C | 455 - 509 °F | Injection Molding |
| Mold Temperature | 50.0 - 80.0 °C | 122 - 176 °F | Injection Molding |
| Drying Temperature | 75.0 - 85.0 °C | 167 - 185 °F | Injection Molding |
| Dry Time | 3.00 - 4.00 hour | 3.00 - 4.00 hour | Injection Molding |
| Back Pressure | 0.00200 - 0.00600 MPa | 0.290 - 0.870 psi | Injection Molding |
| Screw Speed | 40 - 70 rpm | 40 - 70 rpm | Injection Molding |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® ML6018R PC (Asia Pacific)
- Polykemi AB POLYfill PP EIP12030RF Polypropylene/EPDM, Mineral Reinforced
- Lehmann & Voss LUVOCOM® 1105-8169 PEEK, with carbon fiber
- DuPont™ Fusabond® E158H Polymer Modifier
- BASF Heligoen® Green L 9361 Color Additive
- Alliance Polymers Viprene™ P85A-22U-BLK Thermoplastic Vulcanizate Elastomer
- 3M Controltac™ 180 Graphic Film
- E-Polymers SEPAZ® C130HS 30% Glass Fiber Reinforced High Temperature Stabilized LCP Resin
- Bulk Molding Compounds BMC T40(18) Die Casting Replacement Grade Molding Compound
Copyright © lookpolymers.com All Rights Reserved