- A. Schulman SCHULADUR® A GB20 20% Glass Bead Reinforced PBT
A. Schulman SCHULADUR® A GB20 20% Glass Bead Reinforced PBT
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), Glass Bead Filled |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | A. Schulman SCHULADUR® A GB20 20% Glass Bead Reinforced PBT.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by A. Schulman.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.45 g/cc | 1.45 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.018 cm/cm | 0.018 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 48.3 MPa | 7000 psi | ASTM D638 |
| Elongation at Break | 3.2 % | 3.2 % | ASTM D638 |
| Flexural Strength | 86.2 MPa | 12500 psi | ASTM D790 |
| Flexural Modulus | 3.45 GPa | 500 ksi | ASTM D790 |
| Izod Impact, Notched | 0.427 J/cm | 0.800 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 2.67 J/cm | 5.00 ft-lb/in | ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 225 °C | 437 °F | ASTM D3418 |
| Deflection Temperature at 0.46 MPa (66 psi) | 177 °C | 350 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 110 °C | 230 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 250 - 260 °C | 482 - 500 °F | |
| Mold Temperature | 30.0 - 65.6 °C | 86.0 - 150 °F | |
| Drying Temperature | 130 °C | 266 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | Predrying |
Users viewing this material also viewed the following:
- REXtac Rextac® RT 2315 Amorphous Polyalphaolefin (APAO)
- ExxonMobil Escorene® UL-7750 EVA Copolymer, Adhesive and Sealant Grade (discontinued **)
- MarkeTech Repton EXP 386 Aluminum Titanate
- Kolon KOPA® KN333MT30BL Mineral Reinforced Nylon 66
- SABIC Innovative Plastics LNP THERMOCOMP PF00CS PA 6 (Europe-Africa-Middle East)
- A. Schulman POLYFORT™ FPP1666 Talc Filled Homopolymer Polypropylene
- Colorite Polymers 81-403 Radiopaque Vinyl Compound
- A. Schulman ComAlloy E-16901B PPS Alloy, Electrically Conductive - Carbon Fiber Filled
- Arkema Group Lacovyl® PB 1152 C PVC
Copyright © lookpolymers.com All Rights Reserved