LG Chemical LUMID GP2339B(W) PA66+GF33%, General Purpose
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled |
| Manufacturer | LG Chemical |
| Trade Name | LUMID |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical LUMID GP2339B(W) PA66+GF33%, General Purpose.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Feature: Injection Molding, PA66+GF33%, General PurposeApplication: Automotive (Cylinder Head Cover)CAS No. 32131-17-2 and 65997-17-3Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.38 g/cc | 1.38 g/cc | ASTM D792 |
| Water Absorption | 0.70 % | 0.70 % | ASTM D570 |
| Maximum Moisture Content | 0.10 | 0.10 | Injection Molding |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0090 cm/cm @Thickness 3.20 mm |
0.0040 - 0.0090 in/in @Thickness 0.126 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 122 | 122 | ASTM D785 |
| Tensile Strength, Yield | 177 MPa @Thickness 3.20 mm |
25600 psi @Thickness 0.126 in |
5mm/min; ASTM D638 |
| Elongation at Break | 3.0 % @Thickness 3.20 mm |
3.0 % @Thickness 0.126 in |
5mm/min; ASTM D638 |
| Flexural Yield Strength | 255 MPa @Thickness 3.20 mm |
37000 psi @Thickness 0.126 in |
1.3mm/min; ASTM D790 |
| Flexural Modulus | 8.83 GPa @Thickness 3.20 mm |
1280 ksi @Thickness 0.126 in |
1.3mm/min; ASTM D790 |
| Izod Impact, Notched | 0.785 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
1.47 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 30.0 µm/m-°C | 16.7 µin/in-°F | ASTM D696 |
| Melting Point | 260 °C | 500 °F | ASTM D3418 |
| Deflection Temperature at 0.46 MPa (66 psi) | 260 °C @Thickness 6.40 mm |
500 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C @Thickness 6.40 mm |
482 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | ASTM D257 |
| Dielectric Constant | 4.0 @Frequency 1.00e+6 Hz |
4.0 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Dielectric Strength | 25.0 kV/mm @Thickness 1.00 mm |
635 kV/in @Thickness 0.0394 in |
ASTM D149 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 260 - 270 °C | 500 - 518 °F | Injection Molding |
| Middle Barrel Temperature | 270 - 285 °C | 518 - 545 °F | Injection Molding |
| Front Barrel Temperature | 270 - 295 °C | 518 - 563 °F | Injection Molding |
| Nozzle Temperature | 270 - 295 °C | 518 - 563 °F | Injection Molding |
| Melt Temperature | 270 - 295 °C | 518 - 563 °F | Injection Molding |
| Mold Temperature | 80.0 - 110 °C | 176 - 230 °F | Injection Molding |
| Drying Temperature | 80.0 - 100 °C | 176 - 212 °F | Injection Molding |
| Dry Time | 4.00 - 5.00 hour | 4.00 - 5.00 hour | Injection Molding |
| Back Pressure | 29.4 - 58.8 MPa | 4260 - 8530 psi | Injection Molding |
| Screw Speed | 30 - 60 rpm | 30 - 60 rpm | Injection Molding |
Users viewing this material also viewed the following:
- Premix Thermoplastics PREWHITE PE 13-60
- Pearl Engineering PEPLPET FR-101-H Monofilament Resin
- Karina 834-48/1-A-ERM-LMP Black PVC Compound
- SPS Guang Zhou POBUXâ„¢ 3001G10 Flame-retarded/GF10%-PBT
- Teknor Apex APEX® 80881-A Polyvinyl Chloride Compound
- Lubrizol STAT-RITE® E-1150 Ether-Type Static Dissipative Polymer
- Borealis HC401BF Polypropylene Homopolymer
- Zeon Chemicals Nipol® 1472X Nitrile Powder and Crumb Elastomer
- Loctite® Durabond® M-31CL Epoxy Adhesive
- Solvay RHODAPON® SB-8208/S STD Surfactant
Copyright © lookpolymers.com All Rights Reserved