SABIC Innovative Plastics LNP KONDUIT OX11314 PPS (Asia Pacific)

Category Polymer , Thermoplastic , Polyphenylene Sulfide (PPS)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP Konduit
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP KONDUIT OX11314 PPS (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Thermally conductive mineral filled PPS FR compound
Physical Properties Metric English Comments
Density 1.89 g/cc
0.0683 lb/in³
ASTM D792
Water Absorption 0.10 %

@Time 86400 sec
 0.10 %

@Time 24.0 hour
 SABIC Method
Moisture Absorption 0.0300 %
0.0300 %
23°C / 50% RH; ISO 62
Linear Mold Shrinkage, Flow 0.0018 cm/cm

@Time 86400 sec
 0.0018 in/in

@Time 24.0 hour
 ASTM D955
Linear Mold Shrinkage, Transverse 0.0024 cm/cm

@Time 86400 sec
 0.0024 in/in

@Time 24.0 hour
 ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 45.0 MPa
6530 psi
Type I, 5 mm/min; ASTM D638
Elongation at Break 0.50 %
0.50 %
Type I, 5 mm/min; ASTM D638
Tensile Modulus 11.4 GPa
1650 ksi
5 mm/min; ASTM D638
Flexural Strength 47.0 MPa
6820 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 11.2 GPa
1620 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 0.210 J/cm
0.393 ft-lb/in
ASTM D256
Izod Impact, Unnotched 0.580 J/cm
1.09 ft-lb/in
ASTM D4812
Charpy Impact Unnotched 0.500 J/cm²
2.38 ft-lb/in²
ISO 179/2C
Charpy Impact, Notched 0.200 J/cm²
0.952 ft-lb/in²
ISO 179/2C
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 26.0 µm/m-°C

@Temperature 40.0 - 120 °C
 14.4 µin/in-°F

@Temperature 104 - 248 °F
 ASTM E 831
CTE, linear, Transverse to Flow 51.0 µm/m-°C

@Temperature 40.0 - 120 °C
 28.3 µin/in-°F

@Temperature 104 - 248 °F
 ASTM E 831
Specific Heat Capacity 1.44 J/g-°C
0.344 BTU/lb-°F
ASTM C351
Thermal Conductivity 0.900 W/m-K
6.25 BTU-in/hr-ft²-°F
through-plane, ø80*3mm discs; ISO 22007-2
1.00 W/m-K
6.94 BTU-in/hr-ft²-°F
through-plane, 10*10*3mm sample; ASTM E 1461-07
2.10 W/m-K
14.6 BTU-in/hr-ft²-°F
in-plane, ø25*0.4mm disc; ASTM E 1461-07
2.22 W/m-K
15.4 BTU-in/hr-ft²-°F
in-plane, ø80*3mm discs; ISO 22007-2
Deflection Temperature at 1.8 MPa (264 psi) 191 °C

@Thickness 6.40 mm
 376 °F

@Thickness 0.252 in
 unannealed; ASTM D648
Flammability, UL94 V-0

@Thickness 0.800 mm
 V-0

@Thickness 0.0315 in
 UL 94
Glow Wire Test 875 °C
1610 °F
IEC 60695-2-13
960 °C
1760 °F
IEC 60695-2-13
960 °C

@Thickness 1.00 mm
 1760 °F

@Thickness 0.0394 in
 IEC 60695-2-12
Electrical Properties Metric English Comments
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
ASTM D257
Dielectric Strength >= 5.00 kV/mm

@Thickness 1.00 mm
 >= 127 kV/in

@Thickness 0.0394 in
 in oil; ASTM D149
Comparative Tracking Index 600 V
600 V
IEC 60112
Hot Wire Ignition, HWI >= 120 sec
>= 120 sec
UL 746A
High Amp Arc Ignition, HAI 60 - 120 arcs
60 - 120 arcs
UL 746A