SABIC Innovative Plastics LNP STAT-KON REP349 PA 66 (Asia Pacific)

Category Polymer , Thermoplastic , Nylon , Nylon 66
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP STAT-KON
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP STAT-KON REP349 PA 66 (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Stat-kon* REP349 is a compound based on Nylon 66 resin containing PTFE, Carbon Fiber. Added features of this material include: Electrically Conductive, Internally Lubricated.
Physical Properties Metric English Comments
Density 1.54 g/cc
0.0556 lb/in³
ASTM D792
1.54 g/cc
0.0556 lb/in³
ISO 1183
Moisture Absorption 0.400 %
0.400 %
50% RH, 24 hrs; ASTM D570
Linear Mold Shrinkage, Flow 0.0018 cm/cm

@Time 86400 sec
 0.0018 in/in

@Time 24.0 hour
 ISO 294
0.0010 - 0.0030 cm/cm

@Time 86400 sec
 0.0010 - 0.0030 in/in

@Time 24.0 hour
 ASTM D955
Linear Mold Shrinkage, Transverse 0.0067 cm/cm

@Time 86400 sec
 0.0067 in/in

@Time 24.0 hour
 ISO 294
0.0060 - 0.0080 cm/cm

@Time 86400 sec
 0.0060 - 0.0080 in/in

@Time 24.0 hour
 ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 167 MPa
24200 psi
ASTM D638
168 MPa
24400 psi
ISO 527
Tensile Strength, Yield 167 MPa
24200 psi
ASTM D638
168 MPa
24400 psi
ISO 527
Elongation at Break 1.7 %
1.7 %
ISO 527
1.8 %
1.8 %
ASTM D638
Elongation at Yield 1.7 %
1.7 %
ISO 527
1.8 %
1.8 %
ASTM D638
Tensile Modulus 18.17 GPa
2635 ksi
1 mm/min; ISO 527
19.3 GPa
2800 ksi
50 mm/min; ASTM D638
Flexural Strength 255 MPa
37000 psi
ASTM D790
263 MPa
38100 psi
ISO 178
Flexural Modulus 15.16 GPa
2199 ksi
ASTM D790
15.3 GPa
2220 ksi
ISO 178
Izod Impact, Notched 0.580 J/cm
1.09 ft-lb/in
ASTM D256
Izod Impact, Unnotched 5.76 J/cm
10.8 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 5.00 kJ/m²
2.38 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 34.0 kJ/m²
16.2 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 5.00 J
3.69 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
Impact Test 2.00 J
1.48 ft-lb
Multiaxial Impact; ISO 6603
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 35.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 19.4 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
36.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 20.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
CTE, linear, Transverse to Flow 12.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 6.67 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
12.6 µm/m-°C

@Temperature -40.0 - 40.0 °C
 7.00 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
Deflection Temperature at 0.46 MPa (66 psi) 251 °C
484 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
250 °C

@Thickness 3.20 mm
 482 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 234 °C
453 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
232 °C

@Thickness 3.20 mm
 450 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Electrical Properties Metric English Comments
Surface Resistance 1.00e+7 - 1.00e+9 ohm
1.00e+7 - 1.00e+9 ohm
ASTM D257