Cossa Polimeri ESTAPROP H 1080 TG Polypropylene, 40% Mineral Filled

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Mineral Reinforced
Manufacturer Cossa Polimeri S.r.L.
Trade Name ESTAPROP
Port Ningbo port,China
Trade Terms EXW, FOB, CFR, CIF
Payment Terms L/C, T/T, PayPal
Download PDF Cossa Polimeri ESTAPROP H 1080 TG Polypropylene, 40% Mineral Filled.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
PP homopolymer 40% mineral fillerExcellent stiffness, good dimensional stabilityInformation provided by Cossa Polimeri S.r.l.
Physical Properties Metric English Comments
Density 1.25 g/cc
0.0452 lb/in³
ASTM D 792
Linear Mold Shrinkage 0.010 - 0.012 cm/cm
0.010 - 0.012 in/in
ASTM D 955
Melt Flow 10 g/10 min
<br>@Load 2.16 kg,<br> Temperature 230 °C
 10 g/10 min
<br>@Load 4.76 lb,<br> Temperature 446 °F
 ASTM D 1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 25.0 MPa
3630 psi
ASTM D 638
Tensile Strength, Yield 30.0 MPa
4350 psi
ASTM D 638
Elongation at Break 10 %
10 %
ASTM D 638
Tensile Modulus 4.10 GPa
595 ksi
ASTM D 638
Flexural Modulus 3.80 GPa
551 ksi
ASTM D 790
Izod Impact, Notched 0.150 J/cm
<br>@Temperature -20.0 °C
 0.281 ft-lb/in
<br>@Temperature -4.00 °F
 ASTM D 638
0.200 J/cm
<br>@Temperature 0.000 °C
 0.375 ft-lb/in
<br>@Temperature 32.0 °F
 ASTM D 638
0.300 J/cm
<br>@Temperature 23.0 °C
 0.562 ft-lb/in
<br>@Temperature 73.4 °F
 ASTM D 256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 72.0 °C
162 °F
120°C/hr; ASTM D 648
Vicat Softening Point 97.0 °C
<br>@Load 5.00 kg
 207 °F
<br>@Load 11.0 lb
 50°C/hr; ASTM D 1525
Flammability, UL94 HB
<br>@Thickness 1.60 mm
 HB
<br>@Thickness 0.0630 in
HB
<br>@Thickness 3.20 mm
 HB
<br>@Thickness 0.126 in