PolyOne Nymax™ 600 Zip 0 Black 13 Polyamide 6 Alloy (Nylon 6 Alloy)

Category	Polymer , Thermoplastic , Nylon , Nylon 6
Manufacturer	PolyOne Corporation
Trade Name	Nymax™
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	PolyOne Nymax™ 600 Zip 0 Black 13 Polyamide 6 Alloy (Nylon 6 Alloy).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

The Nymax® 600 Blend Series of nylon 6 materials are salt-and-pepper pelletized blends combining select nylon resins and process aids, performance modifiers, and color concentrates. These materials have been formulated to provide improved melt processing, part performance, or surface appearance depending upon grade selected and are offered as an economical alternative to fully compounded products.Molded Test Bars: Dry as MoldedInformation provided by PolyOne

Physical Properties	Metric	English	Comments
Specific Gravity	1.14 g/cc	1.14 g/cc	ASTM D792
Water Absorption	1.5 % @Thickness 3.18 mm	1.5 % @Thickness 0.125 in	@ 24 hrs; ASTM D570
Linear Mold Shrinkage, Flow	0.0080 - 0.010 cm/cm	0.0080 - 0.010 in/in	ASTM D955

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	75.8 MPa	11000 psi	Type I, 5.1 mm/min; ASTM D638
Elongation at Break	10 %	10 %	Type I, 5.1 mm/min; ASTM D638
Tensile Modulus	2.76 GPa	400 ksi	ASTM D638
Flexural Strength	117 MPa	17000 psi	ASTM D790
Flexural Modulus	2.76 GPa	400 ksi	ASTM D790
Izod Impact, Notched	0.590 J/cm @Thickness 3.18 mm, Temperature 23.0 °C	1.11 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F	Injection Molded; ASTM D256A

Thermal Properties	Metric	English	Comments
Melting Point	220 °C	428 °F	ASTM D789
Deflection Temperature at 1.8 MPa (264 psi)	55.0 °C @Thickness 3.18 mm	131 °F @Thickness 0.125 in	Unannealed; ASTM D648

Processing Properties	Metric	English
Mold Temperature	48.9 - 93.3 °C	120 - 200 °F
Drying Temperature	82.2 °C	180 °F
Dry Time	4.00 hour	4.00 hour

Descriptive Properties	Value	Comments
Appearance	Black
Features	General Purpose
	Nucleated
Forms	Pellets
Generic Material	Nylon 6 Alloy
Generic Name	Polyamide 6 Alloy (Nylon 6 Alloy)
Processing Method	Injection Molding
Regional Availability	North America
	South America
Uses	Automotive Applications
	Construction Applications
	Consumer Applications
	General Purpose
	Industrial Applications