LG Chemical LUPOY GN1002FL PC, Halogen Free, Flame Retardant, High Flow

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Unreinforced, Flame Retardant
Manufacturer LG Chemical
Trade Name LUPOY
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LG Chemical LUPOY GN1002FL PC, Halogen Free, Flame Retardant, High Flow.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Injection Molding, PC, Halogen Free Flame Retardant, High Flow, High ImpactApplication: IT/OA (M/P Battery Inner Pack Housing)CAS: 103598-77-2, 25232-40-0 and 139189-30-3Information provided by LG Chemical
Physical Properties Metric English Comments
Specific Gravity 1.20 g/cc
1.20 g/cc
ASTM D792
Maximum Moisture Content 0.020
0.020
Injection Molding
Linear Mold Shrinkage, Flow 0.0050 - 0.0080 cm/cm

@Thickness 3.20 mm
 0.0050 - 0.0080 in/in

@Thickness 0.126 in
 ASTM D955
Melt Flow 25 g/10 min

@Load 1.20 kg,
Temperature 300 °C
 25 g/10 min

@Load 2.65 lb,
Temperature 572 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 117
117
ASTM D785
Tensile Strength, Yield 60.8 MPa

@Thickness 3.20 mm
 8820 psi

@Thickness 0.126 in
 50mm/min; ASTM D638
Elongation at Break >= 100 %

@Thickness 3.20 mm
 >= 100 %

@Thickness 0.126 in
 50mm/min; ASTM D638
Flexural Yield Strength 92.2 MPa

@Thickness 3.20 mm
 13400 psi

@Thickness 0.126 in
 10mm/min; ASTM D790
Flexural Modulus 2.29 GPa

@Thickness 3.20 mm
 333 ksi

@Thickness 0.126 in
 10mm/min; ASTM D790
Izod Impact, Notched >= 6.37 J/cm

@Thickness 3.20 mm,
Temperature 23.0 °C
 >= 11.9 ft-lb/in

@Thickness 0.126 in,
Temperature 73.4 °F
 ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) >= 115 °C

@Thickness 6.40 mm
 >= 239 °F

@Thickness 0.252 in
 Unannealed; ASTM D648
UL RTI, Electrical 80.0 °C

@Thickness >=1.50 mm
 176 °F

@Thickness >=0.0591 in
80.0 °C

@Thickness >=3.00 mm
 176 °F

@Thickness >=0.118 in
UL RTI, Mechanical with Impact 80.0 °C

@Thickness >=1.50 mm
 176 °F

@Thickness >=0.0591 in
80.0 °C

@Thickness >=3.00 mm
 176 °F

@Thickness >=0.118 in
UL RTI, Mechanical without Impact 80.0 °C

@Thickness >=1.50 mm
 176 °F

@Thickness >=0.0591 in
80.0 °C

@Thickness >=3.00 mm
 176 °F

@Thickness >=0.118 in
Flammability, UL94 V-0

@Thickness >=1.50 mm
 V-0

@Thickness >=0.0591 in
V-0

@Thickness >=2.00 mm
 V-0

@Thickness >=0.0787 in
5VA

@Thickness >=2.00 mm
 5VA

@Thickness >=0.0787 in
Processing Properties Metric English Comments
Rear Barrel Temperature 270 - 285 °C
518 - 545 °F
Injection Molding
Middle Barrel Temperature 275 - 290 °C
527 - 554 °F
Injection Molding
Front Barrel Temperature 275 - 290 °C
527 - 554 °F
Injection Molding
Nozzle Temperature 270 - 285 °C
518 - 545 °F
Injection Molding
Melt Temperature 275 - 290 °C
527 - 554 °F
Injection Molding
Mold Temperature 80.0 - 100 °C
176 - 212 °F
Injection Molding
Drying Temperature 90.0 - 100 °C
194 - 212 °F
Injection Molding
Dry Time 3.00 - 4.00 hour
3.00 - 4.00 hour
Injection Molding
Back Pressure 0.981 - 3.92 MPa
142 - 569 psi
Injection Molding
Screw Speed 40 - 80 rpm
40 - 80 rpm
Injection Molding