Master Bond EP126 Two Component Toughened Epoxy Adhesive System

Category	Polymer , Adhesive , Thermoset , Epoxy , Epoxy Adhesive
Manufacturer	Master Bond Inc.
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Master Bond EP126 Two Component Toughened Epoxy Adhesive System.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Master Bond Polymer System EP126 is a two component toughened epoxy resin based high temperature resistant adhesive system with continuous service capability at 500°F and outstanding chemical resistance. This unique high performance epoxy adhesive compound can also withstand temperatures as high as 700°F for limited time periods.

Physical Properties	Metric	English	Comments
Density	1.48 g/cc	0.0535 lb/in³
Water Absorption	<= 1.5 %	<= 1.5 %	2 hour water boil

Mechanical Properties	Metric	English	Comments
Flexural Strength	59.3 MPa	8600 psi
Flexural Modulus	4.00 GPa	580 ksi
Shear Strength	9.24 MPa @Temperature 260 °C	1340 psi @Temperature 500 °F	Tensile lap, Al/Al
	9.72 MPa @Temperature 260 °C	1410 psi @Temperature 500 °F	Tensile lap, Stainless steel/Stainless steel
	15.9 MPa @Temperature 23.9 °C	2310 psi @Temperature 75.0 °F	Tensile lap, Stainless steel/Stainless steel
	18.9 MPa @Temperature 23.9 °C	2740 psi @Temperature 75.0 °F	Tensile lap, Al/Al
	7.72 MPa @Temperature 260 °C, Time 1.80e+6 sec	1120 psi @Temperature 500 °F, Time 500 hour	Tensile lap, Al/Al
	8.00 MPa @Temperature 260 °C, Time 1.80e+6 sec	1160 psi @Temperature 500 °F, Time 500 hour	Tensile lap, Stainless steel/Stainless steel
Izod Impact, Notched	0.347 J/cm	0.650 ft-lb/in
Peel Strength	>= 0.982 kN/m @Temperature 23.9 °C	>= 5.60 pli @Temperature 75.0 °F	Al/
	>= 0.121 kN/m @Temperature 260 °C, Time 1.80e+6 sec	>= 0.690 pli @Temperature 500 °F, Time 500 hour	Al/

Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Air	260 °C	500 °F	Continuous
Heat Distortion Temperature	>= 110 °C	>= 230 °F

Descriptive Properties	Value	Comments
Gasoline immersion	<1.0%	14 days