LG Chemical LUPOY GN1008RF PC, Halogen Free, Flame Retardant, High impact strength

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Unreinforced, Flame Retardant
Manufacturer LG Chemical
Trade Name LUPOY
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LG Chemical LUPOY GN1008RF PC, Halogen Free, Flame Retardant, High impact strength.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Injection Molding, PC, Halogen Free Flame Retardant, High impact strengthApplication: IT&OA (Notebook PC battery pack housing)CAS: 103598-77-2, 137050-02-03 and 139189-30-3Information provided by LG Chemical
Physical Properties Metric English Comments
Specific Gravity 1.19 g/cc
1.19 g/cc
ASTM D792
Maximum Moisture Content 0.040
0.040
Injection Molding
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm

@Thickness 3.20 mm
 0.0050 - 0.0070 in/in

@Thickness 0.126 in
 ASTM D955
Melt Flow 18 g/10 min

@Load 1.20 kg,
Temperature 300 °C
 18 g/10 min

@Load 2.65 lb,
Temperature 572 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength, Yield 59.8 MPa

@Thickness 3.20 mm
 8680 psi

@Thickness 0.126 in
 50mm/min; ASTM D638
Elongation at Break 100 %

@Thickness 3.20 mm
 100 %

@Thickness 0.126 in
 50mm/min; ASTM D638
Flexural Yield Strength 91.2 MPa

@Thickness 3.20 mm
 13200 psi

@Thickness 0.126 in
 10mm/min; ASTM D790
Flexural Modulus 2.35 GPa

@Thickness 3.20 mm
 341 ksi

@Thickness 0.126 in
 10mm/min; ASTM D790
Izod Impact, Notched >= 7.85 J/cm

@Thickness 3.20 mm,
Temperature 23.0 °C
 >= 14.7 ft-lb/in

@Thickness 0.126 in,
Temperature 73.4 °F
 ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) >= 101 °C

@Thickness 6.40 mm
 >= 214 °F

@Thickness 0.252 in
 Unannealed; ASTM D648
UL RTI, Electrical 80.0 °C
176 °F
UL RTI, Mechanical with Impact 80.0 °C
176 °F
UL RTI, Mechanical without Impact 80.0 °C
176 °F
Flammability, UL94 V-2

@Thickness >=0.400 mm
 V-2

@Thickness >=0.0157 in
V-0

@Thickness >=3.00 mm
 V-0

@Thickness >=0.118 in
V-0

@Thickness >=0.800 mm
 V-0

@Thickness >=0.0315 in
V-0

@Thickness >=0.600 mm
 V-0

@Thickness >=0.0236 in
Processing Properties Metric English Comments
Rear Barrel Temperature 245 - 260 °C
473 - 500 °F
Injection Molding
Middle Barrel Temperature 260 - 275 °C
500 - 527 °F
Injection Molding
Front Barrel Temperature 265 - 280 °C
509 - 536 °F
Injection Molding
Nozzle Temperature 270 - 285 °C
518 - 545 °F
Injection Molding
Melt Temperature 245 - 285 °C
473 - 545 °F
Injection Molding
Mold Temperature 70.0 - 90.0 °C
158 - 194 °F
Injection Molding
Drying Temperature 85.0 - 95.0 °C
185 - 203 °F
Injection Molding
Dry Time 3.00 - 5.00 hour
3.00 - 5.00 hour
Injection Molding
Back Pressure 0.981 - 1.96 MPa
142 - 284 psi
Injection Molding
Screw Speed 40 - 70 rpm
40 - 70 rpm
Injection Molding