Solvay Technyl® C 218 MT25 V15 25% Mineral, 15% Glass Filled, Heat Stabilized Nylon 6
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Glass/Mineral Reinforced |
| Manufacturer | Solvay |
| Trade Name | Technyl® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay Technyl® C 218 MT25 V15 25% Mineral, 15% Glass Filled, Heat Stabilized Nylon 6.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Rhodia; Rhodia has been acquired by Solvay.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.47 g/cc | 0.0531 lb/in³ | ISO 1183-A |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 125 MPa | 18100 psi | ISO 527 |
| Elongation at Break | 2.5 % | 2.5 % | ISO 527 |
| Tensile Modulus | 9.72 GPa | 1410 ksi | ISO 527 |
| Izod Impact, Notched (ISO) | 4.20 kJ/m² | 2.00 ft-lb/in² | ISO 180 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 222 °C | 432 °F | ISO 3146-C |
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | ISO 75-2 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 230 - 240 °C | 446 - 464 °F | |
| Middle Barrel Temperature | 250 - 255 °C | 482 - 491 °F | Compression Zone |
| Front Barrel Temperature | 250 - 255 °C | 482 - 491 °F | |
| Melt Temperature | 230 - 260 °C | 446 - 500 °F | |
| Mold Temperature | 100 - 120 °C | 212 - 248 °F | Surface |
| Drying Temperature | 80.0 °C | 176 °F | Dehumidifying Dryer |
| Dry Time | 3 - 4 hour | 3 - 4 hour | |
| Moisture Content | <= 0.20 % | <= 0.20 % | |
| Back Pressure | 0.138 - 0.689 MPa | 20.0 - 100 psi | |
| Fill Speed | 200 - 600 mm/sec | 7.87 - 23.6 in/sec | Peripheral Screw Speed |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Injection Speed (cm3/sec) | 120 - 170 cm3/sec |
Users viewing this material also viewed the following:
- RheTech Products T40P108-01 40% Talc Reinforced Polypropylene, Black
- Premix Premi-Glas® 1100-20 Fiberglass Reinforced Thermoset BMC
- SABIC Innovative Plastics LNP LUBRICOMP AL002 ABS
- Kotec Carbotex K-30F5 Polycarbonate, Wear Resistant
- Solvay ANTAROX® BL 214 Surfactant
- Unitika M1030E PA6, Dry
- A. Schulman SUPERLINEAR™ XL 0360 Rotational Molding Resin
- Total PSC 529 Polystyrene
- DSM Stanyl® TE250F6 Nylon 46-30% Glass Reinforced (European and Asian Grade) (Cond)
- RheTech Products M20P101-01 20% Mica Reinforced Polypropylene, Black
Copyright © lookpolymers.com All Rights Reserved