LG Chemical LUMID HI5083A(W) PA6/ABS+MF8%, High Impact

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Impact Grade, Molded , Nylon , Nylon 6 , Nylon 6, 20% Mineral Filled , Nylon 6, Impact Grade
Manufacturer LG Chemical
Trade Name LUMID
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LG Chemical LUMID HI5083A(W) PA6/ABS+MF8%, High Impact.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Feature: Injection Molding, PA6/ABS+MF8%, High ImpactApplication: Electric/Electronic Components (Shaver Die)CAS No. 25038-54-4, 9003-56-9, 9003-54-7 and 14807-96-6Information provided by LG Chemical
Physical Properties Metric English Comments
Specific Gravity 1.11 g/cc
1.11 g/cc
ASTM D792
Water Absorption 0.60 %
0.60 %
ASTM D570
Linear Mold Shrinkage, Flow 0.0050 - 0.010 cm/cm

@Thickness 3.20 mm
 0.0050 - 0.010 in/in

@Thickness 0.126 in
 ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength, Yield 49.0 MPa

@Thickness 3.20 mm
 7110 psi

@Thickness 0.126 in
 50mm/min; ASTM D638
Elongation at Break 37 %

@Thickness 3.20 mm
 37 %

@Thickness 0.126 in
 50mm/min; ASTM D638
Flexural Yield Strength 73.0 MPa

@Thickness 6.40 mm
 10600 psi

@Thickness 0.252 in
 2.8mm/min; ASTM D790
Flexural Modulus 2.3500 GPa

@Thickness 6.40 mm
 340.83 ksi

@Thickness 0.252 in
 2.8mm/min; ASTM D790
Izod Impact, Notched 1.03 J/cm

@Thickness 3.20 mm,
Temperature 23.0 °C
 1.93 ft-lb/in

@Thickness 0.126 in,
Temperature 73.4 °F
 ASTM D256
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 80.0 µm/m-°C
44.4 µin/in-°F
ASTM D696
Deflection Temperature at 1.8 MPa (264 psi) 89.4 °C

@Thickness 6.40 mm
 193 °F

@Thickness 0.252 in
 Unannealed; ASTM D648
UL RTI, Electrical 60.0 °C

@Thickness >=0.750 mm
 140 °F

@Thickness >=0.0295 in
60.0 °C

@Thickness >=1.50 mm
 140 °F

@Thickness >=0.0591 in
60.0 °C

@Thickness >=3.00 mm
 140 °F

@Thickness >=0.118 in
UL RTI, Mechanical with Impact 60.0 °C

@Thickness >=0.750 mm
 140 °F

@Thickness >=0.0295 in
60.0 °C

@Thickness >=1.50 mm
 140 °F

@Thickness >=0.0591 in
60.0 °C

@Thickness >=3.00 mm
 140 °F

@Thickness >=0.118 in
UL RTI, Mechanical without Impact 60.0 °C

@Thickness >=0.750 mm
 140 °F

@Thickness >=0.0295 in
60.0 °C

@Thickness >=1.50 mm
 140 °F

@Thickness >=0.0591 in
60.0 °C

@Thickness >=3.00 mm
 140 °F

@Thickness >=0.118 in
Flammability, UL94 HB

@Thickness >=0.750 mm
 HB

@Thickness >=0.0295 in
HB

@Thickness >=1.50 mm
 HB

@Thickness >=0.0591 in
HB

@Thickness >=3.00 mm
 HB

@Thickness >=0.118 in
Processing Properties Metric English Comments
Rear Barrel Temperature 245 - 260 °C
473 - 500 °F
Injection Molding
Middle Barrel Temperature 250 - 270 °C
482 - 518 °F
Injection Molding
Front Barrel Temperature 260 - 270 °C
500 - 518 °F
Injection Molding
Nozzle Temperature 260 - 275 °C
500 - 527 °F
Injection Molding
Melt Temperature 260 - 275 °C
500 - 527 °F
Injection Molding
Mold Temperature 80.0 - 100 °C
176 - 212 °F
Injection Molding
Drying Temperature 70.0 - 90.0 °C
158 - 194 °F
Injection Molding
Dry Time 4.00 - 5.00 hour
4.00 - 5.00 hour
Injection Molding