SABIC Innovative Plastics Cycoloy® C6800 PC+ABS

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Cycoloy®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Cycoloy® C6800 PC+ABS.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PC+ABS, nonchlorinated, nonbrominated flame retardant.This data was supplied by SABIC-IP for the Americas region.
Physical Properties Metric English Comments
Specific Gravity 1.18 g/cc
1.18 g/cc
color; ASTM D 792
1.19 g/cc
1.19 g/cc
ASTM D 792
Water Absorption 0.10 %

@Time 86400 sec
 0.10 %

@Time 24.0 hour
 ASTM D 570
Moisture Absorption at Equilibrium 0.40 %

@Temperature 23.0 °C
 0.40 %

@Temperature 73.4 °F
 ASTM D 570
Linear Mold Shrinkage, Flow 0.0040 - 0.0060 cm/cm

@Thickness 3.20 mm
 0.0040 - 0.0060 in/in

@Thickness 0.126 in
 SABIC Method
Linear Mold Shrinkage, Transverse 0.0040 - 0.0060 cm/cm

@Thickness 3.20 mm
 0.0040 - 0.0060 in/in

@Thickness 0.126 in
 SABIC Method
Melt Flow 11 g/10 min

@Load 2.16 kg,
Temperature 260 °C
 11 g/10 min

@Load 4.76 lb,
Temperature 500 °F
 ASTM D 1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 120
120
ASTM D 785
Tensile Strength, Yield 62.0 MPa
8990 psi
Type I, 50 mm/min; ASTM D 638
Elongation at Break 50 %
50 %
Type I, 50 mm/min; ASTM D 638
Elongation at Yield 5.0 %
5.0 %
Type I, 50 mm/min; ASTM D 638
Tensile Modulus 2.68 GPa
389 ksi
50 mm/min; ASTM D 638
Flexural Yield Strength 103 MPa
14900 psi
1.3 mm/min, 50 mm span; ASTM D 790
Flexural Modulus 2.68 GPa
389 ksi
1.3 mm/min, 50 mm span; ASTM D 790
Izod Impact, Notched 5.87 J/cm

@Temperature 23.0 °C
 11.0 ft-lb/in

@Temperature 73.4 °F
 ASTM D 256
Impact Test 67.0 J

@Temperature 23.0 °C
 49.4 ft-lb

@Temperature 73.4 °F
 Instrumented Impact Total Energy; ASTM D 3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 72.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 40.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
CTE, linear, Transverse to Flow 72.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 40.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
Thermal Conductivity 0.200 W/m-K
1.39 BTU-in/hr-ft²-°F
ASTM C 177
Deflection Temperature at 0.46 MPa (66 psi) 109 °C

@Thickness 3.20 mm
 228 °F

@Thickness 0.126 in
 unannealed; ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 98.0 °C

@Thickness 3.20 mm
 208 °F

@Thickness 0.126 in
 unannealed; ASTM D 648
UL RTI, Electrical 90.0 °C
194 °F
UL 746B
UL RTI, Mechanical with Impact 85.0 °C
185 °F
UL 746B
UL RTI, Mechanical without Impact 90.0 °C
194 °F
UL 746B
Flammability, UL94 V-1

@Thickness 1.47 mm
 V-1

@Thickness 0.0579 in
 UL 94
V-0

@Thickness 2.00 mm
 V-0

@Thickness 0.0787 in
 UL 94
5VB

@Thickness 2.59 mm
 5VB

@Thickness 0.102 in
 UL 94
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+17 ohm-cm
1.00e+17 ohm-cm
ASTM D 257
Surface Resistance >= 1.00e+14 ohm
>= 1.00e+14 ohm
ASTM D 257
Dielectric Constant 3.0

@Frequency 50.0 - 60.0 Hz
 3.0

@Frequency 50.0 - 60.0 Hz
 ASTM D 150
3.0

@Frequency 100 Hz
 3.0

@Frequency 100 Hz
 ASTM D 150
Dielectric Strength 17.9 kV/mm

@Thickness 3.20 mm
 455 kV/in

@Thickness 0.126 in
 in oil; ASTM D 149
Dissipation Factor 0.0048

@Frequency 50.0 - 60.0 Hz
 0.0048

@Frequency 50.0 - 60.0 Hz
 ASTM D 150
Comparative Tracking Index >= 600 V
>= 600 V
PLC code 0; UL 746A
Hot Wire Ignition, HWI 30 - 60 sec
30 - 60 sec
PLC code 2; UL 746A
High Amp Arc Ignition, HAI >= 120 arcs
>= 120 arcs
surface, PLC code 0; UL 746A