LG Chemical LUPOL GP3202Z PP+MF20%
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Mineral Reinforced |
| Manufacturer | LG Chemical |
| Trade Name | LUPOL |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical LUPOL GP3202Z PP+MF20%.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Injection Molding, PP+MF20%, Good WeatherabilityApplication: Electrical, Electronic and Automotive Interior PartsCAS: 9003-07-0 and 14807-96-6Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.05 g/cc | 1.05 g/cc | ASTM D792 |
| Maximum Moisture Content | 0.010 | 0.010 | Injection Molding |
| Melt Flow | 10 g/10 min @Load 2.16 kg, Temperature 230 °C |
10 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 28.4 MPa @Thickness 3.20 mm |
4120 psi @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Elongation at Break | 45 % @Thickness 3.20 mm |
45 % @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Flexural Yield Strength | 39.2 MPa @Thickness 6.40 mm |
5690 psi @Thickness 0.252 in |
30mm/min; ASTM D790 |
| Flexural Modulus | 2.45 GPa @Thickness 6.40 mm |
356 ksi @Thickness 0.252 in |
30mm/min; ASTM D790 |
| Izod Impact, Notched | >= 0.343 J/cm @Thickness 6.40 mm, Temperature -10.0 °C |
>= 0.643 ft-lb/in @Thickness 0.252 in, Temperature 14.0 °F |
ASTM D256 |
| >= 0.588 J/cm @Thickness 6.40 mm, Temperature 23.0 °C |
>= 1.10 ft-lb/in @Thickness 0.252 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 137 °C @Thickness 3.20 mm |
279 °F @Thickness 0.126 in |
Unannealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 190 - 210 °C | 374 - 410 °F | Injection Molding |
| Middle Barrel Temperature | 200 - 230 °C | 392 - 446 °F | Injection Molding |
| Front Barrel Temperature | 200 - 230 °C | 392 - 446 °F | Injection Molding |
| Nozzle Temperature | 210 - 230 °C | 410 - 446 °F | Injection Molding |
| Melt Temperature | 200 - 230 °C | 392 - 446 °F | Injection Molding |
| Mold Temperature | 40.0 - 60.0 °C | 104 - 140 °F | Injection Molding |
| Drying Temperature | 70.0 - 80.0 °C | 158 - 176 °F | Injection Molding |
| Dry Time | 3.00 - 4.00 hour | 3.00 - 4.00 hour | Injection Molding |
| Back Pressure | 29.4 - 58.8 MPa | 4260 - 8530 psi | Injection Molding |
| Screw Speed | 30 - 60 rpm | 30 - 60 rpm | Injection Molding |
Users viewing this material also viewed the following:
- Nanocyl PLASTICYL™ PBT1501 Polybutylene Terephthalate - Carbon Nanotube Masterbatch
- Polykemi AB POLYblend 65H MA5 PC/ABS-blend, Low Friction
- SABIC Innovative Plastics Lexan® CFR9111 PC COPOLYMER (Europe-Africa-Middle East)
- PTS Trilac® ABS-HS6500 High Impact ABS Resin
- PolyOne Geon™ Vinyl Flexible B6DB1 Polyvinyl Chloride, Flexible (PVC, Flexible)
- Overview of materials for Polypropylene with 30% Talc Filler
- Lucent Polymers PC/PBT-1212 Polycarbonate+PBT, General Purpose, Injection Grade
- A. Schulman PP 1667-01 Polypropylene Natural Homopolymer Polypropylene
- ArcelorMittal Dual Phase 780 Y450 Very high strength steel, Cold Rolled Steel
- Sawbones Fourth-Generation Simulated Cortical Bone (Short Fiber Filled Epoxy)
Copyright © lookpolymers.com All Rights Reserved