LG Chemical LUPOL LW-4407 Low Warpage Polypropylene, 40% Glass Fiber/Mineral Filler Reinforced, Heat Resistant
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Glass/Mineral Reinforced |
| Manufacturer | LG Chemical |
| Trade Name | LUPOL |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical LUPOL LW-4407 Low Warpage Polypropylene, 40% Glass Fiber/Mineral Filler Reinforced, Heat Resistant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LUPOL resins, based on polyolefin with a wide range of characteristics, are a family of low cost engineering plastics.Applications: Automotive: Bumper cover, instrument panel, glove box, air cleaner, mud guard, door trim, garnishElectrical and Electronic: Tail lamp housing, air conditioner housing, fan, socket, washing machine partsIndustrial Parts and Household Appliance:Propeller fan, pulley, container, pump container, pump casing, handle and switch cover of electric jar, fan shroud/supportInformation Provided by LG Chem
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.21 g/cc | 1.21 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0050 cm/cm | 0.0050 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 63.0 MPa | 9140 psi | ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| Flexural Strength | 86.0 MPa | 12500 psi | ASTM D790 |
| Flexural Modulus | 5.88 GPa | 853 ksi | ASTM D790 |
| Izod Impact, Notched | 0.600 J/cm @Temperature 23.0 °C |
1.12 ft-lb/in @Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 150 °C | 302 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 200 - 220 °C | 392 - 428 °F | |
| Middle Barrel Temperature | 200 - 230 °C | 392 - 446 °F | |
| Front Barrel Temperature | 210 - 230 °C | 410 - 446 °F | |
| Nozzle Temperature | 210 - 240 °C | 410 - 464 °F | |
| Melt Temperature | 210 - 240 °C | 410 - 464 °F | |
| Mold Temperature | 40.0 - 90.0 °C | 104 - 194 °F | |
| Drying Temperature | 70.0 - 90.0 °C | 158 - 194 °F | |
| Dry Time | 2 - 3 hour | 2 - 3 hour | |
| Injection Pressure | 29.4 - 118 MPa | 4260 - 17100 psi | First |
| 78.45 - 98.07 MPa | 11380 - 14220 psi | Second | |
| Back Pressure | 0.490 - 3.92 MPa | 71.1 - 569 psi | |
| Screw Speed | 40 - 60 rpm | 40 - 60 rpm |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Wire & Cable 3311-xx23D Polyvinyl Chloride, Flexible (PVC, Flexible)
- Plastcom PLASTALEN® PQ 82 N Polypropylene with improved impact strength
- Polykemi AB SCANMID 6 B43^ D F15 Nylon 6, Glass Fiber Reinforced, Modified
- Formosa Plastics Formolene® FORMAX® L91507E2 Film (Hexene Grade) LLDPE (discontinued **)
- Huntsman Araldite EPN 1139 Epoxy Phenol Novolac
- Kennametal Stellite Stellite® 12 PM cast
- 3M Scotchkote™ HTX 517 Epoxy HT Lining
- PolyOne Lubri-Tech™ SF-000/40T Polyphenylene Sulfide - 40% PTFE (discontinued **)
- Solvay Specialty Polymers Ixef® 5002 Polyarylamide (PARA), 20% GlassPTFE (discontinued **)
- Indium Corp. Indalloy 203 Indium Solder Alloy
Copyright © lookpolymers.com All Rights Reserved