Braskem CX7020 Cast Film Extrusion Low Density Polyethylene
| Category | Polymer , Film , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Film Grade |
| Manufacturer | Braskem |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Braskem CX7020 Cast Film Extrusion Low Density Polyethylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Smooth or embossed films for diapers, disposable sheets, etc. Films for lamination, Injection-Blow Molding, Foamed applications.Information provided by Braskem.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.922 g/cc | 0.922 g/cc | ASTM D1505/D792 |
| Thickness | 50.0 microns | 1.97 mil | |
| Melt Flow | 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
2.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Elongation at Break, MD | 350 % | 350 % | ASTM D882 |
| Film Elongation at Break, TD | 650 % | 650 % | ASTM D882 |
| 2% Secant Modulus | 0.130 GPa | 18.9 ksi | MD; ASTM D882 |
| 0.140 GPa | 20.3 ksi | TD; ASTM D882 | |
| Elmendorf Tear Strength MD | 410 g | 410 g | gF; ASTM D1922 |
| Elmendorf Tear Strength TD | 280 g | 280 g | gF; ASTM D1922 |
| Dart Drop Test | 120 g | 0.265 lb | g/F50; ASTM D1709 |
| Film Tensile Strength at Break, MD | 22.0 MPa | 3190 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 20.0 MPa | 2900 psi | ASTM D882 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 8.0 % @Thickness 0.500 mm |
8.0 % @Thickness 0.0197 in |
ASTM D1003 |
| Gloss | 100 % @Thickness 0.500 mm |
100 % @Thickness 0.0197 in |
60°; ASTM D2457 |
Users viewing this material also viewed the following:
- Lehmann & Voss LUVOCOM® 1301-7449 PPS, linear, with carbon fiber and PTFE
- Mearthane Durethaneâ„¢ M DM-720A Foam Polyurethane
- HP Alloys Alloy C-276, 40% Cold Worked
- A. Schulman POLYFORT™ PP 2268UX Heat Resistant Polypropylene
- TIMET 6-4 Titanium Alloy (Ti-6Al-4V; ASTM Grade 5), >1.000-1.500 in, STD, Per Mil-T-9047G
- A. Schulman POLYBATCH™ Woodland Green 30233U/4 Concentrate Based In LLDPE
- Eastman Provista MP001 Copolymer
- DuPont™ Appeel® 20D855 Ethylene Acrylate
- Dow UNIVAL™ DMDC-6400 NT 7 High Density Polyethylene Resin (HDPE)
- Ineos Nova W441A Expandable Polystyrene
Copyright © lookpolymers.com All Rights Reserved