LG Chemical LUMID LW4303B(W) PA66+MF30%, Low Warpage
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Mineral Filled |
| Manufacturer | LG Chemical |
| Trade Name | LUMID |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical LUMID LW4303B(W) PA66+MF30%, Low Warpage.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Feature: Injection Molding, PA66+MF30%, Low WarpageApplication: Automotive PartsCAS No. 32131-17-2, 13983-17-0 and 65997-17-3Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.40 g/cc | 1.40 g/cc | ASTM D792 |
| Water Absorption | 0.70 % | 0.70 % | ASTM D570 |
| Maximum Moisture Content | 0.090 | 0.090 | Injection Molding |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.011 cm/cm @Thickness 3.20 mm |
0.0050 - 0.011 in/in @Thickness 0.126 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 122 | 122 | ASTM D785 |
| Tensile Strength, Yield | 186 MPa @Thickness 3.20 mm |
27000 psi @Thickness 0.126 in |
5mm/min; ASTM D638 |
| Elongation at Break | 2.0 % @Thickness 3.20 mm |
2.0 % @Thickness 0.126 in |
5mm/min; ASTM D638 |
| Flexural Yield Strength | 186 MPa @Thickness 3.20 mm |
27000 psi @Thickness 0.126 in |
1.3mm/min; ASTM D790 |
| Flexural Modulus | 5.88 GPa @Thickness 3.20 mm |
853 ksi @Thickness 0.126 in |
1.3mm/min; ASTM D790 |
| Izod Impact, Notched | 0.490 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
0.918 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 40.0 µm/m-°C | 22.2 µin/in-°F | ASTM D696 |
| Melting Point | 260 °C | 500 °F | ASTM D3418 |
| Deflection Temperature at 1.8 MPa (264 psi) | 235 °C @Thickness 6.40 mm |
455 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | ASTM D257 |
| Dielectric Strength | 21.0 kV/mm @Thickness 1.00 mm |
533 kV/in @Thickness 0.0394 in |
ASTM D149 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 270 - 285 °C | 518 - 545 °F | Injection Molding |
| Middle Barrel Temperature | 275 - 290 °C | 527 - 554 °F | Injection Molding |
| Front Barrel Temperature | >= 280 °C | >= 536 °F | Injection Molding |
| Nozzle Temperature | 280 - 295 °C | 536 - 563 °F | Injection Molding |
| Melt Temperature | 270 - 295 °C | 518 - 563 °F | Injection Molding |
| Mold Temperature | 80.0 - 110 °C | 176 - 230 °F | Injection Molding |
| Drying Temperature | 80.0 - 100 °C | 176 - 212 °F | Injection Molding |
| Dry Time | 4.00 - 5.00 hour | 4.00 - 5.00 hour | Injection Molding |
| Back Pressure | 29.4 - 58.8 MPa | 4260 - 8530 psi | Injection Molding |
| Screw Speed | 30 - 60 rpm | 30 - 60 rpm | Injection Molding |
Users viewing this material also viewed the following:
- MV Labs TL1000 Tl2SO4 Thallium(I) sulfate
- Polimeri Europa Clearflex® H&T FHH 508 Octene Copolymer Linear Medium Density Polyethylene
- LyondellBasell Alathon® M6061 High Density Polyethylene, Injection Molding Grade
- Momentive Performance Materials UltraPruf® SCS 2300 Construction Sealant
- Saint-Gobain CHR® C661 Copper Foil Backing Acrylic Adhesive Pressure Sensitive Tape
- A. Schulman INVISION™ VX-5075UI Soft Touch Polyolefin Thermoplastic
- Tisan TISARBON® UNR Polycarbonate
- Diamond Polymers ABSPC 9802 ABS/PC Molding Grade, High Impact, High Heat
- ExxonMobil Teresstic 320
- Eurostar Staramide BG6U PA6, 30% Glass Fiber Filled, UV Stabilized, Injection Molded
Copyright © lookpolymers.com All Rights Reserved