LG Chemical LUPOY EC5000A PC/ABS
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | LG Chemical |
| Trade Name | LUPOY |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical LUPOY EC5000A PC/ABS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Injection Molding, PC/ABS, General Purpose, Anti-Static.Application: E&E (Housing)Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.18 g/cc | 1.18 g/cc | ASTM D792 |
| Maximum Moisture Content | 0.020 | 0.020 | Injection Molding |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0060 cm/cm @Thickness 3.20 mm |
0.0040 - 0.0060 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 9.0 g/10 min @Load 2.16 kg, Temperature 250 °C |
9.0 g/10 min @Load 4.76 lb, Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 54.9 MPa @Thickness 3.20 mm |
7970 psi @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Elongation at Break | 80 % @Thickness 3.20 mm |
80 % @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Flexural Yield Strength | 94.1 MPa @Thickness 3.20 mm |
13700 psi @Thickness 0.126 in |
10mm/min; ASTM D790 |
| Flexural Modulus | 3.14 GPa @Thickness 3.20 mm |
455 ksi @Thickness 0.126 in |
10mm/min; ASTM D790 |
| Izod Impact, Notched | >= 4.90 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
>= 9.18 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 97.0 °C @Thickness 6.40 mm |
207 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| UL RTI, Electrical | 60.0 °C | 140 °F | |
| UL RTI, Mechanical with Impact | 60.0 °C | 140 °F | |
| UL RTI, Mechanical without Impact | 60.0 °C | 140 °F | |
| Flammability, UL94 | HB @Thickness >=1.50 mm |
HB @Thickness >=0.0591 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+10 - 1.00e+11 ohm-cm | 1.00e+10 - 1.00e+11 ohm-cm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 210 - 240 °C | 410 - 464 °F | Injection Molding |
| Middle Barrel Temperature | 215 - 250 °C | 419 - 482 °F | Injection Molding |
| Front Barrel Temperature | 225 - 260 °C | 437 - 500 °F | Injection Molding |
| Nozzle Temperature | 220 - 260 °C | 428 - 500 °F | Injection Molding |
| Melt Temperature | 230 - 260 °C | 446 - 500 °F | Injection Molding |
| Mold Temperature | 50.0 - 70.0 °C | 122 - 158 °F | Injection Molding |
| Drying Temperature | 60.0 - 80.0 °C | 140 - 176 °F | Injection Molding |
| Dry Time | 4.00 - 6.00 hour | 4.00 - 6.00 hour | Injection Molding |
| Back Pressure | 0.981 - 3.92 MPa | 142 - 569 psi | Injection Molding |
| Screw Speed | 40 - 70 rpm | 40 - 70 rpm | Injection Molding |
Users viewing this material also viewed the following:
- Rogers Corporation RT/duroid® 5870 Glass Microfiber Reinforced PTFE High Frequency Laminate
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 10 PHR Mistron Vapor Filler
- Lanxess Pocan® B 1700 000000 PBT
- Kazanorgsintez 108-278 Low Density Polyethylene Composition with Improved Processibility
- Stir SpA SG 75 OIL (PVC)
- Techmer ES Plastiblend® PBT/ABS GF/M40 FR 40/40% Glass/Mineral Filled
- Polyplastics Duranex® 751SA Polybutylene Terephthalate (PBT), Low density, Low wear, GF filled
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 40 PHR Carbon Black, N-326 (HS-HAF)
- Ceradyne SEMICORE® S1-5A MMOA 20/15 SmCo5 Samarium Cobalt Magnet
- Saint-Gobain CHR® 2045-10 Skived PTFE Film Backing Silicone Adhesive Pressure Sensitive Tape
Copyright © lookpolymers.com All Rights Reserved